Numerical modeling on the formation process of keyhole-induced porosity for laser welding steel with T-joint

被引：0

作者：

机构：

[1] Li, Xibin

[2] Lu, Fenggui

[3] Cui, Haichao

[4] Tang, Xinhua

[5] Wu, Yixiong

来源：

Lu, F. (Lfg119@sjtu.edu.cn) | 1600年 / Springer London卷 / 72期

关键词：

A mathematical model of laser welding steel with a T-joint was developed in this paper to investigate the formation process of keyhole-induced porosity; helping to understand the mechanism of porosity formation in laser welding steels with heavy section. Solidification model and adiabatic bubble model were coupled in this model; which could more approximately reflect the formation process of bubble and its evolution into porosity. The volume-of-fluid (VOF) method was taken to track free surfaces of keyhole and porosity. The numerical results showed that the unstable keyhole during the laser welding process induced the collapse of keyhole and then resulted in bubbles in the molten pool. These bubbles moved following with the fluid flow in the molten pool; where some bubbles could escape out of molten pool under the competition of flow and solidification speed. But some bubbles captured by a solidified wall during the migration process in the molten pool would evolve into porosities. It was also found that some bubbles formed adjacent to a fusion line were easier to be captured by a solidification surface; which could give explanation for some porosities occurring close to the fusion line. A good agreement of simulation and experimental results proved the reliability of this mathematical model; while the mechanism of porosity formation was better clarified with this model. © 2014 Springer-Verlag London;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

下载

页码：1 / 4

共 50 条

[21] Numerical study of keyhole instability and porosity formation mechanism in laser welding of aluminum alloy and steel
Huang, Lijin
Hua, Xueming
Wu, Dongsheng
Li, Fang
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2018, 252 : 421 - 431
[22] Influence of Arc Power on Keyhole-Induced Porosity in Laser plus GMAW Hybrid Welding of Aluminum Alloy: Numerical and Experimental Studies
Xu, Guoxiang
Li, Pengfei
Li, Lin
Hu, Qingxian
Zhu, Jie
Gu, Xiaoyan
Du, Baoshuai
MATERIALS, 2019, 12 (08)
[23] Numerical investigation of weld bead porosity reduction in the oscillating laser T-joint welding of aluminum alloy
Ai, Yuewei
Cheng, Jian
Yu, Long
Lei, Chang
Yuan, Pengcheng
JOURNAL OF LASER APPLICATIONS, 2022, 34 (01)
[24] Keyhole-induced porosity in laser-arc hybrid welded aluminum
Ola, O. T.
Doern, F. E.
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2015, 80 (1-4): : 3 - 10
[25] Keyhole-induced porosity in laser-arc hybrid welded aluminum
O. T. Ola
F. E. Doern
The International Journal of Advanced Manufacturing Technology, 2015, 80 : 3 - 10
[26] Factors controlling keyhole-induced porosity in cold wire laser welded aluminum
Ola, O. T.
Doern, F. E.
JOURNAL OF LASER APPLICATIONS, 2017, 29 (01)
[27] Investigation on the effects of shielding gas on porosity in fiber laser welding of T-joint steels
Kai Li
Fenggui Lu
Haichao Cui
Xibin Li
Xinhua Tang
Zhuguo Li
The International Journal of Advanced Manufacturing Technology, 2015, 77 : 1881 - 1888
[28] Keyhole-induced pore formation mechanism in laser-MIG hybrid welding of aluminum alloy based on experiment and multiphase numerical model
Huang, Shuang
Xu, Lidong
Lou, Ming
Chen, Hui
Zhang, Ke
Li, Yongbing
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2023, 314
[29] Numerical simulation of keyhole formation process in laser deep penetration welding
Wang, Renping
Lei, Yongping
Shi, Yaowu
Hanjie Xuebao/Transactions of the China Welding Institution, 2010, 31 (11): : 38 - 40
[30] Formation mechanisms of lack of fusion and keyhole-induced pore defects in laser powder bed fusion process: A numerical study
Yang, Xuan
Li, Yazhi
Li, Biao
INTERNATIONAL JOURNAL OF THERMAL SCIENCES, 2023, 188

← 1 2 3 4 5 →