Growth and characterization of 4H-SiC by horizontal hot-wall CVD

被引：0
|
作者：
Sun, GS [1 ]
Gao, X [1 ]
Wang, L [1 ]
Zhao, WS [1 ]
Zeng, YP [1 ]
Li, JM [1 ]
机构：
[1] Chinese Acad Sci, Inst Semicond, Novel Semicond Mat Lab, Beijing 100083, Peoples R China
来源：
SMIC-XIII: 2004 13th International Conference on Semiconducting & Insulating Materials | 2004年
关键词：
D O I：
暂无
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
4H-SiC layers have been homoepitaxially grown at 1500 degrees C with the use of a horizontal hot-wall chemical vapor deposition (CVD) system, which was built in the author's group. The typical growth rate was 2 mu m/h at a pressure of 40 Torr. The background donor concentration has been reduced to 2.3 x 10(15) cm(-3) during a prolonged growth run. It confirmed the idea that the high background concentration of thin films was caused by the impurities inside the susceptor and thermal insulator The FWHM of x-ray co-rocking curves show 9 similar to 15 aresecs in five different areas of a 32-mu m-thick 4H-SiC epilayer The free exciton peaks dominated in the near-band-edge low-temperature photoluminescence spectrum (LTPL), indicating high crystal quality.
引用
收藏
页码：89 / 92
页数：4
相关论文
共 50 条
  • [41] Etching of 4° and 8° 4H-SiC using various hydrogen-propane mixtures in a commercial hot-wall CVD reactor
    Lew, Kok-Keong
    VanMil, Brenda L.
    Myers-Ward, Rachael L.
    Holm, Ronald T.
    Eddy, Charles R., Jr.
    Gaskill, D. Kurt
    SILICON CARBIDE AND RELATED MATERIALS 2006, 2007, 556-557 : 513 - 516
  • [42] SiC and ill-nitride growth in a hot-wall CVD reactor
    Janzén, E
    Bergman, JP
    Danielsson, Ö
    Forsberg, U
    Hallin, C
    Ul Hassan, J
    Henry, A
    Ivanov, IG
    Kakanakova-Georgieva, A
    Persson, P
    ul Wahab, Q
    SILICON CARBIDE AND RELATED MATERIALS 2004, 2005, 483 : 61 - 66
  • [43] Hot-wall CVD growth of 4H-SiC using Si2Cl6+C 3H8+H2 system
    Miyanagi, Toshiyuki
    Nishino, Shigehiro
    Materials Science Forum, 2002, 389-393 (01) : 199 - 202
  • [44] Fast epitaxial growth of 4H-SiC by chimney-type vertical hot-wall chemical vapor deposition
    Kimoto, T., 1600, Japan Society of Applied Physics (40):
  • [45] Fast epitaxial growth of 4H-SiC by chimney-type vertical hot-wall chemical vapor deposition
    Kimoto, T
    Tamura, S
    Chen, Y
    Fujihira, K
    Matsunami, H
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 2001, 40 (4B): : L374 - L376
  • [46] Etch rates near hot-wall CVD growth temperature for Si-face 4H-SiC using H2 and C3H8
    VanMil, B. L.
    Lew, K-K.
    Myers-Ward, R. L.
    Holm, R. T.
    Gaskill, D. K.
    Eddy, C. R., Jr.
    Wang, L.
    Zhao, P.
    JOURNAL OF CRYSTAL GROWTH, 2009, 311 (02) : 238 - 243
  • [47] High growth rate (up to 20 μm/h) SiC epitaxy in a horizontal hot-wall reactor
    Zhang, J
    Mazzola, J
    Hoff, C
    Koshka, Y
    Casady, J
    SILICON CARBIDE AND RELATED MATERIALS 2004, 2005, 483 : 77 - 80
  • [48] Epitaxial growth of 4H-SIC on 4° off-axis (0001) and (0001) substrates by hot-wall chemical vapor deposition
    Wada, Keiji
    Kimoto, Tsunenobu
    Nishikawa, Kimito
    Matsunami, Hiroyuki
    JOURNAL OF CRYSTAL GROWTH, 2006, 291 (02) : 370 - 374
  • [49] High-voltage (>2.5kV) 4H-SiC Schottky rectifiers processed on hot-wall CVD and high-temperature CVD layers
    Kimoto, T
    Wahab, Q
    Ellison, A
    Forsberg, U
    Tuominen, M
    Yakimova, R
    Henry, A
    Janzen, E
    SILICON CARBIDE, III-NITRIDES AND RELATED MATERIALS, PTS 1 AND 2, 1998, 264-2 : 921 - 924
  • [50] CVD epitaxial growth of 4H-SiC on porous SiC substrates
    Shishkin, Y.
    Ke, Yue
    Yan, Fei
    Devaty, R. P.
    Choyke, W. J.
    Saddow, S. E.
    SILICON CARBIDE AND RELATED MATERIALS 2005, PTS 1 AND 2, 2006, 527-529 : 255 - 258
12345