DEPENDENCE OF MAGNETIC-PROPERTIES OF CO/PT MULTILAYERS ON DEPOSITION TEMPERATURE OF PT BUFFER LAYERS

被引:3
|
作者
SHIOMI, S
NISHIMURA, T
KOBAYASHI, T
MASUDA, M
机构
[1] Department of Electrical and Electronic Engineering, Mie University, Tsu, Mie
来源
关键词
CO/PT MULTILAYER; PT BUFFER LAYER; PERPENDICULAR MAGNETIC ANISOTROPY; COERCIVITY; SUBSTRATE TEMPERATURE; (111) PREFERRED ORIENTATION; EVAPORATION;
D O I
10.1143/JJAP.32.L495
中图分类号
O59 [应用物理学];
学科分类号
摘要
A 15-nm-thick Pt buffer layer was deposited on a glass slide at temperature T(s)(Pt(buf)) ranging from 30 to 300-degrees-C by e-gun evaporation. Following the cooling in vacuum to ambient temperature, Co and Pt layers have been alternately deposited on it. Very large perpendicular anisotropy and coercivity have been obtained at T(s)(Pt(buf)) higher than 200-degrees-C. The (111) preferred orientation of the Co/Pt multilayer as well as the Pt buffer layer became more pronounced with elevating T(s)(Pt(buf)), to which the enhancement of perpendicular anisotropy with elevating T(s)(Pt(buf)) might be ascribable.
引用
收藏
页码:L495 / L497
页数:3
相关论文
共 50 条
  • [21] Structural and magnetic properties of Co/Pt(111) with Ni buffer layers
    Ho, H. Y.
    Chen, Y. J.
    Chen, R. H.
    Shern, C. S.
    JOURNAL OF APPLIED PHYSICS, 2006, 99 (12)
  • [22] Effect of a Cu spacer between Co and Pt layers on the structural and magnetic properties in (Co/Cu/Pt)5/Pt type multilayers
    Bandiera, S.
    Sousa, R. C.
    Rodmacq, B.
    Lechevallier, L.
    Dieny, B.
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2013, 46 (48)
  • [23] Temperature and ion irradiation dependence of magnetic domains and microstructure in Co/Pt multilayers
    Kusinski, GJ
    Thomas, G
    Denbeaux, G
    Krishnan, KM
    Terris, BD
    JOURNAL OF APPLIED PHYSICS, 2002, 91 (10) : 7541 - 7543
  • [24] TEMPERATURE-DEPENDENCE OF THE MAGNETIZATION OF CO/PT MULTILAYERS
    BLOEMEN, PJH
    SWUSTE, CHW
    POODT, GJM
    HOVING, W
    DENBROEDER, FJA
    JOURNAL OF APPLIED PHYSICS, 1990, 67 (09) : 4470 - 4470
  • [25] TEMPERATURE-DEPENDENCE OF MAGNETIC-PROPERTIES IN CO-PT, FE-PT AND CR-PT PERMANENT-MAGNET ALLOYS
    WATANABE, K
    KANEKO, T
    OHNUMA, S
    MATERIALS TRANSACTIONS JIM, 1994, 35 (02): : 136 - 141
  • [26] The role of W seed and spacer layers on the magnetic properties of Co/Pt multilayers
    Tokac, M.
    Piskin, H.
    Ekinci, G.
    Ozkal, B.
    Kazan, S.
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2025, 618
  • [27] DEPENDENCE OF MAGNETIC-PROPERTIES OF CO-PT FILMS ON SPUTTERING CONDITIONS
    HOSHI, Y
    MATSUOKA, M
    NAOE, M
    JOURNAL OF APPLIED PHYSICS, 1985, 57 (08) : 4022 - 4024
  • [28] Temperature dependence of spin-orbit torques in Pt/Co/Pt multilayers
    Chen, Shiwei
    Li, Dong
    Cui, Baoshan
    Xi, Li
    Si, Mingsu
    Yang, Dezheng
    Xue, Desheng
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2018, 51 (09)
  • [29] TEMPERATURE-DEPENDENCE OF MAGNETIC-PROPERTIES IN CO-PT, FE-PT AND CR-PT PERMANENT-MAGNET ALLOY SYSTEM
    WATANABE, K
    KANEKO, T
    OHNUMA, S
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1992, 56 (12) : 1495 - 1500
  • [30] MAGNETIC-PROPERTIES OF COXNI1-X/PT MULTILAYERS
    KRISHNAN, R
    LASSRI, H
    SEDDAT, M
    PORTE, M
    TESSIER, M
    APPLIED PHYSICS LETTERS, 1994, 64 (17) : 2312 - 2314