Effects of Cryogenic Forging and Anodization on the Mechanical Properties of AA 7075-T73 Aluminum Alloys

被引：0
|
作者：
Teng-Shih Shih
Tien-Wei Liao
Wen-Nong Hsu
机构：
[1] National Central University,Department of Mechanical Engineering
来源：
Journal of Materials Engineering and Performance | 2016年 / 25卷
关键词：
7075-T73; anodization; cryogenic forging; precipitates;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this study, high-strength AA7075 alloy samples were cryogenically forged after annealing and then subjected to solution and aging treatments. The cryogenically forged 7075-T73 alloy samples displayed equiaxed fine grains associated with abundant fine precipitates in their matrix. Compared with conventional 7075-T73 alloy samples, the cryogenically forged samples exhibited an 8-12% reduction in tensile strength and an increased fatigue strength and higher corrosion resistance. The fatigue strength measured at 107 cycles was 225 MPa in the bare samples; the strength was increased to 250 MPa in the cryogenically forged samples. The effect of anodization on the corrosion resistance of the bare samples was improved from (Ecorr) −0.80 to −0.61 V.
引用
收藏
页码：1211 / 1218
页数：7
相关论文
共 50 条
  • [1] Effects of Cryogenic Forging and Anodization on the Mechanical Properties of AA 7075-T73 Aluminum Alloys
    Shih, Teng-Shih
    Liao, Tien-Wei
    Hsu, Wen-Nong
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2016, 25 (03) : 1211 - 1218
  • [2] Effects of Cryogenic Forging and Anodization on the Mechanical Properties and Corrosion Resistance of AA6066-T6 Aluminum Alloys
    Shih, Teng-Shih
    Yong, Hwa-Sheng
    Hsu, Wen-Nong
    [J]. METALS, 2016, 6 (03):
  • [3] The Effects of Anodization Treatment on the Microstructure and Fatigue Behavior of 7075-T73 Aluminum Alloy
    Shih, Teng-Shih
    Lee, Tin-Hou
    Jhou, Ying-Jhe
    [J]. MATERIALS TRANSACTIONS, 2014, 55 (08) : 1280 - 1285
  • [4] Experimental investigation on the post-fire mechanical properties of structural aluminum alloys 6061-T6 and 7075-T73
    Chen, Zhihua
    Lu, Jie
    Liu, Hongbo
    Liao, Xiangwei
    [J]. THIN-WALLED STRUCTURES, 2016, 106 : 187 - 200
  • [5] Femtosecond Laser Peening of Friction Stir Welded 7075-T73 Aluminum Alloys
    Kawashima, Terumasa
    Sano, Tomokazu
    Hirose, Akio
    Tsutsumi, Seiichiro
    Masaki, Kiyotaka
    Arakawa, Kazuto
    Hori, Hisashi
    [J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2018, 262 : 111 - 122
  • [6] Quantifying spectrum loading effects on fatigue crack growth in 7075-T73 aluminum
    Zion, HL
    Johnson, WS
    Ball, DL
    Everett, RA
    [J]. JOURNAL OF THE AMERICAN HELICOPTER SOCIETY, 2000, 45 (01) : 11 - 18
  • [7] Microwaves Furnace Heat Effect on Aluminum Alloy 7075-T73
    Aziz, Sadiq Jaffer
    Shandookh, Ahmed Adnan
    Salman, Rafeef Jumaa
    [J]. 2018 INTERNATIONAL CONFERENCE ON ADVANCE IN SUSTAINABLE ENGINEERING AND ITS APPLICATION (ICASEA), 2018, : 238 - 243
  • [8] Surface Characterization of 7075-T73 Aluminum Exposed to Anodizing Pretreatment Solutions
    Terence P. Savas
    James C. Earthman
    [J]. Journal of Materials Engineering and Performance, 2008, 17 : 674 - 681
  • [9] Surface characterization of 7075-T73 aluminum exposed to anodizing pretreatment solutions
    Savas, Terence P.
    Earthman, James C.
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2008, 17 (05) : 674 - 681
  • [10] Fatigue Crack Nucleation Studies on Sulfuric Acid Anodized 7075-T73 Aluminum
    Terence P. Savas
    James C. Earthman
    [J]. Journal of Materials Engineering and Performance, 2014, 23 : 2131 - 2138
12345