Study of the effects of slurry acid radical on the corrosive-abrasive characteristics of high chromium cast iron

被引：0
|
作者：
Rao, Qichang [1 ]
Gao, Yimin [1 ]
Liu, Fuling [1 ]
Zhang, Jinzhu [1 ]
机构：
[1] Xi'an Jiaotong Univ, Xi'an, China
来源：
Hsi-An Chiao Tung Ta Hsueh/Journal of Xi'an Jiaotong University | 1993年 / 27卷 / 03期
关键词：
Acid resistance - Corrosive effects - Iron alloys - Wear resistance;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The effects of five kinds of inorganic acid, namely, phosphoric acid, sulphuric acid, nitric acid, hydrochloric acid and hydrofluoric acid(pH value was from 3 to 4, acid density was 0.1 N and 1N) on the corrosive-abrasive characteristics of high chromium cast iron were studied. The results show that variable acid radical had an important influence on the corrosive-abrasive characteristics of high chromium cast iron under the same slurry condition. The influence degree of slurry acid radical was in the sequence of HCl(HF)&rarrH2SO4(HNO3)&rarrH3PO4 according to the corrosive-abrasive rate from high to low. The increase of acid radical density had no influence on the sequence, but the corrosive-abrasive rate increased with the increase of acid density. As acid density was high than 0.1N the corrosive-abrasive rate higher than that of stainless steel. The influence of acid radical on the corrosive-abrasive rate was closely related to the influence of acid radical on the corrosive rate of high chromium cast iron.
引用
收藏
页码：15 / 18
相关论文
共 50 条
  • [41] Effects of Destabilization Temperature on the Microstructure and Mechanical Properties of High Chromium Cast Iron
    J. P. Lai
    Q. L. Pan
    Z. B. Wang
    H. R. Cui
    X. D. Wang
    Z. Z. Gao
    Journal of Materials Engineering and Performance, 2017, 26 : 4667 - 4675
  • [42] SLURRY SPEED DEPENDENCE OF SAND-EROSION RATE IN HIGH-CHROMIUM WHITE CAST-IRON
    ASO, S
    SUGAWARA, T
    TAGAMI, M
    GOTO, S
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1993, 57 (03) : 312 - 319
  • [43] Effects of Quenching Medium on Microstructure and Mechanical Properties of High Chromium Cast Iron
    Li, Yi
    Zhu, Peng-Xiao
    Tang, Cai
    Sun, Zhi
    CRYSTALS, 2022, 12 (10)
  • [44] Effects of Si on the Microstructures and Mechanical Properties of High-Chromium Cast Iron
    J. P. Lai
    Q. L. Pan
    H. J. Peng
    H. R. Cui
    C. A. Xiao
    Journal of Materials Engineering and Performance, 2016, 25 : 4617 - 4623
  • [45] Microstructural characteristics of a high-chromium cast iron hard-facing alloy
    Fras, Teresa
    Koenig, Benjamin
    Meyer, Paul P.
    Diop, Ibra
    BULLETIN OF THE POLISH ACADEMY OF SCIENCES-TECHNICAL SCIENCES, 2025, 73 (01)
  • [46] A study of the connection mechanism of cast-in high chromium cast iron-carbon cast steel by cast-in process
    Liu, X
    Shen, SX
    Xu, QY
    PROGRESS IN EXPERIMENTAL AND COMPUTATIONAL MECHANICS IN ENGINEERING, 2003, 243-2 : 159 - 163
  • [47] A study of wear of high-chromium cast iron under dry friction
    Ş. H. Atapek
    Ş. Polat
    Metal Science and Heat Treatment, 2013, 55 : 181 - 183
  • [48] Impact Abrasive Wear Resistance of High-Chromium Cast Iron Bars Reinforced Hadfield Steel Matrix Composite
    Niu, Libin
    Sun, Wangchang
    Hojamberdiev, Mirabbos
    MANUFACTURING PROCESS TECHNOLOGY, PTS 1-5, 2011, 189-193 : 1176 - +
  • [49] Three-Body Abrasive Wear Performance of High Chromium White Cast Iron with Different Ti and C Content
    Huq, Mohammad Jobayer
    Shimizu, Kazumichi
    Kusumoto, Kenta
    Purba, Riki Hendra
    LUBRICANTS, 2022, 10 (12)
  • [50] Study of high chromium cast iron lining plates for vertical cement mills
    Li, Jiabao
    Zheng, Wei
    Zhuzao Jishu/Foundry Technology, (02): : 13 - 15
12345