Sulfide stress corrosion susceptibility and hydrogen trapping efficiency of the welded joint of X70 MS pipeline steel

被引：0
|
作者：
Yuan, Wei [1 ,2 ]
Huang, Feng [1 ,2 ]
Zhao, Xiao-Yu [1 ,2 ]
Fan, Li-Xia [1 ,2 ]
Liu, Jing [1 ,2 ]
机构：
[1] Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan,430081, China
[2] Hubei Engineering Technology Research Center of Marine Materials and Service Safety, Wuhan,430081, China
来源：
Surface Technology | 2020年 / 49卷 / 08期
关键词：
D O I：
10.16490/j.cnki.issn.1001-3660.2020.08.005
中图分类号：
学科分类号：
摘要：
33
引用
收藏
页码：34 / 44
相关论文
共 50 条
  • [21] A Study on Stress Corrosion Cracking of X70 Pipeline Steel in Carbonate Solution by EIS
    Shahriari, A.
    Shahrabi, T.
    Oskuie, A. A.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (05) : 1459 - 1470
  • [22] Stress corrosion behavior of X70 pipeline steel in simulated solution of acid soil
    Liu, Zhiyong
    Zhai, Guoli
    Du, Cuiwei
    Li, Xiaogang
    Jinshu Xuebao/Acta Metallurgica Sinica, 2008, 44 (02): : 209 - 214
  • [23] Stress Corrosion Cracking of X70 Pipeline Steel immersed in Synthetic Soil solution
    Galvan-Martinez, R.
    Carmona, A.
    Baltazar, M.
    Contreras, A.
    Orozco-Cruz, R.
    AFINIDAD, 2019, 76 (585) : 52 - 62
  • [24] Characteristics and mechanism of high pH stress corrosion cracking of pipeline steel X70
    Li, Guangfu
    Zhang, Guoliang
    Zhou, Jianjiang
    Huang, Chunbo
    Yang, Wu
    PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 : 219 - 222
  • [25] Experimental research on stress corrosion cracking of X70 pipeline steel in nitrate solutions
    Wang, Bo
    Dong, Yuexiang
    Zhang, Wei
    Gao, Zengliang
    Yang, Tiecheng
    EVALUATION, INSPECTION AND MONITORING OF STRUCTURAL INTEGRITY, 2008, : 385 - 388
  • [26] Stress corrosion behavior of X70 pipeline steel in simulated solution of acid soil
    Liu Zhiyong
    Zhai Guoli
    Du Cuiwei
    Li Xiaogang
    ACTA METALLURGICA SINICA, 2008, 44 (02) : 209 - 214
  • [27] Comparative Study on Hydrogen Embrittlement Susceptibility of X60 and X70 Pipeline Steels and Their Welded Joints
    Wang W.
    Chen Y.
    Zhan X.
    Liu J.
    Tang W.
    Surface Technology, 2024, 53 (04): : 117 - 124
  • [28] Tension fracture behaviors of welded joints in X70 steel pipeline
    Kong, Dejun
    Wu, Yongzhong
    Long, Dan
    Zhou, Chaozheng
    THEORETICAL AND APPLIED MECHANICS LETTERS, 2011, 1 (03)
  • [29] Tension fracture behaviors of welded joints in X70 steel pipeline
    Dejun Kong
    Theoretical & Applied Mechanics Letters, 2011, 1 (03) : 39 - 43
  • [30] Hydrogen embrittlement susceptibility of X70 pipeline steel weld under a low partial hydrogen environment
    Thanh Tuan Nguyen
    Tak, Naehyung
    Park, Jaeyeong
    Nahm, Seung Hoon
    Beak, Un Bong
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2020, 45 (43) : 23739 - 23753
12345