Analysis of brazing joints of CMCs/TC4 by Ag-Cu-Ti-Si filler

被引：0
|
作者：
Aerospace Research Institute of Material and Processing Technology, Beijing 100076, China [1 ]
机构：
来源：
Cailiao Kexue yu Gongyi | 2009年 / SUPPL. 1卷 / 40-43期
关键词：
Silver alloys - Filler metals - Fillers - Scanning electron microscopy - Silicon alloys - Titanium alloys - Brazing - Copper alloys;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
C/SiC CMCs and TC4 alloy are brazed successfully by Ag-Cu-Ti-Si filler in this research. The shear strength of the joints are tested, the interface microstructure and fracture appearance are observed by SEM method, and the microstructure is analyzed by EDS. The results show that the max. value of shear strength is 118.2 MPa, by using Ag-Cu-Ti-Si filler(Ti:Ti=1:1, wt%), while the brazing parameter is 900°C/10min.
引用
下载
收藏
相关论文
共 50 条
  • [41] Interface microstructure and thermal stress of diamond brazing with Ag-Cu-Ti filler
    Lu, Jinbin
    Xu, Jiuhua
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2009, 38 (04): : 642 - 646
  • [42] Interface Microstructure and Thermal Stress of Diamond Brazing with Ag-Cu-Ti Filler
    Lu Jinbin
    Xu Jiuhua
    RARE METAL MATERIALS AND ENGINEERING, 2009, 38 (04) : 642 - 646
  • [43] The design of a new Ti-Zr-Cu-Ni-Ag brazing filler metal for brazing of titanium alloys
    Jing, Yongjuan
    Yang, Haibo
    Shang, Yonglai
    Xiong, Huaping
    WELDING IN THE WORLD, 2021, 65 (11) : 2231 - 2237
  • [44] Single-pass laser brazing of TC4 alloy and 304 stainless steel with Cu interlayer and Cu-Zn filler metal
    Chen, YanKun
    Zhou, JianPing
    Zhang, Yan
    Xu, Yan
    Bao, Yang
    MATERIALS LETTERS, 2021, 291
  • [45] The design of a new Ti-Zr-Cu-Ni-Ag brazing filler metal for brazing of titanium alloys
    Yongjuan Jing
    Haibo Yang
    Yonglai Shang
    Huaping Xiong
    Welding in the World, 2021, 65 : 2231 - 2237
  • [46] Microstructure of interface between Ag-Cu-Ti brazing filler metal and diamond
    Lu, Jinbin
    Xu, Jiuhua
    Hanjie Xuebao/Transactions of the China Welding Institution, 2007, 28 (08): : 29 - 32
  • [47] Role of the reaction product in the solidification of Ag-Cu-Ti filler for brazing diamond
    Yamazaki, T
    Suzumura, A
    JOURNAL OF MATERIALS SCIENCE, 1998, 33 (05) : 1379 - 1384
  • [48] Brazing TC4 alloy to Si3N4 ceramic using nano-Si3N4 reinforced AgCu composite filler
    Zhao, Y. X.
    Wang, M. R.
    Cao, J.
    Song, X. G.
    Tang, D. Y.
    Feng, J. C.
    MATERIALS & DESIGN, 2015, 76 : 40 - 46
  • [49] Brazing ZTA ceramic to TC4 alloy using the Cu foam as interlayer
    Wang, Xiaoyang
    Li, Chun
    Si, Xiaoqing
    Qi, Junlei
    Feng, Jicai
    Cao, Jian
    VACUUM, 2018, 155 : 7 - 15
  • [50] Reaction-composite brazing of carbon fiber reinforced SiC composite and TC4 alloy using Ag-Cu-Ti-(Ti plus C) mixed powder
    Cui, Bing
    Huang, Ji Hua
    Xiong, Jin Hui
    Zhang, Hua
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 562 : 203 - 210
12345