Sulfide stress corrosion susceptibility and hydrogen trapping efficiency of the welded joint of X70 MS pipeline steel

被引：0
|
作者：
Yuan, Wei [1 ,2 ]
Huang, Feng [1 ,2 ]
Zhao, Xiao-Yu [1 ,2 ]
Fan, Li-Xia [1 ,2 ]
Liu, Jing [1 ,2 ]
机构：
[1] Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan,430081, China
[2] Hubei Engineering Technology Research Center of Marine Materials and Service Safety, Wuhan,430081, China
来源：
Surface Technology | 2020年 / 49卷 / 08期
关键词：
D O I：
10.16490/j.cnki.issn.1001-3660.2020.08.005
中图分类号：
学科分类号：
摘要：
33
引用
收藏
页码：34 / 44
相关论文
共 50 条
  • [31] Effects of hydrogen on the fracture toughness of a X70 pipeline steel
    Wang, Rong
    CORROSION SCIENCE, 2009, 51 (12) : 2803 - 2810
  • [32] Modeling bulk diffusion of hydrogen in X70 pipeline steel
    Drexler, Andreas
    Pastore, Sergio
    Domitner, Josef
    SCIENTIFIC REPORTS, 2025, 15 (01):
  • [33] Influence of stress triaxiality on hydrogen assisted ductile damage in an X70 pipeline steel
    Depraetere, Robin
    De Waele, Wim
    Cauwels, Margo
    Depover, Tom
    Verbeken, Kim
    Boone, Matthieu
    Hertele, Stijn
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2023, 864
  • [34] Effect of hydrogen-induced plasticity on the stress corrosion cracking of X70 pipeline steel in simulated soil environments
    Liu, Z. Y.
    Wang, X. Z.
    Du, C. W.
    Li, J. K.
    Li, X. G.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 658 : 348 - 354
  • [35] Hydrogen induced cracking susceptibility in different layers of a hot rolled X70 pipeline steel
    Mohtadi-Bonab, M. A.
    Szpunar, J. A.
    Razavi-Tousi, S. S.
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2013, 38 (31) : 13831 - 13841
  • [36] STRESS CORROSION CRACK INITIATION BEHAVIOR FOR THE X70 PIPELINE STEEL BENEATH A DISBONDED COATING
    Wang Zhiying
    Wang Jianqiu
    Han En-hou
    Ke Wei
    Yan Maocheng
    Zhang Junwei
    Liu Chuwei
    ACTA METALLURGICA SINICA, 2012, 48 (10) : 1267 - 1272
  • [37] Effect of applied potentials on stress corrosion cracking of X70 pipeline steel in alkali solution
    Zhang Liang
    Li Xiaogang
    Du Cuiwei
    Huang Yizhong
    MATERIALS & DESIGN, 2009, 30 (06) : 2259 - 2263
  • [38] CTOA levels of welded joint in API X70 pipe steel
    Hashemi, S. H.
    Sedghi, S.
    Soleymani, V.
    Mohammadyani, D.
    ENGINEERING FRACTURE MECHANICS, 2012, 82 : 46 - 59
  • [39] Effects of laser shock processing on H2S stress corrosion fractures of X70 pipeline steel welded joints
    Kong, Dejun
    Wu, Yongzhong
    Long, Dan
    Hanjie Xuebao/Transactions of the China Welding Institution, 2011, 32 (10): : 13 - 16
  • [40] Salt spray corrosion behavior of X70 pipeline steel welded joints by submerged arc automatic welding
    Yang, Guang
    Kong, De-Jun
    Ye, Cun-Dong
    Xie, Chun-Yang
    Guo, Hao-Yuan
    Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2014, 35 (08): : 157 - 162
12345