Hot corrosion evaluation of Gd2O3-Yb2O3 co-doped Y2O3 stabilized ZrO2 thermal barrier oxides exposed to Na2SO4+V2O5 molten salt

被引：71
|
作者：
Guo, Lei [1 ,2 ,3 ]
Zhang, Chenglong [1 ,2 ]
Li, Mingzhu [1 ,2 ]
Sun, Wei [1 ]
Zhang, Zhaoyang [1 ]
Ye, Fuxing [1 ,2 ,3 ]
机构：
[1] Tianjin Univ, Sch Mat Sci & Engn, 92 Weijin Rd, Tianjin 300072, Peoples R China
[2] Tianjin Univ, Tianjin Key Lab Adv Joining Technol, 92 Weijin Rd, Tianjin 300072, Peoples R China
[3] Tianjin Univ, Key Lab Adv Ceram & Machining Technol, Minist Educ, 92 Weijin Rd, Tianjin 300072, Peoples R China
来源：
CERAMICS INTERNATIONAL | 2017年 / 43卷 / 02期
基金：
中国国家自然科学基金;
关键词：
Thermal barrier coatings (TBCs); Doped YSZ; Hot corrosion; Molten salt; PHYSICAL VAPOR-DEPOSITION; ZIRCONIA COATINGS; PHASE-STABILITY; VANADATE SALT; EB-PVD; BEHAVIOR; YTTRIA; CERAMICS; SULFATE; RESISTANCE;
D O I：
10.1016/j.ceramint.2016.11.109
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
1 mol% Gd2O3 and 1 mol% Yb2O3 co-doped 3.5 mol% Y2O3 stabilized ZrO2 (GdYb-YSZ) ceramics in metastable tetragonal (t') structure were fabricated, and their hot corrosion behaviors were evaluated. The corrosion tests were performed at 700 degrees C, 800 degrees C, 900 degrees C and 1000 degrees C for 4 h in the presence of Na2SO4+V2O5 molten salt. After corrosion, t' phase could still be detected on the corroded surfaces and its content decreased with increasing the corrosion temperature. The corrosion products were composed of doped YVO4 and m-ZrO2, but some amounts of Na4V2O7 were found at low corrosion temperatures (700 degrees C and 800 degrees C). The corrosion resistance characteristic of GdYb-YSZ was compared with that of YSZ. Under an identical corrosion condition, GdYb-YSZ had less monoclinic phase formed, indicative of a better hot corrosion resistance. The hot corrosion mechanism was discussed in detail.
引用
收藏
页码：2780 / 2785
页数：6
相关论文
共 50 条
  • [21] Preparation and conductivity of Yb2O3-Y2O3 and Gd2O3-Y2O3 co-doped zirconia ceramics
    Kan, Yanmei
    Li, Songli
    Wang, Peiling
    Zhang, Guo-Jun
    Van der Biest, Omer
    Vleugels, Jef
    SOLID STATE IONICS, 2008, 179 (27-32) : 1531 - 1534
  • [22] y ZrO2-Sc2O3 Solid Electrolytes Doped with Yb2O3 or Y2O3
    Lomonova, E. E.
    Agarkov, D. A.
    Borik, M. A.
    Eliseeva, G. M.
    Kulebyakin, A. V.
    Kuritsyna, I. E.
    Milovich, F. O.
    Myzina, V. A.
    Osiko, V. V.
    Chislov, A. S.
    Tabachkova, N. Yu.
    RUSSIAN JOURNAL OF ELECTROCHEMISTRY, 2020, 56 (02) : 118 - 123
  • [23] ???????Study on thermal shock resistance of Sc2O3 and Y2O3 co-stabilized ZrO2 thermal barrier coatings
    Dong, Y. S.
    Yan, C. L.
    Li, J.
    Jiang, Z. C.
    Mo, W. L.
    Zhang, Q. J.
    CERAMICS INTERNATIONAL, 2023, 49 (12) : 20034 - 20040
  • [24] Effect of thermal treatment at high temperature on phase stability and transformation of Yb2O3 and Y2O3 co-doped ZrO2 ceramics
    Cao, Zheng
    An, Shengli
    Song, Xiwen
    SCIENTIFIC REPORTS, 2022, 12 (01):
  • [25] Effect of thermal treatment at high temperature on phase stability and transformation of Yb2O3 and Y2O3 co-doped ZrO2 ceramics
    Zheng Cao
    Shengli An
    Xiwen Song
    Scientific Reports, 12 (1)
  • [26] Phase stability, thermal conductivity and crystal growth behavior of RE2O3 (RE = La,Yb,Ce,Gd) co-doped Y2O3 stabilized ZrO2 powder
    Shi, Qingyun
    Yuan, Wuhua
    Chao, Xiongyu
    Zhu, Zhifei
    JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2017, 84 (02) : 341 - 348
  • [27] Phase stability, thermal conductivity and crystal growth behavior of RE2O3 (RE = La,Yb,Ce,Gd) co-doped Y2O3 stabilized ZrO2 powder
    Qingyun Shi
    Wuhua Yuan
    Xiongyu Chao
    Zhifei Zhu
    Journal of Sol-Gel Science and Technology, 2017, 84 : 341 - 348
  • [28] Corrosion of soda lime silicate glasses co-doped with Gd2O3 and Y2O3
    Wang, Mitang
    Li, Mei
    Cheng, Jinshu
    He, Feng
    Liu, Zhaogang
    Hu, Yanhong
    JOURNAL OF NUCLEAR MATERIALS, 2014, 444 (1-3) : 247 - 251
  • [29] Hot corrosion behavior of TiO2 doped, Yb2O3 stabilized zirconia exposed to V2O5 + Na2SO4 molten salt at 700-1000 °C
    Guo, Lei
    Yan, Zheng
    Yu, Jianxing
    Zhang, Chenglong
    Li, Mingzhu
    Ye, Fuxing
    Ji, Vincent
    CERAMICS INTERNATIONAL, 2018, 44 (01) : 261 - 268
  • [30] Effects of sintering additives on hot corrosion behavior of γ-Y2Si2O7 ceramics in Na2SO4+V2O5 molten salt
    Fan, Xingyu
    Sun, Runjun
    Dong, Jie
    Wei, Liang
    Wang, Qiushi
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2021, 41 (01) : 517 - 525
12345