Oxidation of P92 steel weldment between 600 and 800 °C in air

被引：0
|
作者：
Sang-Hwan Bak
Dong-Bok Lee
机构：
[1] SungkyunkwanUniversity,School of Advanced Materials Science and Engineering
来源：
Metals and Materials International | 2011年 / 17卷
关键词：
alloys; welding; oxidation; scanning electron microscopy (SEM); P92 steel;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
P92 alloy with a composition of Fe-9.1Cr-0.5Mo-1.7W (wt.%) was welded, and its oxidation behavior was studied at 600, 700 and 800 °C for up to 6 months in air. The oxidation resistance decreased in the order of the base metal, weld metal, and the heat affected zone. The morphology and the composition of the scales formed on these samples were similar. The scales were either uniform in thickness or nodular. The scales consisted mainly of Fe2O3. As oxidation progressed, thick, nodular oxide scales formed. The alloying elements such as Cr, W, and Mn tended to incorporate in the lower part of the oxide scale.
引用
收藏
页码：949 / 956
页数：7
相关论文
共 50 条
  • [21] Creep, fatigue, and creep-fatigue crack growth behaviours of P92 steel at 600 °C
    Alang, N. A.
    Nikbin, K.
    STRENGTH FRACTURE AND COMPLEXITY, 2022, 15 (01) : 29 - 45
  • [22] Creep Behavior of P92 and P92 Welds at 675 °C
    Tanner, David W. J.
    Saber, Mohammed
    Sun, Wei
    Hyde, Thomas H.
    JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2013, 135 (05):
  • [23] Ripening behavior of M23C6 carbides in P92 steel during aging at 800 °C
    Xu Yang
    Bo Liao
    Fu-ren Xiao
    Wei Yan
    Yi-yin Shan
    Ke Yang
    Journal of Iron and Steel Research International, 2017, 24 : 858 - 864
  • [24] CREEP BEHAVIOUR OF P92 AND P92 WELDS AT 675°C
    Tanner, David W. J.
    Saber, Mohammed
    Sun, Wei
    Hyde, Thomas H.
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, PVP 2012, VOL 6, PTS A AND B, 2012, : 359 - 368
  • [25] Ripening behavior of M23C6 carbides in P92 steel during aging at 800°C
    Xu Yang
    Bo Liao
    Fu-ren Xiao
    Wei Yan
    Yi-yin Shan
    Ke Yang
    Journal of Iron and Steel Research(International), 2017, 24 (08) : 858 - 864
  • [26] Ripening behavior of M23C6 carbides in P92 steel during aging at 800 °C
    Yang, Xu
    Liao, Bo
    Xiao, Fu-ren
    Yan, Wei
    Shan, Yi-yin
    Yang, Ke
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2017, 24 (08) : 858 - 864
  • [27] Influence of Multi-Thermal Cycle and Constraint Condition on Residual Stress in P92 Steel Weldment
    Deng Dean
    Ren Sendong
    Li Suo
    Zhang Yanbin
    ACTA METALLURGICA SINICA, 2017, 53 (11) : 1532 - 1540
  • [28] CREEP PROPERTIES OF STEEL P92
    Vlasak, Tomas
    Hakl, Jan
    Kasl, Josef
    Cmakal, Josef
    METAL 2010: 19TH INTERNATIONAL METALLURGICAL AND MATERIALS CONFERENCE, 2010, : 398 - 402
  • [29] Investigation on the Enhanced Oxidation of Ferritic/Martensitic Steel P92 in Pure Steam
    Yuan, Juntao
    Wu, Ximao
    Wang, Wen
    Zhu, Shenglong
    Wang, Fuhui
    MATERIALS, 2014, 7 (04): : 2772 - 2783
  • [30] Creep behaviour of laser welded P92 steel sheets in different heat treatment and welding conditions at 600°C
    Dilthey, Ulrich
    El-Magd, Essam A.
    Brandenburg, Anette
    Gebhard, Jürgen
    Piontek, Damian
    Welding and Cutting, 2006, 5 (03): : 148 - 153
12345