Fatigue crack propagation analysis for micro solder joints with void

被引：0

作者：

Terasaki, Takeshi ^{[1
]}

Tanie, Hisashi ^{[1
]}

机构：

[1] Hitachi Ltd, Mech Engn Res Lab, Hitachi, Ibaraki 3120034, Japan

来源：

EMAP 2005: INTERNATIONAL SYMPOSIUM ON ELECTRONICS MATERIALS AND PACKAGING | 2005年

关键词：

D O I：

暂无

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

Voids in a solder joint can reduce their fatigue life. Voids are caused by the presence of flux in solder paste during reflow soldering, and they are difficult to remove completely. From numerical analysis, we aimed to obtain criteria for evaluating the effect of voids on fatigue life in a solder joint. We investigated crack propagation in the micro-solder joints of a semiconductor and developed a new crack propagation model. In our model, the fatigue life of a solder joint is evaluated based on damage that is accumulated during crack propagation, and crack paths are automatically calculated. The crack-propagation behavior of a center-cracked-plate (CCP) specimen calculated using the new model agreed well with that obtained from measurement. Using our model, we analyzed the effect of positions and sizes of voids on crack paths and the fatigue life of a ball grid array (BGA) structure. The crack paths and the fatigue life were both found to strongly depend on the positions and sizes of voids. We have achieved a reliable method of evaluating the effects of voids in a solder joint.

引用

页码：37 / 42

页数：6

共 50 条

[41] EXPERIMENTAL AND MICROMECHANICS ANALYSIS ON FATIGUE CRACK PROPAGATION BEHAVIOR IN Sn-Ag EUTECTIC SOLDER
Yao, Yao
Vaynman, Semyon
Keer, Leon M.
Fine, Morris E.
[J]. FATIGUE OF MATERIALS: ADVANCES AND EMERGENCES IN UNDERSTANDING, 2010, : 19 - 28
[42] Fatigue crack propagation analysis of tubular K-joints. I: Experimental test
School of Civil Engineering, Yantai University, Yantai 264005, China
不详
[J]. Jisuan Lixue Xuebao, 2007, 5 (643-647):
[43] A method based on a crack propagation model for predicting solder fatigue life
Terasaki, Takeshi
Tanie, Hisashi
[J]. Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 2008, 74 (04): : 574 - 582
[44] Analysis of the uncertainties in time to crack initiation and propagation of fatigue surface cracks in welded joints
Lassen, T
[J]. INTERNATIONAL CONFERENCE ON FATIGUE OF WELDED COMPONENTS AND STRUCTURES, 1996, : 183 - 190
[45] Effect of residual stresses on the fatigue crack propagation in welded joints
Gubeljak, N
Predan, J
Pippan, R
Oblak, M
[J]. Fatigue and Fracture Mechanics, 34th Volume, 2005, (1461): : 281 - 298
[46] Fatigue crack propagation properties of welded joints at 300°C
Ohta, A
Suzuki, N
Maeda, Y
[J]. JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2003, 125 (02): : 131 - 135
[47] Fatigue crack propagation in welded joints X70
Deliou, Adel
Bouchouicha, Benattou
[J]. FRATTURA ED INTEGRITA STRUTTURALE, 2018, (46): : 306 - 318
[48] Stress distribution and fatigue crack propagation analyses in welded joints
Dong, Y.
Guedes Soares, C.
[J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2019, 42 (01) : 69 - 83
[49] Effect of Micro Structure on Fatigue Characteristics of Lead Free Solder Joints
Akutsu, Takahiro
Yu, Qiang
Nishimura, Yuji
[J]. 2010 12TH ELECTRONICS PACKAGING TECHNOLOGY CONFERENCE (EPTC), 2010, : 550 - 555
[50] EFFECT OF MICRO STRUCTURE ON FATIGUE CHARACTERISTICS OF LEAD FREE SOLDER JOINTS
Akutsu, Takahiro
Yu, Qiang
[J]. PROCEEDINGS OF THE ASME PACIFIC RIM TECHNICAL CONFERENCE AND EXHIBITION ON PACKAGING AND INTEGRATION OF ELECTRONIC AND PHOTONIC SYSTEMS, MEMS AND NEMS 2011, VOL 2, 2012, : 691 - 700

← 1 2 3 4 5 →