FRACTURE TEST OF ALUMINUM ALLOY PLATES WITH ELLIPTICAL HOLE

被引：0
|
作者：
Wang, W. Z. [1 ]
Su, R. Q. [2 ]
Ji, H. T. [3 ]
Wang, X. T. [1 ]
机构：
[1] Ningbo Univ, Ningbo, Zhejiang, Peoples R China
[2] Shanxi Railway Inst, Xian, Shaanxi, Peoples R China
[3] Lanzhou Univ Technol, Lanzhou, Gansu, Peoples R China
来源：
PROCEEDINGS OF THE 12TH INTERNATIONAL CONFERENCE ON INSPECTION APPRAISAL REPAIRS AND MAINTENANCE OF STRUCTURES, VOLS 1 AND 2 | 2010年
关键词：
aluminum alloy; plate with hole; crack; fracture mode; MECHANISMS;
D O I：
暂无
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
17 aluminum alloy plates with elliptical hole were tested in the simple tension fracture experiment. The load-displacement curves were recorded accurately. The effect of the ratio of the major axis to the minor axis of elliptical hole on the fracture ductility and fracture mode was studied. The experimental results showed that the macro-crack was initiated at the inner side of the edge of major axis of elliptical hole, and quickly expanded vertically the direction of loading until the specimen fractured. Fracture section was dark gray. Fracture mode was combination of shear and normal fracture. The smaller ratio value was; the higher the fracture ductility was. Fracture load located at the descending branch of load-displacement curve.
引用
收藏
页码：173 / +
页数：2
相关论文
共 50 条
  • [21] Incremental Hole Drilling Residual Stress Measurement in Thin Aluminum Alloy Plates Subjected to Laser Shock Peening
    J. P. Nobre
    C. Polese
    S. N. van Staden
    Experimental Mechanics, 2020, 60 : 553 - 564
  • [22] Elastic-plastic stress analysis and plastic region expansion of clamped aluminum metal-matrix laminated plates with an elliptical hole
    Aktas, A
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2004, 23 (18) : 1997 - 2009
  • [23] Fracture analysis on a cracked elliptical hole with surface effect in magnetoelectroelastic solid
    Xiao, Junhua
    Xu, Bai-Xiang
    Xu, Yaoling
    Zhang, Fucheng
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2020, 107
  • [24] WELDING ALUMINUM AND ALUMINUM-ALLOY TUBES TO TUBE-PLATES
    GRUDZINS.BV
    STEPANOV, GA
    YATSKOV, AP
    WELDING PRODUCTION, 1972, 19 (03): : 36 - &
  • [25] CLEAVAGE FRACTURE OF ALUMINUM PLATES ACCOMPANYING PULSED HEATING
    AKHMADEEV, NK
    SOROKINA, EP
    YAUSHEV, KK
    COMBUSTION EXPLOSION AND SHOCK WAVES, 1983, 19 (05) : 652 - 654
  • [26] Impact delamination and fracture in aluminum/acrylic sandwich plates
    Liaw, BM
    Zeichner, G
    Liu, YX
    PROCEEDINGS OF THE SEM IX INTERNATIONAL CONGRESS ON EXPERIMENTAL MECHANICS, 2000, : 515 - 518
  • [27] Effect of Alloy Purity on Fracture Behavior of Overaged 7000 Alloy Plates
    Cvijovic, Z.
    Vratnica, M.
    Cvijovic-Alagic, I.
    INTERNATIONAL JOURNAL OF DAMAGE MECHANICS, 2011, 20 (02) : 179 - 193
  • [28] Study of Local Cold Working and Tensile Test for 7050 High Strength Aluminum Alloy Hole Plate
    Fan Juan
    Li Fuguo
    Li Jiang
    Wang Shaogang
    RARE METAL MATERIALS AND ENGINEERING, 2012, 41 (06) : 978 - 982
  • [29] Experiments and Simulations on Tensile Properties and Fracture Toughness of 7050-T7451 Aluminum Alloy Hole Specimens
    Xue Fengmei
    Li Fuguo
    Fan Juan
    Li Jiang
    Yuan Zhanwei
    RARE METAL MATERIALS AND ENGINEERING, 2013, 42 (09) : 1767 - 1772
  • [30] IMPROVING THE EFFICIENCY OF THE STRETCHING PROCESS OF ALUMINUM ALLOY PLATES
    Veli, Yelda
    Petre, Marin
    Morega, Alexandru M.
    UPB Scientific Bulletin, Series B: Chemistry and Materials Science, 2023, 85 (02): : 155 - 166
12345