Regulation of the mechanical properties of thermoplastic carbon fiber-reinforced plastics by changing their production conditions and surface treatment of the fibers

The effect of technological parameters of processing and surface treatment of carbon fibers on the mechanical properties of carbon fiber-reinforced plastics (CFRPs) was investigated. The copolymer of 1,3,5-trioxane with 1,3-dioxolane was used as the polymer matrix, and medium-modulus hydrated cellulose Ural LO-24 carbon fibers served as the reinforcing filler. The polymer matrix was mixed with the carbon fibers by the method of combined extrusion. The dependence of the mechanical properties of CFRPs on the technological parameters of screw-disk extrusion was studied. It was found that the properties of the composites were greatly affected by the size of the working disk gap, the disk rotation rate, and the temperature in the zone of normal stresses. The surface of the carbon fibers was activated with atmospheric oxygen in the temperature range of 450–600°C, with mass loss of the fibers no greater than 3–4%. A 30–40% increase in the mechanical properties of the CFRPs was achieved. A decrease in the melt index of the 1,3,5-trioxane copolymer with 1,3-dioxolane reinforced with oxidized carbon fibers was observed, which should be taken into account in processing the composites into products. Introduction of carbon fibers in the 1,3,5-trioxane copolymer with 1,3-dioxolane allows us to increase the wear resistance and decrease the friction coefficient, which makes it possibile to use these materials in the friction units of machines and mechanisms, such as plain bearings, gears, and flange packings.