Twin-Wire Pulsed Tandem Gas Metal Arc Welding of API X80 Steel Linepipe

被引：0
|
作者：
Wu, Wenhao [1 ]
Zhao, Ming [1 ]
Wang, Haiyan [1 ]
Zhang, Yanxia [1 ]
Wu, Tong [1 ]
机构：
[1] China Univ Petr, Coll Mech & Elect Engn, Qingdao, Peoples R China
来源：
INTERNATIONAL JOURNAL OF CORROSION | 2018年 / 2018卷
基金：
中国国家自然科学基金;
关键词：
D O I：
暂无
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
Twin-Wire Pulsed Tandem Gas Metal Arc Welding process with high welding production efficiency was used to join the girth weld seam of API X80 steel linepipe of 18.4 mm wall thickness and 1422 mm diameter. The macrostructure, microstructure, hardness, and electrochemical corrosion behavior of welded joints were studied. Effects of temperature and Cl- concentration on the corrosion behavior of base metal and weld metal were investigated. Results show that the welded joint has good morphology, mechanical properties, and corrosion resistance. The corrosion resistance of both the base metal and the weld metal decreases with increasing temperature or Cl- concentration. In the solution with high Cl(-)concentration, the base metal and weld metal are more susceptible to pitting. The corrosion resistance of the weld metal is slightly lower than that of the base metal.
引用
收藏
页数：11
相关论文
共 50 条
  • [21] An overview on the cold wire pulsed gas metal arc welding
    R. A. Ribeiro
    P. D. C. Assunção
    E. B. F. Dos Santos
    E. M. Braga
    A. P. Gerlich
    [J]. Welding in the World, 2020, 64 : 123 - 140
  • [22] An overview on the cold wire pulsed gas metal arc welding
    Ribeiro, R.A.
    Gerlich, A.P.
    Assunção, P.D.C.
    Braga, E.M.
    Dos Santos, E.B.F.
    [J]. Rivista Italiana della Saldatura, 2021, 73 (03): : 277 - 302
  • [23] Corrosion resistance of stainless steel layer prepared by twin-wire indirect arc surfacing welding
    Wu, Dongting
    An, Qi
    Zhao, Guanlin
    Zhang, Yongang
    Zou, Yong
    [J]. VACUUM, 2020, 177
  • [24] IMPACT OF WELDING PARAMETERS ON WELD SEAM PROPERTIES OF SEAMLESS X80 LINEPIPE STEEL GRADE
    Biuns, Claas
    Wiebe, Joerg
    Niklasch, Dorothee
    Mahn, Denise
    Schmidt, Tanja
    [J]. PROCEEDINGS OF THE 10TH INTERNATIONAL PIPELINE CONFERENCE - 2014, VOL 3, 2014,
  • [25] Numerical simulation of temperature field in multiple-wire submerged arc welding of X80 pipeline steel
    Yan, Chunyan
    Jiang, Han
    Wu, Lichao
    Kan, Chenxia
    Yu, Wen
    [J]. 2017 3RD INTERNATIONAL CONFERENCE ON ENVIRONMENTAL SCIENCE AND MATERIAL APPLICATION (ESMA2017), VOLS 1-4, 2018, 108
  • [26] Influence of transverse auxiliary magnetic field on weld formation and joint quality in spiral submerged arc welding of X80 steel linepipe
    Zhao, Ming
    Feng, Xuezhi
    Cui, Zhaopeng
    Wang, Junjie
    Chen, Hongyuan
    [J]. WELDING IN THE WORLD, 2022, 66 (12) : 2497 - 2508
  • [27] Analysis of microstructure and corrosion resistance of X80 pipeline steel welded by shielded metal arc welding
    Zhao, Wei
    Zou, Yong
    Xia, Dianxiu
    Zou, Zengda
    [J]. Hanjie Xuebao/Transactions of the China Welding Institution, 2016, 37 (10): : 51 - 54
  • [28] Influence of transverse auxiliary magnetic field on weld formation and joint quality in spiral submerged arc welding of X80 steel linepipe
    Ming Zhao
    Xuezhi Feng
    Zhaopeng Cui
    Junjie Wang
    Hongyuan Chen
    [J]. Welding in the World, 2022, 66 : 2497 - 2508
  • [29] Twin-wire submerged arc welding process of a high-strength low-alloy steel
    Xiuzhi Yang
    Qinghua Xu
    Niandong Yin
    Xinhua Xiao
    [J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2011, 26 : 114 - 117
  • [30] Hybrid laser arc welding of X80 and X120 steel grade
    Gook, S.
    Gumenyuk, A.
    Rethmeier, M.
    [J]. SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2014, 19 (01) : 15 - 24
12345