Effects of Cryogenic Forging and Anodization on the Mechanical Properties of AA 7075-T73 Aluminum Alloys

被引：0
|
作者：
Teng-Shih Shih
Tien-Wei Liao
Wen-Nong Hsu
机构：
[1] National Central University,Department of Mechanical Engineering
来源：
Journal of Materials Engineering and Performance | 2016年 / 25卷
关键词：
7075-T73; anodization; cryogenic forging; precipitates;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this study, high-strength AA7075 alloy samples were cryogenically forged after annealing and then subjected to solution and aging treatments. The cryogenically forged 7075-T73 alloy samples displayed equiaxed fine grains associated with abundant fine precipitates in their matrix. Compared with conventional 7075-T73 alloy samples, the cryogenically forged samples exhibited an 8-12% reduction in tensile strength and an increased fatigue strength and higher corrosion resistance. The fatigue strength measured at 107 cycles was 225 MPa in the bare samples; the strength was increased to 250 MPa in the cryogenically forged samples. The effect of anodization on the corrosion resistance of the bare samples was improved from (Ecorr) −0.80 to −0.61 V.
引用
收藏
页码：1211 / 1218
页数：7
相关论文
共 50 条
  • [31] Single and Multi-Response Optimization and Validation of Mechanical Properties in Dissimilar Friction Stir Welded AA2219-T87 and AA7075-T73 Alloys Using T-GRA
    Kumar, R. Dinesh
    Ul Hassan, M. S. Ilhar
    Muthukumaran, S.
    Venkateswaran, T.
    Sivakumar, D.
    [J]. EXPERIMENTAL TECHNIQUES, 2019, 43 (03) : 245 - 259
  • [32] Single and Multi-Response Optimization and Validation of Mechanical Properties in Dissimilar Friction Stir Welded AA2219-T87 and AA7075-T73 Alloys Using T-GRA
    R. Dinesh Kumar
    M. S. Ilhar Ul Hassan
    S. Muthukumaran
    T. Venkateswaran
    D. Sivakumar
    [J]. Experimental Techniques, 2019, 43 : 245 - 259
  • [33] Effects of cryogenic deformation on the microstructure and mechanical properties of high-strength aluminum alloys
    Wang, Dang
    Huang, Shiquan
    Yi, Youping
    He, Hailin
    Li, Chen
    [J]. MATERIALS CHARACTERIZATION, 2022, 187
  • [34] Effect of Tool Temperature on Mechanical Properties and Microstructure of Thermo-Mechanically Processed AA6082 and AA7075 Aluminum Alloys
    Sajadifar, S., V
    Scharifi, E.
    Weidig, U.
    Steinhoff, K.
    Niendorf, T.
    [J]. HTM-JOURNAL OF HEAT TREATMENT AND MATERIALS, 2020, 75 (03): : 177 - 191
  • [35] ON CHEMICAL AND MECHANICAL PROPERTIES OF AA7075 T651
    Stefanica, Roxana-Gabriela
    Nejneru, Carmen
    Dima, Adrian
    [J]. MODTECH 2010: NEW FACE OF TMCR, PROCEEDINGS, 2010, : 579 - 582
  • [36] EVALUATION OF ELECTROPLATING EFFECTS ON MECHANICAL PROPERTIES AND FATIGUE OF AA7075-T6 ALLOY
    Omran, Salman H.
    Shandook, Ahmed A.
    Ali, Moaz H.
    Wahhab, Hasanain A. Abdul
    [J]. JOURNAL OF ENGINEERING SCIENCE AND TECHNOLOGY, 2023, : 225 - 239
  • [37] Corrosion Behavior of AA7075-T73 Aluminum Alloy During Machining of Aeronautical Components
    Lourenco, Julio Cesar
    Marie Robin, Alain Laurent
    Sodero Toledo Faria, Maria Ismenia
    Prisco, Luciana Prates
    Puccini, Mario Coelho
    de Oliveira, Lucemar Diogo
    [J]. MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, 2019, 22 (04):
  • [38] Evaluation of post-weld heat treatments to restore the corrosion resistance of friction stir welded aluminum alloy 7075-T73 vs. 7075-T6
    Widener, C. A.
    Burford, D. A.
    Kumar, B.
    Talia, J. E.
    Tweedy, B.
    [J]. THERMEC 2006, PTS 1-5, 2007, 539-543 : 3781 - +
  • [39] Microstructure and mechanical properties of friction stir welded dissimilar aluminum joints of AA2024-T3 and AA7075-T6
    Khodir, Saad Ahmed
    Shibayanagi, Toshiya
    [J]. MATERIALS TRANSACTIONS, 2007, 48 (07) : 1928 - 1937
  • [40] MECHANISMS OF DISLOCATION-MOTION IN 7075-T73 ALUMINUM-ALLOY AT STRAIN RATES AROUND 105 S-1
    BURSTOW, CG
    LOVELL, MC
    RODGERS, AL
    [J]. MECHANICAL PROPERTIES OF MATERIALS AT HIGH RATES OF STRAIN 1989, 1989, 102 : 317 - 322
12345