Structural stability of (Ba, Sr)RuO3 electrodes on hydrogen annealing and effect of interfacial layers in (Ba,Sr)TiO3 thin films

被引：0
|
作者：
Choi, Eun-Suck [1 ]
Park, Sang-Shik [2 ]
Yoon, Soon-Gil [1 ]
机构：
[1] Department of Materials Engineering, Chungnam National University, Daedeok Science Town, Daejeon, 305-764, Korea, Republic of
[2] Department of Advanced Materials Engineering, Sangju National University, Kyungbuk, 742-711, Korea, Republic of
来源：
Integrated Ferroelectrics | 2002年 / 47卷
关键词：
Annealing - Barium compounds - Ferroelectric thin films - Metallorganic chemical vapor deposition - Permittivity;
D O I：
10.1080/713718271
中图分类号：
学科分类号：
摘要：
(Ba, Sr)RuO3(BSR) electrodes were deposited on n-type Si (100) substrates by liquid-delivery metalorganic chemical vapor deposition (LDMOCVD) and their stability in a hydrogen ambient was investigated. BSR films showed the structural and morphological stability when annealed in hydrogen forming gas (4 % H2+96% balance N2) temperatures of up to 500. The abrupt increase of resistivity with increasing hydrogen annealing temperature can be attributed to oxygen loss in BSR films without phase change and was completely recovered by annealing at 700 in an O2 ambient. The dielectric constant of the Pt/BSR/BST/Pt structures increased with increasing BSR interfacial layers. The dielectric constant of a BSR/BST/Pt capacitor with a 35 nm thick BST without top Pt electrode showed about 425. © 2002 Taylor & Francis.
引用
收藏
页码：31 / 40
相关论文
共 50 条
  • [31] The properties of oriented (Ba, Sr)TiO3 thin Films
    Ding, W
    Meng, ZY
    FOURTH INTERNATIONAL CONFERENCE ON THIN FILM PHYSICS AND APPLICATIONS, 2000, 4086 : 675 - 678
  • [32] Dielectric relaxation of (Ba, Sr)TiO3 thin films
    Horikawa, Tsuyoshi, 1600, JJAP, Minato-ku, Japan (34):
  • [33] Metal Organic Chemical Vapor Deposition of (Ba, Sr)RuO3 oxide electrode for (Ba, Sr)TiO3 using nozzle type injector
    Park, Jeong-Hee
    Kang, Joong-Seo
    Kim, Young-Bae
    Choi, Duck-Kyun
    Han, Young-Ki
    Yang, Doo-Young
    Oh, Ki-Young
    Ferroelectrics, 2001, 260 (01) : 105 - 111
  • [34] Metal organic chemical vapor deposition of (Ba,Sr)RuO3 oxide electrode for (Ba,Sr)TiO3 using nozzle type injector
    Park, JH
    Kang, JS
    Kim, YB
    Choi, DK
    Han, YK
    Yang, DY
    Oh, KY
    FERROELECTRICS, 2001, 260 (1-4) : 449 - 455
  • [35] Prevention of degradation of (Ba,Sr)TiO3 during forming gas anneal by a SiO2 capped (Ba,Sr)RuO3 electrode
    Kim, Y.-B. (duck@hanyang.ac.kr), 1600, American Institute of Physics Inc. (93):
  • [36] Prevention of degradation of (Ba,Sr)TiO3 during forming gas anneal by a SiO2 capped (Ba,Sr) RuO3 electrode
    Kim, YB
    Park, JH
    Hong, DH
    Choi, DK
    Yoo, CY
    Horii, H
    JOURNAL OF APPLIED PHYSICS, 2003, 93 (11) : 9212 - 9217
  • [37] (Ba,Sr)RuO3 bottom electrode deposited by liqud delivery metalorganic chemical vapor deposition for (Ba,Sr)TiO3 high dielectric
    Choi, ES
    Shin, WC
    Yoon, SG
    FERROELECTRICS, 2002, 271 : 1701 - 1706
  • [38] Preparation and characterization of (Ba, Sr)TiO3 thin films using interdigital electrodes
    Cheng, YL
    Wang, Y
    Chan, HLW
    Choy, CL
    MICROELECTRONIC ENGINEERING, 2003, 66 (1-4) : 872 - 879
  • [39] (BA, SR)TIO3 HETEROEPITAXIAL FILMS
    MUKHORTOV, VM
    GOLOVKO, YI
    ALESHIN, VA
    SVIRIDOV, EV
    MUKHORTOV, VM
    DUDKEVICH, VP
    FESENKO, EG
    PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1983, 78 (01): : 253 - 257
  • [40] Preparation and properties of (Ba,Sr)TiO3 thin films with various bottom electrodes
    Ahn, JH
    Park, JH
    Kim, HG
    JOURNAL OF THE KOREAN PHYSICAL SOCIETY, 1998, 32 : S1513 - S1516
12345