Oxidation of P92 steel weldment between 600 and 800 °C in air

被引：0
|
作者：
Sang-Hwan Bak
Dong-Bok Lee
机构：
[1] SungkyunkwanUniversity,School of Advanced Materials Science and Engineering
来源：
Metals and Materials International | 2011年 / 17卷
关键词：
alloys; welding; oxidation; scanning electron microscopy (SEM); P92 steel;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
P92 alloy with a composition of Fe-9.1Cr-0.5Mo-1.7W (wt.%) was welded, and its oxidation behavior was studied at 600, 700 and 800 °C for up to 6 months in air. The oxidation resistance decreased in the order of the base metal, weld metal, and the heat affected zone. The morphology and the composition of the scales formed on these samples were similar. The scales were either uniform in thickness or nodular. The scales consisted mainly of Fe2O3. As oxidation progressed, thick, nodular oxide scales formed. The alloying elements such as Cr, W, and Mn tended to incorporate in the lower part of the oxide scale.
引用
收藏
页码：949 / 956
页数：7
相关论文
共 50 条
  • [1] Oxidation of P92 Steel Weldment Between 600 and 800°C in Air
    Bak, Sang-Hwan
    Lee, Dong-Bok
    METALS AND MATERIALS INTERNATIONAL, 2011, 17 (06) : 949 - 956
  • [2] Characterization of creep deformation and rupture behaviour of P92 steel weldment at 600 degrees C
    Alang, N. A.
    JOURNAL OF MECHANICAL ENGINEERING AND SCIENCES, 2018, 12 (03) : 3976 - 3987
  • [3] Creep rupture behaviour of P92 steel weldment
    Wang Xue
    Pan Qian-gang
    Liu Zhi-jun
    Zeng Hui-qiang
    Tao Yong-shun
    ENGINEERING FAILURE ANALYSIS, 2011, 18 (01) : 186 - 191
  • [4] Effect of Shot Peening on the Surface Oxidation of P92 Steel in the Steam Environment at 600 °C
    Huang, Yuhui
    Xuan, Fu-Zhen
    JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2022, 144 (05):
  • [5] Creep behavior and microstructural damage of martensitic P92 steel weldment
    Kim, Bumjoon
    Jeong, Chanseo
    Lim, Byeongsoo
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 483-84 : 544 - 546
  • [6] Experimental Characterisation and Modelling of the Creep Properties of a P92 Steel Weldment
    Petry, C.
    Gariboldi, E.
    CREEP & FRACTURE IN HIGH TEMPERATURE COMPONENTS: DESIGN & LIFE ASSESSMENT ISSUES, PROCEEDINGS, 2009, : 189 - +
  • [7] Experimental characterisation and modelling of the creep properties of a P92 steel weldment
    Petry, C.
    Gariboldi, E.
    MATERIALS AT HIGH TEMPERATURES, 2010, 27 (01) : 1 - 10
  • [8] TYPE IV CREEP RUPTURE CHARACTERISTICS OF P92 STEEL WELDMENT
    Wang Xue
    Pan Qiangang
    Tao Yongshun
    Zhang Yinglin
    Zeng Huiqiang
    Liu Hong
    ACTA METALLURGICA SINICA, 2012, 48 (04) : 427 - 434
  • [9] Creep crack growth in P92 and P122 alloy steel weldment
    Jeong, CS
    Bae, SY
    Lim, BS
    ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4, 2005, 297-300 : 446 - 451
  • [10] Microstructure and type IV cracking behavior of HAZ in P92 steel weldment
    Wang Xue
    Pan Qian-gang
    Ren Yao-yao
    Shang Wei
    Zeng Hui-qiang
    Liu Hong
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 552 : 493 - 501
12345