Fabrication of Al/Al2O3 composites and FGM

被引：0

作者：

Tao, H ^{[1
]}

Deng, CJ ^{[1
]}

Zhang, LM ^{[1
]}

Yuan, RZ ^{[1
]}

机构：

[1] Wuhan Univ Technol, State Key Lab Adv Technol Mat Synth & Proc, Wuhan 430070, Peoples R China

来源：

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY | 2001年 / 17卷 / 06期

关键词：

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Al/Al2O3 composites of different ratios were hot-press sintered at 575 similar to 640 degreesC under a pressure of 30 MPa for 2 h in a vacuum furnace. It was found that the relative density of the Al/Al2O3 composites could be increased evidently with the rise of sinter temperature. No reaction occurred between Al and Al2O3 at the sinter temperatures. Under 640 degreesC-30 MPa-2 h experimental condition, Al/Al2O3 system FGM was successfully fabricated, and its density range changed quasi-continuously from 2.887x10(3) kg/m(3) to 3.1909x10(3) kg/m3 within the middle 1.0 mm thickness range.

引用

页码：646 / 648

页数：3

共 50 条

[41] The Influence of Al2O3 Powder Morphology on the Properties of Cu-Al2O3 Composites Designed for Functionally Graded Materials (FGM)
Strojny-Nedza, Agata
Pietrzak, Katarzyna
Weglewski, Witold
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2016, 25 (08) : 3173 - 3184
[42] The Influence of Al2O3 Powder Morphology on the Properties of Cu-Al2O3 Composites Designed for Functionally Graded Materials (FGM)
Agata Strojny-Nędza
Katarzyna Pietrzak
Witold Węglewski
Journal of Materials Engineering and Performance, 2016, 25 : 3173 - 3184
[43] Fabrication and optical properties of nanostructured plasmonic Al2O3/Au-Al2O3/Al2O3 metamaterials
Bakkali, H.
Blanco, E.
Dominguez, M.
Garitaonandia, J. S.
NANOTECHNOLOGY, 2017, 28 (33)
[44] Effect of γ-Al2O3 content on the thermoelectric performance of ZrNiSn/γ-Al2O3 composites
Huang, XY
Xu, Z
Chen, LD
Tang, XF
COMPOSITE MATERIALS III, 2003, 249 : 79 - 82
[45] Fabrication and Characterization of Functionally Graded Nanomaterials (Al/Al2O3) and (Al/Ni/Al2O3) using the Sputtering Technique
Sadek, Engy M.
Mohamed, Lamiaa Z.
El-Kashif, Emad F.
Abdelfatah, Aliaa
EGYPTIAN JOURNAL OF CHEMISTRY, 2024, 67 (07): : 233 - 249
[46] Microstructure of in-situ Al2O3/Al composites
Ji, Y
Zhong, TX
Wang, Y
Tang, JH
Xu, XD
JOURNAL OF TRACE AND MICROPROBE TECHNIQUES, 1997, 15 (04): : 489 - 492
[47] BRAIDED AL2O3/AL-LI COMPOSITES
MAJIDI, AP
YANG, JM
CHOU, TW
JOURNAL OF METALS, 1986, 38 (03): : 27 - 27
[48] In situ fabrication of α-Al2O3 and Ni2Al3 reinforced aluminum matrix composites in an Al-Ni2O3 system
Zhu, Heguo
Ai, Yinglu
Li, Jianliang
Min, Jing
Chu, Da
Zhao, Jun
Chen, Jie
ADVANCED POWDER TECHNOLOGY, 2011, 22 (05) : 629 - 633
[49] FABRICATION AND PROPERTIES OF AL2O3-FIBER-REINFORCED AL2O3
LEWIS, D
CONGDON, JW
AMERICAN CERAMIC SOCIETY BULLETIN, 1977, 56 (03): : 313 - 313
[50] MICROSTRUCTURAL OBSERVATIONS OF PRESSURE CAST NI3AL/AL2O3 AND NI/AL2O3 COMPOSITES
NOURBAKHSH, S
MARGOLIN, H
LIANG, FL
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (10): : 2159 - 2166

← 1 2 3 4 5 →