STRONTIUM-RICH TL-1223 SUPERCONDUCTOR FILMS FROM ACETATE SOL

被引：3
|
作者：
LEE, BI [1 ]
DOI, TJ [1 ]
YUASA, T [1 ]
机构：
[1] CLEMSON UNIV,DEPT CERAM ENGN,CLEMSON,SC 29634
来源：
PHYSICA C | 1994年 / 226卷 / 3-4期
关键词：
D O I：
10.1016/0921-4534(94)90219-4
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
Tl0.5Pb0.5Sr1.7Ba0.3Ca2Cu3Ox superconducting films were prepared from metal acetate sol. A simple procedure was developed to prepare the films. Nearly phase pure films on MgO and strontium titanate substrates with preferred grain orientation were obtained. The T(c) and J(c) of the films were above 120 K and 10(5) A/cm2 respectively in the absence of applied magnetic fields and above 10(4) A/cm2 at an applied magnetic field of 10(4) G. Experimental procedures, microstructures, and electrical properties of the films with respect to J(c) are presented.
引用
收藏
页码：377 / 384
页数：8
相关论文
共 50 条
  • [21] FABRICATION AND PROPERTIES OF DC-SPUTTERED TL-1223 SUPERCONDUCTING THIN-FILMS
    JUANG, JY
    HORNG, JH
    LIN, HC
    WANG, SJ
    FU, CM
    WU, KH
    UEN, TM
    GOU, YS
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1995, 5 (02) : 1689 - 1692
  • [22] Growth of Tl-1223 superconducting thin films by rapidly heating-up sintering technology
    Xie Qing-Lian
    Su Ling-Ling
    Jiang Yan-Ling
    Tang Ping-Ying
    Liu Li-Qin
    Yue Hong-Wei
    Chen Ming-Xian
    Huang Guo-Hua
    ACTA PHYSICA SINICA, 2018, 67 (13)
  • [23] The pre-oxidation process of electropolishing for the textured {113} <121> Ag substrate for Tl-1223 superconductor substrate
    Y. H. Kim
    D. Y. Jeong
    P. M. Shirage
    S. Y. Kim
    U. C. Chung
    W. S. Chung
    Metals and Materials International, 2007, 13 : 217 - 221
  • [24] Controllable growth and magneto-resistivity investigations on Tl-1223 superconducting films with high Tc
    Liang, Xuelian
    Niu, Zihan
    Li, Tianci
    Xing, Jian
    Guo, Rong
    Chen, Jihuang
    Zhao, Haiting
    Yang, Qian
    He, Ming
    Yan, Shaolin
    Feng, Min
    Ming, Xue
    Wen, Hai-Hu
    Ji, Lu
    CERAMICS INTERNATIONAL, 2023, 49 (05) : 8240 - 8247
  • [25] Investigation into microwave power dependence of high quality Tl-1223 thin films on LSAT substrate
    Jacob, MV
    Sundaresan, A
    Mazierska, J
    Tanaka, Y
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2005, 15 (02) : 3596 - 3599
  • [26] Magnetoresistivity measurements of Tl1Ba2Ca2Cu3Ox (Tl-1223) high temperature superconductor films synthesized via an electrodeposited precursor
    Natarajan, A
    Wang, W
    Ma, E
    Bhattacharya, RN
    Blaugher, RD
    MATERIALS LETTERS, 1999, 39 (01) : 58 - 62
  • [27] Magnetoresistivity measurements of Tl1Ba2Ca2Cu3Ox (Tl-1223) high temperature superconductor films synthesized via an electrodeposited precursor
    Microsystems Eng. Team , Dept. Mech. Eng., Louisiana Stt. U., Baton Rouge, LA 70803, United States
    不详
    Mater Lett, 1 (58-62):
  • [28] The Study of Purity Improvement on Tl-1223 Thin Films by DC Sputtering and Post-annealing Method
    X. X. Gao
    W. Xie
    Z. Wang
    X. J. Zhao
    M. He
    X. Zhang
    S. L. Yan
    L. Ji
    Journal of Superconductivity and Novel Magnetism, 2014, 27 : 1665 - 1670
  • [29] Preparation of Tl-2212 and -1223 superconductor thin films and their microwave properties
    Sundaresan, A
    Asada, H
    Crisan, A
    Nie, JC
    Kito, H
    Iyo, A
    Tanaka, Y
    Kusunoki, M
    Ohshima, S
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 388 : 473 - 474
  • [30] Properties of Tl-1223 superconducting thick films fabricated from precursor inks using a thallium vapor transport process
    Kampwirth, R.T., 1954, IEEE, Piscataway, NJ, United States (05):
12345