Oxidation of P92 steel weldment between 600 and 800 °C in air

被引：0
|
作者：
Sang-Hwan Bak
Dong-Bok Lee
机构：
[1] SungkyunkwanUniversity,School of Advanced Materials Science and Engineering
来源：
Metals and Materials International | 2011年 / 17卷
关键词：
alloys; welding; oxidation; scanning electron microscopy (SEM); P92 steel;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
P92 alloy with a composition of Fe-9.1Cr-0.5Mo-1.7W (wt.%) was welded, and its oxidation behavior was studied at 600, 700 and 800 °C for up to 6 months in air. The oxidation resistance decreased in the order of the base metal, weld metal, and the heat affected zone. The morphology and the composition of the scales formed on these samples were similar. The scales were either uniform in thickness or nodular. The scales consisted mainly of Fe2O3. As oxidation progressed, thick, nodular oxide scales formed. The alloying elements such as Cr, W, and Mn tended to incorporate in the lower part of the oxide scale.
引用
收藏
页码：949 / 956
页数：7
相关论文
共 50 条
  • [41] Creep Behavior of P92 Steel in the Steam Environment at 600 A°C Using Miniature Three-Point Bend Test
    Huang, Yuhui
    Xuan, Fu-Zhen
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2016, 25 (12) : 5440 - 5449
  • [42] Fireside Corrosion of P92 Steel with Mixed Sulfate Deposit at 650 °C
    Shang, C. G.
    Xin, L.
    Xu, Q. L.
    Lu, Y. H.
    OXIDATION OF METALS, 2020, 94 (3-4): : 323 - 341
  • [43] Fireside Corrosion of P92 Steel with Mixed Sulfate Deposit at 650 °C
    C. G. Shang
    L. Xin
    Q. L. Xu
    Y. H. Lu
    Oxidation of Metals, 2020, 94 : 323 - 341
  • [44] Relationship between Laves phase and the impact brittleness of P92 steel reevaluated
    Zhong, Wanli
    Wang, Wei
    Yang, Xu
    Li, Wensheng
    Yan, Wei
    Sha, Wei
    Wang, Wei
    Shan, Yiyin
    Yang, Ke
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 639 : 252 - 258
  • [45] Effects of Pack Cementation Aluminizing and Vapor Aluminizing on Oxidation Behavior of P92 Steel in Saturated Steam at 650 °C
    Zhou Yongli
    Lu Jintao
    Huang Jinyang
    Yang Zhen
    Yuan Yong
    Gu Yuefeng
    Zhao Qinxin
    CHINA SURFACE ENGINEERING, 2020, 33 (04) : 111 - 120
  • [46] High Temperature Deformation Behavior of P92 Steel
    Alsagabi, Sultan
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2016, 69 (08) : 1513 - 1518
  • [47] Creep-to-rupture of the steel P92 at 650 °C in oxygen-controlled stagnant lead in comparison to air
    Yurechko, Mariya
    Schroer, Carsten
    Skrypnik, Aleksandr
    Wedemeyer, Olaf
    Konys, Juergen
    JOURNAL OF NUCLEAR MATERIALS, 2013, 432 (1-3) : 78 - 86
  • [48] High Temperature Deformation Behavior of P92 Steel
    Sultan Alsagabi
    Transactions of the Indian Institute of Metals, 2016, 69 : 1513 - 1518
  • [49] Microstructural Evolution of P92 Steel during Creep
    Zhao, Qinxin
    Li, Ting
    Deng, Xiang
    Cheng, Dingnan
    ADVANCES IN MATERIALS TECHNOLOGY FOR FOSSIL POWER PLANTS: PROCEEDINGS FROM THE SIXTH INTERNATIONAL CONFERENCE, 2010, 2011, : 693 - 704
  • [50] Characteristics of Residual Stress in P92 Steel Welds
    Yoo, Keun Bong
    Choi, Hyun Sun
    Kim, Eui Hyun
    Kim, Jae Hoon
    ADVANCED MATERIALS AND PROCESSING, 2007, 26-28 : 1175 - +
12345