Hot corrosion evaluation of Gd2O3-Yb2O3 co-doped Y2O3 stabilized ZrO2 thermal barrier oxides exposed to Na2SO4+V2O5 molten salt

被引：71

作者：

Guo, Lei ^{[1
,2
,3
]}

Zhang, Chenglong ^{[1
,2
]}

Li, Mingzhu ^{[1
,2
]}

Sun, Wei ^{[1
]}

Zhang, Zhaoyang ^{[1
]}

Ye, Fuxing ^{[1
,2
,3
]}

机构：

[1] Tianjin Univ, Sch Mat Sci & Engn, 92 Weijin Rd, Tianjin 300072, Peoples R China

[2] Tianjin Univ, Tianjin Key Lab Adv Joining Technol, 92 Weijin Rd, Tianjin 300072, Peoples R China

[3] Tianjin Univ, Key Lab Adv Ceram & Machining Technol, Minist Educ, 92 Weijin Rd, Tianjin 300072, Peoples R China

来源：

CERAMICS INTERNATIONAL | 2017年 / 43卷 / 02期

基金：

中国国家自然科学基金;

关键词：

Thermal barrier coatings (TBCs); Doped YSZ; Hot corrosion; Molten salt; PHYSICAL VAPOR-DEPOSITION; ZIRCONIA COATINGS; PHASE-STABILITY; VANADATE SALT; EB-PVD; BEHAVIOR; YTTRIA; CERAMICS; SULFATE; RESISTANCE;

D O I：

10.1016/j.ceramint.2016.11.109

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

1 mol% Gd2O3 and 1 mol% Yb2O3 co-doped 3.5 mol% Y2O3 stabilized ZrO2 (GdYb-YSZ) ceramics in metastable tetragonal (t') structure were fabricated, and their hot corrosion behaviors were evaluated. The corrosion tests were performed at 700 degrees C, 800 degrees C, 900 degrees C and 1000 degrees C for 4 h in the presence of Na2SO4+V2O5 molten salt. After corrosion, t' phase could still be detected on the corroded surfaces and its content decreased with increasing the corrosion temperature. The corrosion products were composed of doped YVO4 and m-ZrO2, but some amounts of Na4V2O7 were found at low corrosion temperatures (700 degrees C and 800 degrees C). The corrosion resistance characteristic of GdYb-YSZ was compared with that of YSZ. Under an identical corrosion condition, GdYb-YSZ had less monoclinic phase formed, indicative of a better hot corrosion resistance. The hot corrosion mechanism was discussed in detail.

引用

页码：2780 / 2785

页数：6

共 50 条

[31] Preparation and properties of Yb2O3-Y2O3- Gd2O3-ZrO2 ceramics for thermal barrier coatings
Sun, Xian-Kai
Wang, Quan-Sheng
Liu, Yan-Bo
Du, Zhong
Zhang, Rui
Rengong Jingti Xuebao/Journal of Synthetic Crystals, 2013, 42 (06): : 1213 - 1216
[32] Y2O3 and Yb2O3 Co-doped Strontium Hafnate as a New Thermal Barrier Coating Material
Ma, Wen
Li, Peng
Dong, Hongying
Bai, Yu
Zhao, Jinlan
Fan, Xiaoze
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2014, 23 (1-2) : 154 - 159
[33] Y2O3 and Yb2O3 Co-doped Strontium Hafnate as a New Thermal Barrier Coating Material
Wen Ma
Peng Li
Hongying Dong
Yu Bai
Jinlan Zhao
Xiaoze Fan
Journal of Thermal Spray Technology, 2014, 23 : 154 - 159
[34] TWEED MICROSTRUCTURE IN Y2O3 STABILIZED ZRO2
HEUER, AH
LANTERI, V
CHAIM, R
JOURNAL OF METALS, 1985, 37 (11): : A58 - A58
[35] Preparation and Phase Stability of La2O3, Y2O3 Co-doped ZrO2 Ceramic Powder Application for Thermal Barrier Coating
Liu Huai-Fei
Li Song-Lin
Li Qi-Lian
Li Yong-Ming
Zhou Wu-Xi
JOURNAL OF INORGANIC MATERIALS, 2009, 24 (06) : 1226 - 1230
[36] Ta2O5/Nb2O5 and Y2O3 co-doped zirconias for thermal barrier coatings
Raghavan, S
Wang, H
Dinwiddie, RB
Porter, WD
Vassen, R
Stöver, D
Mayo, MJ
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2004, 87 (03) : 431 - 437
[37] Luminescence Properties of Ho2O3-Doped Y2O3 Stabilized ZrO2 Single Crystals
Yang, Yuhua
Xu, Shoulei
Li, Siyao
Wu, Wenxia
Pan, Yihua
Wang, Daini
Hong, Xing
Cheng, Zeyu
Deng, Wen
CRYSTALS, 2022, 12 (03)
[38] Ceramics Based on Cubic ZrO2 (Y2O3) with Addition of a Fused Al2O3 – ZrO2 (Y2O3) Eutectic
S. S. Ordan'yan
P. S. Gudovskikh
D. N. Pigunova
Refractories and Industrial Ceramics, 2004, 45 : 1 - 2
[39] Corrosion behavior of Sc2O3-Y2O3 co-stabilized ZrO2 thermal barrier coatings with CMAS attack
Fan, W.
Bai, Y.
Liu, Y. F.
Kang, Y. X.
Wang, Y.
Wang, Z. Z.
Tao, W. Z.
CERAMICS INTERNATIONAL, 2019, 45 (12) : 15763 - 15767
[40] Hot corrosion behavior of nanostructured Gd2O3 doped YSZ thermal barrier coating in presence of Na2SO4 + V2O5 molten salts
Wang, Yixiong
Zhou, Chungen
PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2017, 27 (04) : 507 - 513

← 1 2 3 4 5 →