The impact fretting corrosion behavior and damage mechanism of Inconel 690TT under different impact forces in high temperature pressurized water

被引：0
|
作者：
Bian, W. W. [1 ]
Lu, Y. H. [1 ]
Kang, L. Z. [1 ]
Zhang, X. F. [1 ]
Xin, L. [1 ]
Shoji, T. [1 ,2 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
[2] Tohoku Univ, New Ind Creat Hatchery Ctr, Frontier Res Initiat, 6-6-10 Aramaki Aoba,Aoba Ku, Sendai, Miyagi 9808579, Japan
来源：
CORROSION SCIENCE | 2024年 / 240卷
基金：
中国国家自然科学基金;
关键词：
Inconel; 690; TT; Impact fretting corrosion; Oxidation; Microstructure; SURFACE OXIDE-FILMS; WEAR BEHAVIOR; DYNAMIC RECRYSTALLIZATION; NANOLAMINATED STRUCTURE; ALLOY; 690TT; DEFORMATION; TUBES; SUPERALLOY; EVOLUTION; DIFFUSION;
D O I：
10.1016/j.corsci.2024.112507
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The impact fretting corrosion of Inconel 690TT under different impact forces was investigated. The results indicated that there was a competitive relationship between formation of third body layer (TBL) and fragmentation of TBL caused by impact force. With the increase of impact forces, damage mechanism changed from adhesive wear to delamination wear, and crack initiation sites gradually shifted from TBL to internal oxidation zone in tribologically transformed structure (TTS) layer. Nanocrystalline boundaries and defects induced by impact force provided channels for internal oxidation. The formation mechanism of TTS was the combined effect of continuous dynamic recrystallization (cDRX) and twin-assisted cDRX.
引用
收藏
页数：19
相关论文
共 50 条
  • [41] Investigation into the fretting corrosion of alloy 690 TT against type 304 stainless steel in high temperature pure water under partial slip conditions
    Xin, Long
    Liang, Xue
    Han, Yongming
    Lu, Yonghao
    Shoji, Tetsuo
    TRIBOLOGY INTERNATIONAL, 2019, 134 : 93 - 101
  • [42] Effects of Hydrogen Contents on Oxidation Behavior of Alloy 690TT and Associated Boron Accumulation within Oxides in High-Temperature Water
    Jeon, Soon-Hyeok
    Song, Geun Dong
    Hur, Do Haeng
    SCANNING, 2018,
  • [43] Fretting corrosion running regime and damage mechanism evolution of zirconium alloy mated with Inconel 718 alloy in high temperature high pressure water environment
    Kang, L. Z.
    Lu, Y. H.
    Bian, W. W.
    Xin, L.
    Han, Y. M.
    TRIBOLOGY INTERNATIONAL, 2024, 194
  • [44] Fretting wear between Alloy 690 and 405 stainless steel in high temperature pressurized water with different normal force and displacement
    Ming, Hongliang
    Liu, Xingchen
    Lai, Jiang
    Wang, Jianqiu
    Gao, Lixia
    Han, En-Hou
    JOURNAL OF NUCLEAR MATERIALS, 2020, 529
  • [45] CORROSION BEHAVIOR OF NUCLEAR GRADE ALLOYS 690 AND 800 IN SIMULATED HIGH TEMPERATURE AND HIGH PRESSURE PRIMARY WATER OF PRESSURIZED WATER REACTOR
    Li Xiaohui
    Wang Jianqiu
    Han En-Hou
    Ke Wei
    ACTA METALLURGICA SINICA, 2012, 48 (08) : 941 - 950
  • [46] The role of normal force on the fretting corrosion behaviour of alloy 690 TT tube against 410 stainless steel plate in high temperature high pressure water
    Wang, Shicheng
    Deng, Xiaoyun
    You, Lei
    Hu, Kangkai
    Ren, Lu
    Gao, Wei
    Xu, Jian
    Yu, Hongying
    Sun, Dongbai
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 26 : 6162 - 6181
  • [47] Dynamic corrosion properties of impact-fretting wear in high-temperature pure water
    Sato, Y.
    Iwabuchi, A.
    Uchidate, M.
    Yashiro, H.
    WEAR, 2015, 330 : 182 - 192
  • [48] Wear damage resulting from sliding impact kinematics in pressurized high temperature water: energetical and statistical approaches
    Kaiser, Anne-Laure
    Bec, Sandrine
    Vernot, Jean-Philippe
    Langlade, Cecile
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2006, 39 (15) : 3193 - 3199
  • [49] Fretting corrosion behavior and microstructure evolution of hydrided zirconium alloy under gross slip regime in high temperature high pressure water environment
    Kang, L. Z.
    Lu, Y. H.
    Bian, W. W.
    Yu, P. J.
    Wang, Y. . B.
    Xin, L.
    Han, Y. M.
    CORROSION SCIENCE, 2025, 242
  • [50] Damage behavior of aeronautical perspex (PMMA) under high-velocity water jet impact
    Wang X.
    Xu J.
    Hou N.
    Li Y.
    Hangkong Xuebao/Acta Aeronautica et Astronautica Sinica, 2022, 43 (12):
12345