DEGRADATION OF FATIGUE PROPERTIES OF WELD-BONDED ALUMINUM EXPOSED TO MOISTURE AND ELEVATED-TEMPERATURE

被引：1

作者：

WANG, PC ^{[1
]}

MABERY, P ^{[1
]}

CHISHOLM, CK ^{[1
]}

机构：

[1] FORD MOTOR CO,DEARBORN,MI 48121

来源：

JOURNAL OF ADHESION | 1993年 / 43卷 / 1-2期

关键词：

WELD-BONDING ALUMINUM; VEHICLE APPLICATIONS; MOISTURE AND ELEVATED TEMPERATURE; CONCURRENT FATIGUE TESTING; FATIGUE STRENGTH; ADHESIVE PLASTICIZATION;

D O I：

10.1080/00218469308026592

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Experiments have been completed in order to characterize the fatigue behavior of weld-bonded aluminum 5754-O/bis-phenol-A epoxy adhesive joints subjected to 100% relative humidity at 38-degrees-C. It was found that the presence of water vapor at elevated temperature decreases the fatigue strength of weld-bonded joints by as much as 33% at 5 x 10(6) cycles. Optical microscopy, scanning electron microscopy, dynamic mechanical analysis, and tensile testing of fatigued specimens and exposed bulk adhesive revealed that fatigue strength degradation is mainly due to the plasticization and micro-cracking of adhesive by the water vapor.

引用

页码：121 / 137

页数：17

共 50 条

[41] ELEVATED-TEMPERATURE PROPERTIES OF URANIUM CARBIDE
CRANE, J
GORDON, E
[J]. TRANSACTIONS OF THE AMERICAN NUCLEAR SOCIETY, 1964, 7 (01): : 100 - &
[42] ANALYSIS OF ELEVATED-TEMPERATURE FATIGUE AND CREEP CRACK GROWTH
DONER, M
[J]. MECHANICAL ENGINEERING, 1976, 98 (02): : 82 - 82
[43] ELEVATED-TEMPERATURE HIGH-STRAIN FATIGUE OF METALS
HILL, GJ
THORNTON, DV
QUAASS, ST
[J]. JOURNAL OF THE INSTITUTE OF METALS, 1965, 93 : 451 - +
[44] EFFECTS OF ELECTRODE COVERINGS ON ELEVATED-TEMPERATURE PROPERTIES OF AUSTENITIC STAINLESS-STEEL WELD METAL
BINKLEY, NC
GOODWIN, GM
HARMAN, DG
[J]. WELDING JOURNAL, 1973, 52 (07) : S306 - S311
[45] ELEVATED-TEMPERATURE FATIGUE OF PRESSURE-VESSEL STEELS
PENSE, AW
STOUT, RD
[J]. WELDING JOURNAL, 1975, 54 (08) : S247 - S252
[46] HIGH-STRAIN FATIGUE TESTING AT ELEVATED-TEMPERATURE
SKELTON, RP
[J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1982, 35 (06) : 519 - +
[47] SIMULATION OF ELEVATED-TEMPERATURE ALUMINUM METALLIZATION USING SIMBAD
DEW, SK
SMY, T
BRETT, MJ
[J]. IEEE TRANSACTIONS ON ELECTRON DEVICES, 1992, 39 (07) : 1599 - 1606
[48] ANALYSIS OF ELEVATED-TEMPERATURE FATIGUE AND CREEP CRACK GROWTH
DONER, M
[J]. JOURNAL OF ENGINEERING FOR POWER-TRANSACTIONS OF THE ASME, 1976, 98 (04): : 473 - 479
[49] ELEVATED-TEMPERATURE BEHAVIOR OF THERMOMECHANICALLY TREATED 6061 ALUMINUM
RACK, HJ
[J]. SCRIPTA METALLURGICA, 1978, 12 (09): : 777 - 779
[50] CAVITATION EROSION OF COPPER AND ALUMINUM IN WATER AT ELEVATED-TEMPERATURE
AURET, JG
DAMM, OFRA
WRIGHT, GJ
ROBINSON, FPA
[J]. TRIBOLOGY INTERNATIONAL, 1993, 26 (06) : 421 - 429

← 1 2 3 4 5 →