Twin-Wire Pulsed Tandem Gas Metal Arc Welding of API X80 Steel Linepipe

被引：0
|
作者：
Wu, Wenhao [1 ]
Zhao, Ming [1 ]
Wang, Haiyan [1 ]
Zhang, Yanxia [1 ]
Wu, Tong [1 ]
机构：
[1] China Univ Petr, Coll Mech & Elect Engn, Qingdao, Peoples R China
来源：
INTERNATIONAL JOURNAL OF CORROSION | 2018年 / 2018卷
基金：
中国国家自然科学基金;
关键词：
D O I：
暂无
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
Twin-Wire Pulsed Tandem Gas Metal Arc Welding process with high welding production efficiency was used to join the girth weld seam of API X80 steel linepipe of 18.4 mm wall thickness and 1422 mm diameter. The macrostructure, microstructure, hardness, and electrochemical corrosion behavior of welded joints were studied. Effects of temperature and Cl- concentration on the corrosion behavior of base metal and weld metal were investigated. Results show that the welded joint has good morphology, mechanical properties, and corrosion resistance. The corrosion resistance of both the base metal and the weld metal decreases with increasing temperature or Cl- concentration. In the solution with high Cl(-)concentration, the base metal and weld metal are more susceptible to pitting. The corrosion resistance of the weld metal is slightly lower than that of the base metal.
引用
收藏
页数：11
相关论文
共 50 条
  • [31] Twin-wire Submerged Arc Welding Process of a High-strength Low-alloy Steel
    Yang Xiuzhi
    Xu Qinghua
    Yin Niandong
    Xiao Xinhua
    [J]. JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2011, 26 (01): : 114 - 117
  • [32] Twin-wire Submerged Arc Welding Process of a High-strength Low-alloy Steel
    杨秀芝
    [J]. Journal of Wuhan University of Technology(Materials Science), 2011, (01) : 114 - 117
  • [33] Experimental and numerical investigation on combined girth welding of API X80 pipeline steel
    Zhao, M.
    Wei, F.
    Huang, W. Q.
    Lei, Y.
    [J]. SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2015, 20 (07) : 622 - 630
  • [34] Arc Interference Behavior during Twin Wire Gas Metal Arc Welding Process
    Ye, Dingjian
    Hua, Xueming
    Wu, Yixiong
    [J]. ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2013, 2013
  • [35] Characterization of HAZ of API X70 Microalloyed Steel Welded by Cold-Wire Tandem Submerged Arc Welding
    Mohammadijoo, Mohsen
    Kenny, Stephen
    Collins, Laurie
    Henein, Hani
    Ivey, Douglas G.
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2017, 48A (05): : 2247 - 2259
  • [36] Characterization of HAZ of API X70 Microalloyed Steel Welded by Cold-Wire Tandem Submerged Arc Welding
    Mohsen Mohammadijoo
    Stephen Kenny
    Laurie Collins
    Hani Henein
    Douglas G. Ivey
    [J]. Metallurgical and Materials Transactions A, 2017, 48 : 2247 - 2259
  • [37] Environmental energy efficiency of single wire and tandem gas metal arc welding
    Sproesser, Gunther
    Chang, Ya-Ju
    Pittner, Andreas
    Finkbeiner, Matthias
    Rethmeier, Michael
    [J]. WELDING IN THE WORLD, 2017, 61 (04) : 733 - 743
  • [38] Environmental energy efficiency of single wire and tandem gas metal arc welding
    Gunther Sproesser
    Ya-Ju Chang
    Andreas Pittner
    Matthias Finkbeiner
    Michael Rethmeier
    [J]. Welding in the World, 2017, 61 : 733 - 743
  • [39] Analysis and estimation of yield strength of API X80 linepipe steel pipe by low-cycle fatigue tests
    Seok Su Sohn
    Seung Youb Han
    Sang Yong Shin
    Jin-ho Bae
    Kisoo Kim
    Nack J. Kim
    Hyoung Seop Kim
    Sunghak Lee
    [J]. Metals and Materials International, 2012, 18 : 597 - 606
  • [40] Analysis and estimation of yield strength of API X80 linepipe steel pipe by low-cycle fatigue tests
    Sohn, Seok Su
    Han, Seung Youb
    Shin, Sang Yong
    Bae, Jin-ho
    Kim, Kisoo
    Kim, Nack J.
    Kim, Hyoung Seop
    Lee, Sunghak
    [J]. METALS AND MATERIALS INTERNATIONAL, 2012, 18 (04) : 597 - 606
12345