FRACTURE TEST OF ALUMINUM ALLOY PLATES WITH ELLIPTICAL HOLE

被引：0
|
作者：
Wang, W. Z. [1 ]
Su, R. Q. [2 ]
Ji, H. T. [3 ]
Wang, X. T. [1 ]
机构：
[1] Ningbo Univ, Ningbo, Zhejiang, Peoples R China
[2] Shanxi Railway Inst, Xian, Shaanxi, Peoples R China
[3] Lanzhou Univ Technol, Lanzhou, Gansu, Peoples R China
来源：
PROCEEDINGS OF THE 12TH INTERNATIONAL CONFERENCE ON INSPECTION APPRAISAL REPAIRS AND MAINTENANCE OF STRUCTURES, VOLS 1 AND 2 | 2010年
关键词：
aluminum alloy; plate with hole; crack; fracture mode; MECHANISMS;
D O I：
暂无
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
17 aluminum alloy plates with elliptical hole were tested in the simple tension fracture experiment. The load-displacement curves were recorded accurately. The effect of the ratio of the major axis to the minor axis of elliptical hole on the fracture ductility and fracture mode was studied. The experimental results showed that the macro-crack was initiated at the inner side of the edge of major axis of elliptical hole, and quickly expanded vertically the direction of loading until the specimen fractured. Fracture section was dark gray. Fracture mode was combination of shear and normal fracture. The smaller ratio value was; the higher the fracture ductility was. Fracture load located at the descending branch of load-displacement curve.
引用
收藏
页码：173 / +
页数：2
相关论文
共 50 条
  • [41] Three-dimensional elastic stress fields of finite thickness plates with elliptical hole
    Yang, Zheng
    Cho, Chongdu
    Su, Tingya
    Kim, Chang-Boo
    Beom, Hyeon Gyu
    PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 : 74 - +
  • [42] Damping of structural vibrations in beams and elliptical plates using the acoustic black hole effect
    Georgiev, V. B.
    Cuenca, J.
    Gautier, F.
    Simon, L.
    Krylov, V. V.
    JOURNAL OF SOUND AND VIBRATION, 2011, 330 (11) : 2497 - 2508
  • [43] Study on the surface defect of aluminum alloy hole burnishing
    Liu, Jiahui
    Lin, Xiaoxuan
    Feng, Feng
    Wang, Zibiao
    Zhao, Zirui
    Bai, Zhaoruo
    Zhang, Jianfu
    Feng, Pingfa
    Zhang, Xiangyu
    TRIBOLOGY INTERNATIONAL, 2023, 184
  • [44] Experimental evaluation of fracture properties of aluminum alloy 1050-H14 by small punch test
    The Yen Doan
    Hang Thi Pham
    Khai Quang Le
    Thi-Hang-Nga Nguyen
    Vinh Van Nghiem
    STRENGTH FRACTURE AND COMPLEXITY, 2023, 16 (01) : 61 - 72
  • [45] Experimental and Numerical Fracture Modeling Using XFEM of Aluminum Plates
    Ali, Taghezout
    Mostefa, Bendouba
    Abdelkader, Djebli
    Abdelkrim, Aid
    Habibe, Khellafi
    INTERNATIONAL JOURNAL OF ENGINEERING RESEARCH IN AFRICA, 2020, 46 : 45 - 52
  • [46] A FRACTURE TEST USING CONCENTRICALLY LOADED SQUARE PLATES
    ENTWISTLE, KM
    JOURNAL OF MATERIALS SCIENCE, 1995, 30 (15) : 3773 - 3781
  • [47] Ductile Fracture Prediction in Hole Hemming of Aluminum and Magnesium Sheets
    Kasaei, Mohammad Mehdi
    Pereira, Jose A. C.
    Carbas, Ricardo J. C.
    Marques, Eduardo A. S.
    da Silva, Lucas F. M.
    METALS, 2023, 13 (09)
  • [48] FRACTURE OF FRP PLATES CONTAINING NOTCHES OR A CIRCULAR HOLE UNDER TENSION
    HYAKUTAKE, H
    HAGIO, T
    NISITANI, H
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 1990, 44 (03) : 277 - 290
  • [49] Fracture characteristics of the laser bonding joint between the aluminum alloy and the CFRTP with preset aluminum alloy sheet
    Jiebang Luo
    Hengchang Bu
    Feiyun Wang
    Xiaohong Zhan
    Min Yu
    Dongtao Liu
    The International Journal of Advanced Manufacturing Technology, 2022, 120 : 251 - 263
  • [50] DROPPED OBJECTS PLUGGING CAPACITY OF ALUMINUM-ALLOY PLATES
    LANGSETH, M
    LARSEN, PK
    INTERNATIONAL JOURNAL OF IMPACT ENGINEERING, 1994, 15 (03) : 225 - 241
12345