Hot corrosion evaluation of Gd2O3-Yb2O3 co-doped Y2O3 stabilized ZrO2 thermal barrier oxides exposed to Na2SO4+V2O5 molten salt

被引：71
|
作者：
Guo, Lei [1 ,2 ,3 ]
Zhang, Chenglong [1 ,2 ]
Li, Mingzhu [1 ,2 ]
Sun, Wei [1 ]
Zhang, Zhaoyang [1 ]
Ye, Fuxing [1 ,2 ,3 ]
机构：
[1] Tianjin Univ, Sch Mat Sci & Engn, 92 Weijin Rd, Tianjin 300072, Peoples R China
[2] Tianjin Univ, Tianjin Key Lab Adv Joining Technol, 92 Weijin Rd, Tianjin 300072, Peoples R China
[3] Tianjin Univ, Key Lab Adv Ceram & Machining Technol, Minist Educ, 92 Weijin Rd, Tianjin 300072, Peoples R China
来源：
CERAMICS INTERNATIONAL | 2017年 / 43卷 / 02期
基金：
中国国家自然科学基金;
关键词：
Thermal barrier coatings (TBCs); Doped YSZ; Hot corrosion; Molten salt; PHYSICAL VAPOR-DEPOSITION; ZIRCONIA COATINGS; PHASE-STABILITY; VANADATE SALT; EB-PVD; BEHAVIOR; YTTRIA; CERAMICS; SULFATE; RESISTANCE;
D O I：
10.1016/j.ceramint.2016.11.109
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
1 mol% Gd2O3 and 1 mol% Yb2O3 co-doped 3.5 mol% Y2O3 stabilized ZrO2 (GdYb-YSZ) ceramics in metastable tetragonal (t') structure were fabricated, and their hot corrosion behaviors were evaluated. The corrosion tests were performed at 700 degrees C, 800 degrees C, 900 degrees C and 1000 degrees C for 4 h in the presence of Na2SO4+V2O5 molten salt. After corrosion, t' phase could still be detected on the corroded surfaces and its content decreased with increasing the corrosion temperature. The corrosion products were composed of doped YVO4 and m-ZrO2, but some amounts of Na4V2O7 were found at low corrosion temperatures (700 degrees C and 800 degrees C). The corrosion resistance characteristic of GdYb-YSZ was compared with that of YSZ. Under an identical corrosion condition, GdYb-YSZ had less monoclinic phase formed, indicative of a better hot corrosion resistance. The hot corrosion mechanism was discussed in detail.
引用
收藏
页码：2780 / 2785
页数：6
相关论文
共 50 条
  • [41] Toughening effect of Yb2O3 stabilized ZrO2 doped in Gd2Zr2O7 ceramic for thermal barrier coatings
    Zhang, Yu
    Guo, Lei
    Zhao, Xiaoxiang
    Wang, Caimei
    Ye, Fuxing
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 648 : 385 - 391
  • [42] Failure mechanisms for Gd2O3-Yb2O3 co-doped YSZ thermal barrier coatings under high-temperature gradient
    Fan, Jiabin
    Wang, Quansheng
    Ning, Xianjin
    Li, Li
    Sun, Zhenning
    CERAMICS INTERNATIONAL, 2024, 50 (16) : 28563 - 28572
  • [43] Evaluation of hot corrosion behavior of plasma sprayed ceria and yttria stabilized zirconia thermal barrier coatings in the presence of Na2SO4+V2O5 molten salt
    Ahmadi-Pidani, Raheleh
    Shoja-Razavi, Reza
    Mozafarinia, Reza
    Jamali, Hossein
    CERAMICS INTERNATIONAL, 2012, 38 (08) : 6613 - 6620
  • [44] Thermophysical Properties of Y2O3 and Gd2O3 Co-doped SrZrO3 Thermal Barrier Coating Material
    Ma Wen
    Song Feng-Yu
    Dong Hong-Ying
    Xu Ping
    Lun Wen-Shan
    Zheng Xue-Bin
    JOURNAL OF INORGANIC MATERIALS, 2012, 27 (02) : 209 - 213
  • [45] Microstructure, phase stability and thermal conductivity of plasma sprayed Yb2O3, Y2O3 co-stabilized ZrO2 coatings
    Liu, Huaifei
    Li, Songlin
    Li, Qilian
    Li, Yongming
    Zhou, Wuxi
    SOLID STATE SCIENCES, 2011, 13 (03) : 513 - 519
  • [46] Ceramics based on cubic ZrO2 (Y2O3) with addition of a fused Al2O3-ZrO2 (Y2O3) eutectic
    Ordan'yan, SS
    Gudovskikh, PS
    Pigunova, AN
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2004, 45 (01) : 1 - 2
  • [47] Improvement on the phase stability, mechanical properties and thermal insulation of Y2O3-stabilized ZrO2 by Gd2O3 and Yb2O3 co-doping
    Guo, Lei
    Guo, Hongbo
    Gong, Shengkai
    Xu, Huibin
    CERAMICS INTERNATIONAL, 2013, 39 (08) : 9009 - 9015
  • [48] Specific Features of the Local Structure and Transport Properties of ZrO2–Sc2O3–Y2O3 and ZrO2–Sc2O3–Yb2O3 Crystals
    M. A. Borik
    T. V. Volkova
    I. E. Kuritzyna
    N. A. Larina
    E. E. Lomonova
    V. A. Myzina
    P. A. Ryabochkina
    N. Yu. Tabachkova
    Optics and Spectroscopy, 2018, 125 : 898 - 902
  • [49] La2O3 doped Y2O3 stabilized ZrO2 TBC prepared by EB-PVD
    Matsumoto, Mineaki
    Yamaguchi, Norio
    Matsubara, Hideaki
    SCIENCE OF ENGINEERING CERAMICS III, 2006, 317-318 : 501 - 504
  • [50] Thermal Shock Resistance of Al2O3/ZrO2 (Y2O3) Composites
    Ma Weimin
    Wen Lei
    Sun Xudong
    Cui Tong
    Qiu Guanming
    JOURNAL OF RARE EARTHS, 2007, 25 : 53 - 57
12345