A Study on Stress Corrosion Cracking of X70 Pipeline Steel in Carbonate Solution by EIS

被引：8
|
作者：
Shahriari, A. [1 ]
Shahrabi, T. [1 ]
Oskuie, A. A. [1 ]
机构：
[1] Tarbiat Modares Univ, Dept Mat Sci & Engn, Fac Engn, Tehran, Iran
来源：
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2013年 / 22卷 / 05期
关键词：
carbon/alloy steel; corrosion testing; mechanical testing; ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY; PASSIVE LAYER CRACKING; BEHAVIOR; MACROSEGREGATION; MICROSTRUCTURE; SCC;
D O I：
10.1007/s11665-012-0418-6
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this study, electrochemical impedance spectroscopy (EIS) simultaneously with the slow strain rate testing were used to investigate the stress corrosion cracking (SCC) behavior of X70 pipeline steel in high pH bicarbonate solution at different applied potentials. Potentiostatic EIS tests were also conducted at certain times to determine the changes associated with the SCC. Circuit models for the cracking were proposed by the use of the potentiostatic EIS measurements at different applied potentials. Finally, the results of the potentiostatic EIS tests and the SSR tests showed the decline of the circuit element resistance by increasing the stress which was related to the cracking. It was also observed that the X70 pipeline steel was most susceptible to SCC at potential of -650 mV versus SCE.
引用
收藏
页码：1459 / 1470
页数：12
相关论文
共 50 条
  • [1] A Study on Stress Corrosion Cracking of X70 Pipeline Steel in Carbonate Solution by EIS
    A. Shahriari
    T. Shahrabi
    A. A. Oskuie
    [J]. Journal of Materials Engineering and Performance, 2013, 22 : 1459 - 1470
  • [2] Stress Corrosion Cracking of X70 Pipeline Steel immersed in Synthetic Soil solution
    Galvan-Martinez, R.
    Carmona, A.
    Baltazar, M.
    Contreras, A.
    Orozco-Cruz, R.
    [J]. AFINIDAD, 2019, 76 (585) : 52 - 62
  • [3] Electrochemical impedance spectroscopy analysis of X70 pipeline steel stress corrosion cracking in high pH carbonate solution
    Oskuie, A. A.
    Shahrabi, T.
    Shahriari, A.
    Saebnoori, E.
    [J]. CORROSION SCIENCE, 2012, 61 : 111 - 122
  • [4] Effect of applied potentials on stress corrosion cracking of X70 pipeline steel in alkali solution
    Zhang Liang
    Li Xiaogang
    Du Cuiwei
    Huang Yizhong
    [J]. MATERIALS & DESIGN, 2009, 30 (06) : 2259 - 2263
  • [5] Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in a CO2-Containing Solution
    Zhang, L.
    Li, X. G.
    Du, C. W.
    Cheng, Y. F.
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2009, 18 (03) : 319 - 323
  • [6] Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in a CO2-Containing Solution
    L. Zhang
    X.G. Li
    C.W. Du
    Y.F. Cheng
    [J]. Journal of Materials Engineering and Performance, 2009, 18 : 319 - 323
  • [7] Characteristics and mechanism of high pH stress corrosion cracking of pipeline steel X70
    Li, Guangfu
    Zhang, Guoliang
    Zhou, Jianjiang
    Huang, Chunbo
    Yang, Wu
    [J]. PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 : 219 - 222
  • [8] Experimental research on stress corrosion cracking of X70 pipeline steel in nitrate solutions
    Wang, Bo
    Dong, Yuexiang
    Zhang, Wei
    Gao, Zengliang
    Yang, Tiecheng
    [J]. EVALUATION, INSPECTION AND MONITORING OF STRUCTURAL INTEGRITY, 2008, : 385 - 388
  • [9] Effects of temperature on stress corrosion of X70 pipeline steel in solution with oxygen
    Ye, Cundong
    Kong, Dejun
    Zhang, Lei
    [J]. Zhongnan Daxue Xuebao (Ziran Kexue Ban)/Journal of Central South University (Science and Technology), 2015, 46 (07): : 2432 - 2438
  • [10] Stress Corrosion Cracking of Welded API X70 Pipeline Steel in Simulated Underground Water
    Liu, Z. Y.
    Du, C. W.
    Li, C.
    Wang, F. M.
    Li, X. G.
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (09) : 2550 - 2556
12345