Numerical modeling on the formation process of keyhole-induced porosity for laser welding steel with T-joint

被引：0

作者：

机构：

[1] Li, Xibin

[2] Lu, Fenggui

[3] Cui, Haichao

[4] Tang, Xinhua

[5] Wu, Yixiong

来源：

Lu, F. (Lfg119@sjtu.edu.cn) | 1600年 / Springer London卷 / 72期

关键词：

A mathematical model of laser welding steel with a T-joint was developed in this paper to investigate the formation process of keyhole-induced porosity; helping to understand the mechanism of porosity formation in laser welding steels with heavy section. Solidification model and adiabatic bubble model were coupled in this model; which could more approximately reflect the formation process of bubble and its evolution into porosity. The volume-of-fluid (VOF) method was taken to track free surfaces of keyhole and porosity. The numerical results showed that the unstable keyhole during the laser welding process induced the collapse of keyhole and then resulted in bubbles in the molten pool. These bubbles moved following with the fluid flow in the molten pool; where some bubbles could escape out of molten pool under the competition of flow and solidification speed. But some bubbles captured by a solidified wall during the migration process in the molten pool would evolve into porosities. It was also found that some bubbles formed adjacent to a fusion line were easier to be captured by a solidification surface; which could give explanation for some porosities occurring close to the fusion line. A good agreement of simulation and experimental results proved the reliability of this mathematical model; while the mechanism of porosity formation was better clarified with this model. © 2014 Springer-Verlag London;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

下载

页码：1 / 4

共 50 条

[41] Relationship Between Molten Pool Behavior and Keyhole-Induced Porosity in Pulsed Laser-arc Hybrid Welding of Magnesium Alloy
Xin Lijun
Lin Sanbao
Liu Xuping
Piao Zhigang
Wu Fufa
Chen Minghua
RARE METAL MATERIALS AND ENGINEERING, 2020, 49 (06) : 1894 - 1900
[42] Numerical Simulations of Laser and Hybrid S700MC T-Joint Welding
Kik, Tomasz
Gorka, Jacek
MATERIALS, 2019, 12 (03)
[43] Parameter Optimization of the Laser T-joint Welding of Aluminium Alloy with Low Carbon Steel Using Numerical and Statistical Methods
Huang, W-H.
Long, J-Q.
Xiang, J-W.
LASERS IN ENGINEERING, 2017, 38 (3-6) : 167 - 183
[44] Effects of keyhole status on melt flow and flow-induced porosity formation during double-sided laser welding of AA6056/AA6156 aluminium alloy T-joint
Yang, Zhibin
Zhao, Xin
Tao, Wang
Jin, Cheng
OPTICS AND LASER TECHNOLOGY, 2019, 109 : 39 - 48
[45] Autogeneous laser and hybrid laser arc welding of T-joint low alloy steel with fiber laser systems
Unt, A.
Lappalainen, E.
Salminen, A.
LASERS IN MANUFACTURING (LIM 2013), 2013, 41 : 140 - 143
[46] Modelling of laser welding process in the phase of keyhole formation
Ronda, J.
Siwek, A.
ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING, 2011, 11 (03) : 739 - 752
[47] A VMD-BP Model to Predict Laser Welding Keyhole-Induced Pore Defect in Al Butt-Lap Joint
Wang, Wei
Dong, Yang
Liu, Fuyun
Yang, Biao
Han, Xiaohui
Wei, Lianfeng
Song, Xiaoguo
Tan, Caiwang
MATERIALS, 2024, 17 (13)
[48] Effect of welding parameters on porosity distribution of dual laser beam bilateral synchronous welding in 2219 aluminum alloy T-joint
Kang, Yue
Zhan, Xiaohong
Liu, Ting
JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2019, 33 (23) : 2595 - 2614
[49] Research of Laser Hybrid Welding for T-Joint in the Box Girder
Yu, Yang-Chun
Bao, Kong
Xu, Yan-Ling
Chen, A-Jing
Zhang, Hua-Jun
Chen, Shan-Ben
ROBOTIC WELDING, INTELLIGENCE AND AUTOMATION, RWIA'2014, 2015, 363 : 109 - 117
[50] Computer modeling of keyhole mode laser welding to avoid macro-porosity
Zhao, H
DebRoy, T
TRENDS IN WELDING RESEARCH, PROCEEDINGS, 2003, : 118 - 123

← 1 2 3 4 5 →