Growth and characterization of 4H-SiC by horizontal hot-wall CVD

被引：0
|
作者：
Sun, GS [1 ]
Gao, X [1 ]
Wang, L [1 ]
Zhao, WS [1 ]
Zeng, YP [1 ]
Li, JM [1 ]
机构：
[1] Chinese Acad Sci, Inst Semicond, Novel Semicond Mat Lab, Beijing 100083, Peoples R China
来源：
SMIC-XIII: 2004 13th International Conference on Semiconducting & Insulating Materials | 2004年
关键词：
D O I：
暂无
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
4H-SiC layers have been homoepitaxially grown at 1500 degrees C with the use of a horizontal hot-wall chemical vapor deposition (CVD) system, which was built in the author's group. The typical growth rate was 2 mu m/h at a pressure of 40 Torr. The background donor concentration has been reduced to 2.3 x 10(15) cm(-3) during a prolonged growth run. It confirmed the idea that the high background concentration of thin films was caused by the impurities inside the susceptor and thermal insulator The FWHM of x-ray co-rocking curves show 9 similar to 15 aresecs in five different areas of a 32-mu m-thick 4H-SiC epilayer The free exciton peaks dominated in the near-band-edge low-temperature photoluminescence spectrum (LTPL), indicating high crystal quality.
引用
收藏
页码：89 / 92
页数：4
相关论文
共 50 条
  • [31] Improved surface morphology and background doping concentration in 4H-SiC(000-1) epitaxial growth by hot-wall CVD
    Wada, A
    Kimoto, T
    Nishikawa, K
    Matsunami, H
    SILICON CARBIDE AND RELATED MATERIALS 2004, 2005, 483 : 85 - 88
  • [32] Growth characteristics of SiC in a hot-wall CVD reactor with rotation
    Zhang, J
    Forsberg, U
    Isacson, M
    Ellison, A
    Henry, A
    Kordina, O
    Janzén, E
    JOURNAL OF CRYSTAL GROWTH, 2002, 241 (04) : 431 - 438
  • [33] Homoepitaxial growth and characterization of 4H-SiC epilayers by low-pressure hot-wall chemical vapor deposition
    Sun, Guosheng
    Ning, Jin
    Gong, Quancheng
    Gao, Xin
    Wang, Lei
    Liu, Xingfang
    Zeng, Yiping
    Li, Jinmin
    SILICON CARBIDE AND RELATED MATERIALS 2005, PTS 1 AND 2, 2006, 527-529 : 191 - +
  • [34] High-Quality 4H-SiC Homogeneous Epitaxy via Homemade Horizontal Hot-Wall Reactor
    Gong, Xiaoliang
    Xie, Tianle
    Hu, Fan
    Li, Ping
    Ba, Sai
    Wang, Liancheng
    Zhu, Wenhui
    COATINGS, 2024, 14 (07)
  • [35] Hot-wall CVD growth of 4H-SiC using Si2Cl6+C3H8+H2 system
    Miyanagi, T
    Nishino, S
    SILICON CARBIDE AND RELATED MATERIALS 2001, PTS 1 AND 2, PROCEEDINGS, 2002, 389-3 : 199 - 202
  • [36] Influence of the growth conditions on the layer parameters of 4H-SiC epilayers grown in a hot-wall reactor
    Wagner, G
    Irmscher, K
    SILICON CARBIDE AND RELATED MATERIALS, ECSCRM2000, 2001, 353-356 : 95 - 98
  • [37] High-purity 4H-SiC epitaxial growth by hot-wall chemical vapor deposition
    Nakazawa, S
    Kimoto, T
    Hashimoto, K
    Matsunami, H
    JOURNAL OF CRYSTAL GROWTH, 2002, 237 (1-4 II) : 1213 - 1218
  • [38] Epitaxial growth of 4H-SiC in a vertical hot-wall CVD reactor:: Comparison between up- and down-flow orientations
    Zhang, J
    Ellison, A
    Danielsson, Ö
    Henry, A
    Janzén, E
    SILICON CARBIDE AND RELATED MATERIALS, ECSCRM2000, 2001, 353-356 : 91 - 94
  • [39] Epitaxial growth of 4H-SiC in a vertical hot-wall CVD reactor: comparison between up- and down-flow orientations
    Zhang, J.
    Ellison, A.
    Danielsson, Ö.
    Henry, A.
    Janzén, E.
    Materials Science Forum, 2001, 353-356 : 91 - 94
  • [40] High uniform N-type doping of 4H-SiC homoepitaxy based on a horizontal hot-wall reactor
    Gong, Xiaoliang
    Li, Ping
    Xie, Tianle
    Hu, Fan
    Ba, Sai
    Wang, Liancheng
    Zhu, Wenhui
    JOURNAL OF CRYSTAL GROWTH, 2024, 648
12345