Fretting fatigue and friction of quenched and tempered steel in dry contact with aluminum bronze

被引：7
|
作者：
Hintikka, Jouko [1 ]
Lehtovaara, Arto [1 ]
Mantyla, Antti [2 ]
机构：
[1] Tampere Univ Technol, Dept Mech & Design, FIN-33101 Tampere, Finland
[2] Wartsila Finland Oy, Res & Dev, Vaasa 65101, Finland
来源：
WEAR | 2013年 / 308卷 / 1-2期
关键词：
Fretting fatigue; Quenched and tempered steel; Bronze; Partial slip; Gross sliding; CRACK INITIATION; BEHAVIOR; PREDICTION; WEAR;
D O I：
10.1016/j.wear.2013.07.002
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Bronze-steel contacts are common in machinery where the loading might give rise to fretting conditions. The flat surfaces of the quenched and tempered steel (QT) specimens were fretted with aluminum bronze spheres in partial slip and gross sliding conditions. The dry friction coefficient was around unity in gross sliding. Material transfer occurred from bronze pad to the QT-specimen and cracks initiated at these locations. Fretting map comparisons with QT-QT fretting tests showed that aluminum bronze-QT contact produces fatigue cracks with lower values in terms of displacement amplitude, tangential force amplitude and Findley cracking risk. (C) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码：155 / 165
页数：11
相关论文
共 50 条
  • [1] On the fretting fatigue behavior of quenched and tempered steel in smooth point contact
    Pasanen, A.
    Lehtovaara, A.
    Rabb, R.
    Riihimäki, P.
    Tribologia, 2009, 28 (3-4): : 26 - 37
  • [2] Friction behavior of quenched and tempered steel in partial and gross slip conditions in fretting point contact
    Pasanen, A.
    Lehtovaara, A.
    Rabb, R.
    Riihimaki, P.
    WEAR, 2009, 267 (12) : 2200 - 2207
  • [3] Non-Coulomb friction in gross sliding fretting conditions with aluminium bronze against quenched and tempered steel
    Hintikka, Jouko
    Lehtovaara, Arto
    Mantyla, Antti
    TRIBOLOGY INTERNATIONAL, 2014, 79 : 151 - 161
  • [4] Fretting-induced friction and wear in large flat-on-flat contact with quenched and tempered steel
    Hintikka, Jouko
    Lehtovaara, Arto
    Mantyla, Antti
    TRIBOLOGY INTERNATIONAL, 2015, 92 : 191 - 202
  • [5] Third Particle Ejection Effects on Wear with Quenched and Tempered Steel Fretting Contact
    Hintikka, Jouko
    Lehtovaara, Arto
    Mantyla, Antti
    TRIBOLOGY TRANSACTIONS, 2017, 60 (01) : 70 - 78
  • [6] An insight into the effect of rough surfaces and contact orientation on the fretting characteristics of quenched and tempered steel
    Zabihi, A.
    Juoksukangas, J.
    Hintikka, J.
    Honkanen, M.
    Mantyla, A.
    Vaara, J.
    Frondelius, T.
    Vippola, M.
    TRIBOLOGY INTERNATIONAL, 2023, 189
  • [7] THE EFFECT OF FRETTING AND ENVIRONMENT ON FATIGUE CRACK INITIATION AND EARLY PROPAGATION IN A QUENCHED AND TEMPERED 4130 STEEL
    GAUL, DJ
    DUQUETTE, DJ
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1980, 11 (09): : 1555 - 1561
  • [8] Analysis on internal friction in quenched and tempered hot work steel
    Xue, Chang
    Wang, Hong-Bin
    Wu, Xiao-Chun
    Song, Wen-Wen
    Shanghai Jiaotong Daxue Xuebao/Journal of Shanghai Jiaotong University, 2010, 44 (05): : 640 - 644
  • [9] PARAMETER OPTIMIZATION AND PROPERTIES OF FRICTION WELDED QUENCHED AND TEMPERED STEEL
    RAJAMANI, GP
    SHUNMUGAM, MS
    RAO, KP
    WELDING JOURNAL, 1992, 71 (06) : S225 - S230
  • [10] Fatigue strength of friction-welded joints of aluminum bronze to stainless steel
    Ochi, Hiizu
    Isshiki, Yoshihiro
    Kawai, Gosaku
    STRENGTH FRACTURE AND COMPLEXITY, 2020, 13 (02) : 81 - 90
12345