DIFFRACTION CONTRAST IMAGES OF SMALL STACKING-FAULT TETRAHEDRA IN FCC METALS

被引:17
|
作者
SATOH, Y
TAOKA, H
KOJIMA, S
YOSHIIE, T
KIRITANI, M
机构
[1] KYOTO UNIV,INST RES REACTOR,OSAKA 59004,JAPAN
[2] HOKKAIDO UNIV,DEPT PRECIS ENGN,SAPPORO,HOKKAIDO 060,JAPAN
关键词
D O I
10.1080/01418619408242936
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Transmission electron microscopy images of stacking fault tetrahedra (SFTs) are studied in detail both experimentally and by image simulation. Experimental dark-field diffraction contrast images of SFTs are examined under various conditions. The image contrast of stacking faults and stair-rod dislocations are simulated based on standard multi-beam dynamical theory, and the image contrast of very small SFTs (< 2.6 nm) is calculated by the multi-slice method. The correspondence between experimental and calculated results under systematically varied conditions is quite satisfactory. Stacking faults make a larger contribution to the total SFT image than stair-rod dislocations. The images are generally smaller than the SFT. The difference in size depends on many parameters such as deviation from the Bragg condition, location in the foil, and specimen thickness. However, the difference is always smaller than the fringe spacing in the stacking fault image, and is generally smaller at a larger deviation from the Bragg condition. SFTs smaller than the fringe spacing are sometimes indistinguishable in contrast. The diffracting vector of 200 achieves higher visibility than any other diffracting vectors. The visibility ratio is higher at larger deviations from the Bragg condition. Multi-slice calculations suggest that SFTs smaller than 1 nm can be detected by weak-beam diffraction contrast methods. Suitable observing conditions for data acquisition in radiation damage studies are proposed.
引用
收藏
页码:869 / 891
页数:23
相关论文
共 50 条
  • [41] Influence of grain size and stacking-fault energy on deformation twinning in fcc metals
    El-Danaf, E
    Kalidindi, SR
    Doherty, RD
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (05): : 1223 - 1233
  • [42] COMMENT ON THE CONTRAST OF STACKING-FAULT FRINGES
    WHELAN, MJ
    PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1986, 94 (01): : K39 - K40
  • [43] DISSOCIATION OF LOMER TYPE BARRIERS AND STACKING-FAULT TETRAHEDRA IN COLD-WORKED CFC METALS
    CONDAT, M
    FAYARD, M
    COMPTES RENDUS HEBDOMADAIRES DES SEANCES DE L ACADEMIE DES SCIENCES SERIE C, 1975, 280 (22): : 1339 - 1342
  • [44] FORMATION OF STACKING-FAULT TETRAHEDRA BY GRAIN-BOUNDARY MOVEMENT
    CLAREBROUGH, LM
    FORWOOD, CT
    PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1987, 104 (01): : 51 - 62
  • [45] STACKING-FAULT TETRAHEDRA AND DIHEDRA IN AUSTENITIC STAINLESS-STEELS
    ARTIGUE, F
    CONDAT, M
    FAYARD, M
    SCRIPTA METALLURGICA, 1977, 11 (07): : 623 - 626
  • [46] STACKING-FAULT ENERGIES OF HCP METALS
    FLEISCHER, RL
    SCRIPTA METALLURGICA, 1986, 20 (02): : 223 - 224
  • [47] THE OBSERVATION OF STACKING-FAULT TETRAHEDRA IN III-V COMPOUNDS
    DECOOMAN, BC
    MCKERNAN, S
    CARTER, CB
    RALSTON, JR
    WICKS, GW
    EASTMAN, LF
    PHILOSOPHICAL MAGAZINE LETTERS, 1987, 56 (03) : 85 - 90
  • [48] VACANCY SINK EFFICIENCY OF STACKING-FAULT TETRAHEDRA IN QUNECHED GOLD
    JAIN, KC
    SIEGEL, RW
    JOURNAL OF METALS, 1969, 21 (03): : A67 - &
  • [49] OBSERVATION OF STACKING-FAULT TETRAHEDRA IN AN NI-CR ALLOY
    LEPINAY, A
    EYMERY, JP
    GAREM, H
    COMPTES RENDUS HEBDOMADAIRES DES SEANCES DE L ACADEMIE DES SCIENCES SERIE B, 1976, 282 (06): : 153 - 155
  • [50] Dynamics of dislocation interactions with stacking-fault tetrahedra at high temperature
    Briceno, M.
    Kacher, J.
    Robertson, I. M.
    JOURNAL OF NUCLEAR MATERIALS, 2013, 433 (1-3) : 390 - 396