Fabrication of Al/Al2O3 composites and FGM

被引：0

作者：

Tao, H ^{[1
]}

Deng, CJ ^{[1
]}

Zhang, LM ^{[1
]}

Yuan, RZ ^{[1
]}

机构：

[1] Wuhan Univ Technol, State Key Lab Adv Technol Mat Synth & Proc, Wuhan 430070, Peoples R China

来源：

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY | 2001年 / 17卷 / 06期

关键词：

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Al/Al2O3 composites of different ratios were hot-press sintered at 575 similar to 640 degreesC under a pressure of 30 MPa for 2 h in a vacuum furnace. It was found that the relative density of the Al/Al2O3 composites could be increased evidently with the rise of sinter temperature. No reaction occurred between Al and Al2O3 at the sinter temperatures. Under 640 degreesC-30 MPa-2 h experimental condition, Al/Al2O3 system FGM was successfully fabricated, and its density range changed quasi-continuously from 2.887x10(3) kg/m(3) to 3.1909x10(3) kg/m3 within the middle 1.0 mm thickness range.

引用

页码：646 / 648

页数：3

共 50 条

[31] Design and preparation of Al2TiO5/Al2O3 FGM
Zhang, LM
Shen, Q
Fang, Q
Li, MZ
FUNCTIONALLY GRADED MATERIALS VII, 2003, 423-4 : 187 - 190
[32] FABRICATION AND PROPERTIES OF BA-MICA/AL2O3 COMPOSITES
MCCAULEY, JW
AMERICAN CERAMIC SOCIETY BULLETIN, 1972, 51 (04): : 434 - &
[33] Fabrication and mechanical properties of Al2O3 reinforced NiAl composites
Hwang, CS
Coo, DL
COMPOSITE MATERIALS III, 2003, 249 : 223 - 226
[34] Fabrication of Ti/Al2O3 composites by spark plasma sintering
Wang, Z
Li, ML
Shen, Q
Zhang, LM
COMPOSITE MATERIALS III, 2003, 249 : 137 - 140
[35] Fabrication of Ni-MF/Al2O3 Ceramic Composites
Xing Guohong
Wang Zhi
Liu Jianfei
Shi Guopu
MULTI-FUNCTIONAL MATERIALS AND STRUCTURES II, PTS 1 AND 2, 2009, 79-82 : 751 - 754
[36] FABRICATION AND PROPERTIES OF FUNCTIONALLY GRADED NIAL AL2O3 COMPOSITES
MILLER, DP
LANNUTTI, JJ
NOEBE, RD
JOURNAL OF MATERIALS RESEARCH, 1993, 8 (08) : 2004 - 2013
[37] SLIP CASTING OF AL2O3 AND AL2O3/ZRO2 COMPOSITES
BELLOSI, A
GALASSI, C
GUICCIARDI, S
JOURNAL OF MATERIALS SCIENCE, 1990, 25 (10) : 4331 - 4340
[38] MECHANICAL-PROPERTIES OF AL/AL2O3 AND CU/AL2O3 COMPOSITES WITH INTERPENETRATING NETWORKS
KNECHTEL, M
PRIELIPP, H
MULLEJANS, H
CLAUSSEN, N
RODEL, J
SCRIPTA METALLURGICA ET MATERIALIA, 1994, 31 (08): : 1085 - 1090
[39] Microwave reflection characteristics of the Fe/Al2O3 and Fe3Al/Al2O3 composites
Wei, Jianqiang
Wang, Jianbo
Qiao, Liang
Wang, Tao
Li, Fashen
MATERIALS SCIENCE AND ENGINEERING APPLICATIONS, PTS 1-3, 2011, 160-162 : 984 - 989
[40] Mechanomaking of Fe/Al2O3 and FeCr/Al2O3 nanocomposites powders fabrication
Matteazzi, P
Alcala, M
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 230 (1-2): : 161 - 170

← 1 2 3 4 5 →