The impact fretting corrosion behavior and damage mechanism of Inconel 690TT under different impact forces in high temperature pressurized water

被引：0
|
作者：
Bian, W. W. [1 ]
Lu, Y. H. [1 ]
Kang, L. Z. [1 ]
Zhang, X. F. [1 ]
Xin, L. [1 ]
Shoji, T. [1 ,2 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
[2] Tohoku Univ, New Ind Creat Hatchery Ctr, Frontier Res Initiat, 6-6-10 Aramaki Aoba,Aoba Ku, Sendai, Miyagi 9808579, Japan
来源：
CORROSION SCIENCE | 2024年 / 240卷
基金：
中国国家自然科学基金;
关键词：
Inconel; 690; TT; Impact fretting corrosion; Oxidation; Microstructure; SURFACE OXIDE-FILMS; WEAR BEHAVIOR; DYNAMIC RECRYSTALLIZATION; NANOLAMINATED STRUCTURE; ALLOY; 690TT; DEFORMATION; TUBES; SUPERALLOY; EVOLUTION; DIFFUSION;
D O I：
10.1016/j.corsci.2024.112507
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The impact fretting corrosion of Inconel 690TT under different impact forces was investigated. The results indicated that there was a competitive relationship between formation of third body layer (TBL) and fragmentation of TBL caused by impact force. With the increase of impact forces, damage mechanism changed from adhesive wear to delamination wear, and crack initiation sites gradually shifted from TBL to internal oxidation zone in tribologically transformed structure (TTS) layer. Nanocrystalline boundaries and defects induced by impact force provided channels for internal oxidation. The formation mechanism of TTS was the combined effect of continuous dynamic recrystallization (cDRX) and twin-assisted cDRX.
引用
收藏
页数：19
相关论文
共 50 条
  • [1] Corrosion fatigue damage mechanism and life evaluation of Inconel Alloy 690TT steam generator tube in high temperature pressurized water
    Li, Z. H.
    Lu, Y. H.
    Hong, C.
    Zhao, Y. G.
    Han, Y. M.
    Shoji, T.
    CORROSION SCIENCE, 2023, 212
  • [2] Sequence and mechanism of early microstructure evolution in alloy 690TT subjected to fretting corrosion in high temperature pressurized water
    Bian, W. W.
    Lu, Y. H.
    Kang, L. Z.
    Han, Y. M.
    Xin, L.
    Liu, X.
    Shoji, T.
    CORROSION SCIENCE, 2023, 221
  • [3] Study of fretting wear behavior of 690TT heat exchanger tube under three fretting regimes in high temperature pressurized water
    Zhang, Yusheng
    Wang, Shuji
    Ming, Hongliang
    Wang, Jianqiu
    Han, En-Hou
    JOURNAL OF NUCLEAR MATERIALS, 2025, 605
  • [4] The effect of NaCl concentration on impact-sliding fretting corrosion behavior of Inconel 690TT heat transfer tubes
    Li, Yinghong
    Tan, Wei
    Pei, Wenjie
    Zhu, Guorui
    ANTI-CORROSION METHODS AND MATERIALS, 2024, 71 (05) : 464 - 481
  • [5] Microstructural characteristics of Alloy 690TT subjected to fretting corrosion in high temperature water
    Xin, Long
    Yang, Beibei
    Li, Jie
    Lu, Yonghao
    Shoji, Tetsuo
    CORROSION SCIENCE, 2017, 123 : 116 - 128
  • [6] Effect of fretting wear regimes on stress corrosion cracking of Alloy 690TT in high-temperature pressurized water
    Bian, W. W.
    Lu, Y. H.
    Zhang, X. F.
    Han, Y. M.
    Wang, F.
    Shoji, T.
    CORROSION SCIENCE, 2024, 237
  • [7] Effect of normal force on fretting wear behavior and mechanism of Alloy 690TT in high temperature water
    Xin, L.
    Yang, B. B.
    Wang, Z. H.
    Li, J.
    Lu, Y. H.
    Shoji, T.
    WEAR, 2016, 368 : 210 - 218
  • [8] Effect of the cycle number on fretting wear behavior of alloy 690TT tube in high-temperature pressurized water
    Bian, W. W.
    Hong, C.
    Xin, L.
    Kang, L. Z.
    Han, Y. M.
    Liu, H.
    Shoji, T.
    Lu, Y. H.
    JOURNAL OF NUCLEAR MATERIALS, 2022, 567
  • [9] Effect of the frequency on fretting corrosion behavior between Alloy 690TT tube and 405 stainless steel plate in high temperature pressurized water
    Zhang, Yusheng
    Ming, Hongliang
    Tang, Lichen
    Wang, Jianqiu
    Qian, Hao
    Han, En-Hou
    TRIBOLOGY INTERNATIONAL, 2021, 164
  • [10] The Evolution of Fretting Wear Behavior and Damage Mechanism in Alloy 690TT with Cycle Number
    Xin, Long
    Han, Yongming
    Ling, Ligong
    Zhang, Weidong
    Lu, Yonghao
    Shoji, Tetsuo
    MATERIALS, 2020, 13 (10)
12345