MOLECULAR-BEAM EPITAXIAL-GROWTH OF CDTE(112) ON SI(112) SUBSTRATES

High crystalline quality epitaxial CdTe(112)B/ZnTe films were deposited by molecular-beam epitaxy directly onto vicinal Si(112) substrates, without use of GaAs interfacial layers. The films were characterized with x-ray diffraction, optical microscopy, and wet chemical defect etching. Single crystal, twin-free CdTe(112)B films exhibit structural quality exceeding that previously reported for CdTe(112)B heteroepitaxy on GaAs/Si(112) or GaAs(112)B substrates. X-ray rocking curve full width at half-maximum of 72 arcsec for CdTe(224) reflection and near-surface etch pit densities (EPD) of 2×106 cm-2 have been observed for 8-μm-thick CdTe films. EPD depth profiles indicate that the threading dislocation density decreases with increasing II-VI epilayer thickness up to approximately 5 μm thickness and saturates at 2×106 cm-2 for thickness exceeding 5 μm. The CdTe epilayer orientation was observed to tilt 2°away from the Si(112) substrate orientation toward the [001] direction.© 1995 American Institute of Physics.