Numerical modeling on the formation process of keyhole-induced porosity for laser welding steel with T-joint

被引：0

作者：

机构：

[1] Li, Xibin

[2] Lu, Fenggui

[3] Cui, Haichao

[4] Tang, Xinhua

[5] Wu, Yixiong

来源：

Lu, F. (Lfg119@sjtu.edu.cn) | 1600年 / Springer London卷 / 72期

关键词：

A mathematical model of laser welding steel with a T-joint was developed in this paper to investigate the formation process of keyhole-induced porosity; helping to understand the mechanism of porosity formation in laser welding steels with heavy section. Solidification model and adiabatic bubble model were coupled in this model; which could more approximately reflect the formation process of bubble and its evolution into porosity. The volume-of-fluid (VOF) method was taken to track free surfaces of keyhole and porosity. The numerical results showed that the unstable keyhole during the laser welding process induced the collapse of keyhole and then resulted in bubbles in the molten pool. These bubbles moved following with the fluid flow in the molten pool; where some bubbles could escape out of molten pool under the competition of flow and solidification speed. But some bubbles captured by a solidified wall during the migration process in the molten pool would evolve into porosities. It was also found that some bubbles formed adjacent to a fusion line were easier to be captured by a solidification surface; which could give explanation for some porosities occurring close to the fusion line. A good agreement of simulation and experimental results proved the reliability of this mathematical model; while the mechanism of porosity formation was better clarified with this model. © 2014 Springer-Verlag London;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

页码：1 / 4

共 50 条

[31] Investigation on the effects of shielding gas on porosity in fiber laser welding of T-joint steels
Li, Kai
Lu, Fenggui
Cui, Haichao
Li, Xibin
Tang, Xinhua
Li, Zhuguo
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2015, 77 (9-12): : 1881 - 1888
[32] Numerical Simulation of the Formation Process of the Keyhole in Laser deep Penetration Welding
Wang, Renping
Lei, Yongping
Shi, Yaowu
ENVIRONMENT MATERIALS AND ENVIRONMENT MANAGEMENT PTS 1-3, 2010, 113-116 : 1779 - 1781
[33] Numerical analysis of T-joint Welding with different welding sequences
Patek, Marek
Mician, Miloš
Sládek, Augustín
Kadáš, Dalibor
Manufacturing Technology, 2016, 16 (01): : 234 - 238
[34] A numerical approach to modeling keyhole laser welding
Georgios Pastras
Apostolos Fysikopoulos
Christos Giannoulis
George Chryssolouris
The International Journal of Advanced Manufacturing Technology, 2015, 78 : 723 - 736
[35] Numerical modeling of keyhole dynamics in laser welding
Zhang, WH
Zhou, J
Tsai, HL
FIRST INTERNATIONAL SYMPOSIUM ON HIGH-POWER LASER MACROPROCESSING, 2003, 4831 : 180 - 185
[36] A numerical approach to modeling keyhole laser welding
Pastras, Georgios
Fysikopoulos, Apostolos
Giannoulis, Christos
Chryssolouris, George
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2015, 78 (5-8): : 723 - 736
[37] The influence of shielding gases on keyhole-induced porosity and nitrogen absorption in SS 304 stainless steel fiber laser welds
Khalid M. Hafez
The International Journal of Advanced Manufacturing Technology, 2023, 127 : 1887 - 1894
[38] Numerical simulation and test for influence of laser arc hybrid welding sequence on 304 stainless steel T-joint
Gui X.
Zhang Y.
You D.
Gao X.
Hanjie Xuebao/Transactions of the China Welding Institution, 2021, 42 (12): : 34 - 39
[39] Friction stir welding of steel T-joint configurations
Steel, RJ
Nelson, TW
Sorensen, CD
Packer, SM
PROCEEDINGS OF THE FIFTEENTH (2005) INTERNATIONAL OFFSHORE AND POLAR ENGINEERING CONFERENCE, VOL 4, 2005, : 1 - 5
[40] The influence of shielding gases on keyhole-induced porosity and nitrogen absorption in SS 304 stainless steel fiber laser welds
Khalid, M. Hafez M.
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2023, 127 (3-4): : 1887 - 1894

← 1 2 3 4 5 →