Fabrication of nanostructured silicon surface using selective chemical etching

A two-stage process based on selective chemical etching induced by metal nanoclusters is used to fabricate nanostructured surfaces of silicon plates with a relatively low reflectance. At silicon surfaces covered with silver nanoclusters, the SERS effect is observed for rhodamine concentrations of about 10(-12) M. At certain technological parameters, the depth of the nanostructured layer weakly depends on the conditions for the two-stage etching, in particular, etching time. Under otherwise equal conditions for etching, the rate of the formation of textured layer in the p-type silicon is two times greater than the formation rate in the n-type silicon.