DEGRADATION OF FATIGUE PROPERTIES OF WELD-BONDED ALUMINUM EXPOSED TO MOISTURE AND ELEVATED-TEMPERATURE

被引：1

作者：

WANG, PC ^{[1
]}

MABERY, P ^{[1
]}

CHISHOLM, CK ^{[1
]}

机构：

[1] FORD MOTOR CO,DEARBORN,MI 48121

来源：

JOURNAL OF ADHESION | 1993年 / 43卷 / 1-2期

关键词：

WELD-BONDING ALUMINUM; VEHICLE APPLICATIONS; MOISTURE AND ELEVATED TEMPERATURE; CONCURRENT FATIGUE TESTING; FATIGUE STRENGTH; ADHESIVE PLASTICIZATION;

D O I：

10.1080/00218469308026592

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Experiments have been completed in order to characterize the fatigue behavior of weld-bonded aluminum 5754-O/bis-phenol-A epoxy adhesive joints subjected to 100% relative humidity at 38-degrees-C. It was found that the presence of water vapor at elevated temperature decreases the fatigue strength of weld-bonded joints by as much as 33% at 5 x 10(6) cycles. Optical microscopy, scanning electron microscopy, dynamic mechanical analysis, and tensile testing of fatigued specimens and exposed bulk adhesive revealed that fatigue strength degradation is mainly due to the plasticization and micro-cracking of adhesive by the water vapor.

引用

页码：121 / 137

页数：17

共 50 条

[31] ELEVATED-TEMPERATURE TORSIONAL FATIGUE TESTING FIXTURE
SOCIE, DF
ANTOLOVICH, SD
CHANANI, GR
[J]. REVIEW OF SCIENTIFIC INSTRUMENTS, 1972, 43 (12): : 1784 - +
[32] Elevated-temperature coarsening behavior in aluminum alloys
Mahidhara, RK
[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 1997, 6 (01) : 102 - 105
[33] Elevated-temperature coarsening behavior in aluminum alloys
R.K Mahidhara
[J]. Journal of Materials Engineering and Performance, 1997, 6 : 102 - 105
[34] ELEVATED-TEMPERATURE TENSILE PROPERTIES OF WELD-DEPOSITED AUSTENITIC STAINLESS-STEELS
WARD, AL
BLACKBURN, LD
[J]. JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1976, 98 (03): : 213 - 220
[35] ELEVATED-TEMPERATURE TENSILE PROPERTIES OF WELD-DEPOSITED AUSTENITIC STAINLESS-STEELS
WARD, AL
BLACKBURN, LD
[J]. MECHANICAL ENGINEERING, 1976, 98 (06): : 112 - 112
[36] FATIGUE AND CREEP-FATIGUE TESTING OF BELLOWS AT ELEVATED-TEMPERATURE
YAMAMOTO, S
ISOBE, K
OHTE, S
TANAKA, N
OZAKI, S
KIMURA, K
[J]. JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 1988, 110 (03): : 301 - 307
[37] ESTIMATION OF LOW-CYCLE FATIGUE LIFE AT ELEVATED-TEMPERATURE BY TENSILE PROPERTIES
KANAZAWA, K
[J]. TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 (05): : S549 - S549
[38] Effect of Inner Step Length on the Stress Distribution in Weld-bonded Single Lap Aluminum Joint
Li, Jian-Li
Wang, Peng
You, Min
[J]. PROCEEDINGS OF THE 4TH 2016 INTERNATIONAL CONFERENCE ON MATERIAL SCIENCE AND ENGINEERING (ICMSE 2016), 2016, 101 : 399 - 403
[39] ELEVATED-TEMPERATURE MECHANICAL-PROPERTIES OF ALUMINUM-LITHIUM-COPPER ALLOYS
BRETZ, PE
VASUDEVAN, AK
[J]. JOURNAL OF METALS, 1983, 35 (08): : A16 - A16
[40] MODIFICATION OF XLPE EXPOSED TO PARTIAL DISCHARGES AT ELEVATED-TEMPERATURE
GAMEZGARCIA, M
BARTNIKAS, R
WERTHEIMER, MR
[J]. IEEE TRANSACTIONS ON ELECTRICAL INSULATION, 1990, 25 (04): : 688 - 692

← 1 2 3 4 5 →