Fabrication of Al/Al2O3 composites and FGM

被引：0

作者：

Tao, H ^{[1
]}

Deng, CJ ^{[1
]}

Zhang, LM ^{[1
]}

Yuan, RZ ^{[1
]}

机构：

[1] Wuhan Univ Technol, State Key Lab Adv Technol Mat Synth & Proc, Wuhan 430070, Peoples R China

来源：

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY | 2001年 / 17卷 / 06期

关键词：

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Al/Al2O3 composites of different ratios were hot-press sintered at 575 similar to 640 degreesC under a pressure of 30 MPa for 2 h in a vacuum furnace. It was found that the relative density of the Al/Al2O3 composites could be increased evidently with the rise of sinter temperature. No reaction occurred between Al and Al2O3 at the sinter temperatures. Under 640 degreesC-30 MPa-2 h experimental condition, Al/Al2O3 system FGM was successfully fabricated, and its density range changed quasi-continuously from 2.887x10(3) kg/m(3) to 3.1909x10(3) kg/m3 within the middle 1.0 mm thickness range.

引用

页码：646 / 648

页数：3

共 50 条

[21] Fabrication and Microstructure of the Fe3Al/Al2O3 Composites by Pressureless Sintering
Jiang, Tao
Pan, Kewei
TESTING AND EVALUATION OF INORGANIC MATERIALS I, 2011, 177 : 411 - 414
[22] FABRICATION OF MICROLAMINATED AL/AL2O3 COMPOSITES BY MAGNETRON SPUTTERING FOR TRIBOLOGICAL APPLICATIONS
DING, Y
NORTHWOOD, DO
ALPAS, AT
SURFACE & COATINGS TECHNOLOGY, 1993, 62 (1-3): : 448 - 453
[23] Fabrication of Al/Al2O3 composites by in-situ powder metallurgy (IPM)
Pournaderi, S.
Mahdavi, S.
Akhlaghi, F.
POWDER TECHNOLOGY, 2012, 229 : 276 - 284
[24] Quantitative analysis of Al2O3 particles in Al3Ti/Al2O3/Al composites
Swiderska-Sroda, A
Wejrzanowski, T
Kurzydlowski, KJ
Wyrzykowski, JW
MATERIALS CHARACTERIZATION, 2003, 51 (2-3) : 141 - 146
[25] Fabrication and thermal properties of Al2TiO5/Al2O3 composites
Li, M.
Chen, F.
Shen, Q.
Zhang, L.
MATERIALS SCIENCE-POLAND, 2010, 28 (03): : 663 - 670
[26] Sintering behaviour and microstructures of Ti(Al,O)/Al2O3, Ti3Al(O)/Al2O3 and TiAl(O)/Al2O3 in situ composites
Cai, ZH
Zhang, DL
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 419 (1-2): : 310 - 317
[27] TOUGHENING IN COMPOSITES OF AL2O3 REINFORCED WITH AL
FLINN, BD
RUHLE, M
EVANS, AG
ACTA METALLURGICA, 1989, 37 (11): : 3001 - 3006
[28] BIMODAL SINTERING OF AL2O3/AL2O3 PLATELET CERAMIC COMPOSITES
BELMONTE, M
MOYA, JS
MIRANZO, P
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1995, 78 (06) : 1661 - 1667
[29] Processing and characterization of Al2O3 and Al2O3/Cu alloy composites
McCuiston, RC
Danforth, SC
Niesz, DE
ELECTROACTIVE POLYMERS AND RAPID PROTOTYPING, 2002, 698 : 257 - 261
[30] Bimodal sintering of Al2O3/Al2O3 platelet ceramic composites
Instituto de Ceramica y Vidrio, Madrid, Spain
J Am Ceram Soc, 6 (1661-1667):

← 1 2 3 4 5 →