DIFFRACTION CONTRAST IMAGES OF SMALL STACKING-FAULT TETRAHEDRA IN FCC METALS

被引:17
|
作者
SATOH, Y
TAOKA, H
KOJIMA, S
YOSHIIE, T
KIRITANI, M
机构
[1] KYOTO UNIV,INST RES REACTOR,OSAKA 59004,JAPAN
[2] HOKKAIDO UNIV,DEPT PRECIS ENGN,SAPPORO,HOKKAIDO 060,JAPAN
关键词
D O I
10.1080/01418619408242936
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Transmission electron microscopy images of stacking fault tetrahedra (SFTs) are studied in detail both experimentally and by image simulation. Experimental dark-field diffraction contrast images of SFTs are examined under various conditions. The image contrast of stacking faults and stair-rod dislocations are simulated based on standard multi-beam dynamical theory, and the image contrast of very small SFTs (< 2.6 nm) is calculated by the multi-slice method. The correspondence between experimental and calculated results under systematically varied conditions is quite satisfactory. Stacking faults make a larger contribution to the total SFT image than stair-rod dislocations. The images are generally smaller than the SFT. The difference in size depends on many parameters such as deviation from the Bragg condition, location in the foil, and specimen thickness. However, the difference is always smaller than the fringe spacing in the stacking fault image, and is generally smaller at a larger deviation from the Bragg condition. SFTs smaller than the fringe spacing are sometimes indistinguishable in contrast. The diffracting vector of 200 achieves higher visibility than any other diffracting vectors. The visibility ratio is higher at larger deviations from the Bragg condition. Multi-slice calculations suggest that SFTs smaller than 1 nm can be detected by weak-beam diffraction contrast methods. Suitable observing conditions for data acquisition in radiation damage studies are proposed.
引用
收藏
页码:869 / 891
页数:23
相关论文
共 50 条
  • [31] DEVELOPMENT OF RECRYSTALLIZATION TEXTURES IN FCC METALS WITH A LOW STACKING-FAULT ENERGY
    SLAKHORST, JWHG
    ACTA METALLURGICA, 1975, 23 (03): : 301 - 308
  • [32] ON VARIATION OF WIRE TEXTURE WITH STACKING-FAULT ENERGY IN FCC METALS + ALLOYS
    ENGLISH, AT
    CHIN, GY
    JOM-JOURNAL OF METALS, 1964, 16 (09): : 772 - &
  • [33] CRITICAL NUCLEATION TEMPERATURE OF STACKING-FAULT TETRAHEDRA IN GOLD
    HUSSEIN, AA
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1977, 8 (11): : 1745 - 1747
  • [34] THE GROWTH MECHANISM OF STACKING-FAULT TETRAHEDRA IN QUENCHED GOLD
    KIMURA, H
    KUHLMANNWILSDORF, D
    MADDIN, R
    APPLIED PHYSICS LETTERS, 1963, 3 (01) : 4 - 5
  • [35] The collapse of stacking-fault tetrahedra by interaction with gliding dislocations
    Matsukawa, Y
    Osetsky, YN
    Stoller, RE
    Zinkle, SJ
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 400 : 366 - 369
  • [36] STACKING-FAULT ENERGY INFLUENCE ON LOGARITHMIC TRANSITION CREEP OF METALS WITH FCC LATTICE
    BARINOV, SM
    YUDIN, AA
    FIZIKA METALLOV I METALLOVEDENIE, 1975, 40 (04): : 845 - 848
  • [37] Influence of grain size and stacking-fault energy on deformation twinning in fcc metals
    Ehab El-Danaf
    Surya R. Kalidindi
    Roger D. Doherty
    Metallurgical and Materials Transactions A, 1999, 30 : 1223 - 1233
  • [38] EFFECT OF STACKING-FAULT ENERGY ON THERMALLY ACTIVATED DISLOCATION GLIDE IN FCC METALS
    SAGAR, V
    DAVIES, CKL
    STEVENS, RN
    INDIAN JOURNAL OF TECHNOLOGY, 1973, 11 (11): : 516 - 522
  • [39] STACKING-FAULT ENERGY AND DELAMINATION WEAR OF SINGLE-PHASE FCC METALS
    SUH, NP
    SAKA, N
    WEAR, 1977, 44 (01) : 135 - 143
  • [40] DEVELOPMENT OF ROLLING TEXTURE OF FCC METALS DEPENDENT ON RELATIVE STACKING-FAULT ENERGY
    MUCKLICH, A
    TOBISCH, J
    KLEINSTUCK, K
    KRISTALL UND TECHNIK-CRYSTAL RESEARCH AND TECHNOLOGY, 1978, 13 (09): : 1067 - 1076