Effect of temperature on corrosion fatigue behavior of Inconel Alloy 690TT steam generator tube

被引：7
|
作者：
Li, Z. H. [1 ]
Lu, Y. H. [1 ]
You, L. [2 ]
Zhang, X. F. [1 ]
Wang, L. [2 ]
Tian, D. H. [1 ]
Zhang, W. D. [1 ]
Shoji, T. [1 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
[2] State Key Lab Nucl Power Safety Monitoring Technol, Shenzhen 518172, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 227卷
关键词：
Alloy 690TT tube; Corrosion fatigue; Temperature; Crack initiation; Fatigue life; CRACK-GROWTH-BEHAVIOR; LOW-CYCLE FATIGUE; DISSOLVED-OXYGEN; STAINLESS-STEEL; TIN INCLUSION; MECHANISMS;
D O I：
10.1016/j.corsci.2023.111741
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of temperature on corrosion fatigue behavior of actual Alloy 690TT steam generator (SG) tubes in water environments was studied. Results demonstrated that temperature had significant influence on the for-mation and initiation mechanism of persistent slip bands (PSBs), as well as the crack propagation mode and mechanism, in water environment. With the increase of temperature, the corrosion fatigue life of SG tube decreased, more fatigue cracks initiated along the PSBs, and the synergistic effect of slip dissolution and local plasticity accelerated fatigue crack propagation. Then, the evaluation model of temperature on corrosion fatigue life was established.
引用
收藏
页数：12
相关论文
共 50 条
  • [31] Inconel 690 is alloy of choice for steam generator tubing
    Strauss, SD
    POWER, 1996, 140 (02) : 29 - &
  • [32] The impact fretting corrosion behavior and damage mechanism of Inconel 690TT under different impact forces in high temperature pressurized water
    Bian, W. W.
    Lu, Y. H.
    Kang, L. Z.
    Zhang, X. F.
    Xin, L.
    Shoji, T.
    CORROSION SCIENCE, 2024, 240
  • [33] Numerical Prediction of Maximum Load-Carrying Capacity of Cracked Alloy 690TT Steam Generator Tubes
    Jeon, Jun-Young
    Kim, Yun-Jae
    Kim, Jin-Weon
    Lee, Kuk-Hee
    Kim, Jong-Sung
    JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2016, 138 (04):
  • [34] Effect of Applied Potential and Inhibitors on PbSCC of Alloy 690TT
    Capell, Brent
    Lumsden, Jesse
    Calabrese, Michael
    Eaker, Rick
    PROCEEDINGS OF THE 18TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS - WATER REACTORS, VOL 2, 2018, : 1129 - 1144
  • [35] The single effect of microstructure, residual strain and geometric structure on the stress corrosion cracking behavior of scratched alloy 690TT
    Wu, Bin
    Ming, Hongliang
    Li, Rongbo
    Meng, Fanjiang
    Wang, Jianqiu
    Han, En-Hou
    CORROSION SCIENCE, 2024, 227
  • [36] Effect of the triangular prism dent on stress corrosion cracking behavior of alloy 690TT heat transfer tube in a lead-containing alkaline solution
    Ding, Yun
    Yuan, Sui
    Wu, Renquan
    Wei, Shichen
    Wang, Shuo
    Xu, Jian
    Yu, Hongying
    Sun, Dongbai
    JOURNAL OF NUCLEAR MATERIALS, 2024, 594
  • [37] Role of TiN inclusion on corrosion fatigue behavior of Alloy 690 steam generator tubes in borated and lithiated high temperature water
    Tan, Jibo
    Wu, Xinqiang
    Han, En-Hou
    Ke, Wei
    Liu, Xiaoqiang
    Meng, Fanjiang
    Xu, Xuelian
    CORROSION SCIENCE, 2014, 88 : 349 - 359
  • [38] Effect of fretting wear regimes on stress corrosion cracking of Alloy 690TT in high-temperature pressurized water
    Bian, W. W.
    Lu, Y. H.
    Zhang, X. F.
    Han, Y. M.
    Wang, F.
    Shoji, T.
    CORROSION SCIENCE, 2024, 237
  • [39] Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steelin Pure Water
    Xing-Chen Liu
    Hong-Liang Ming
    Zhi-Ming Zhang
    Jian-Qiu Wang
    Li-Chen Tang
    Hao Qian
    Yong-Cheng Xie
    En-Hou Han
    ActaMetallurgicaSinica(EnglishLetters), 2019, 32 (12) : 1437 - 1448
  • [40] Effects of lead on oxidation behavior of Alloy 690TT within a high temperature aqueous environment
    Hou, Qiang
    Liu, Zhiyong
    Li, Chengtao
    Li, Xiaogang
    APPLIED SURFACE SCIENCE, 2017, 426 : 514 - 526
12345