Effects of hydrothermal aging on glass–fiber/polyetherimide (PEI) composites

被引：1

作者：

Taner Yilmaz

Tamer Sinmazcelik

机构：

[1] Kocaeli University,Civil Aviation College

[2] Kocaeli University,Mechanical Engineering Department

来源：

Journal of Materials Science | 2010年 / 45卷

关键词：

Thermal Cycle; Dynamic Mechanical Thermal Analysis; Fiber Protrusion; Flexural Modulus; Dynamic Mechanical Thermal Analysis;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The moisture absorption behavior and the influence of moisture on thermal and mechanical properties of glass–fiber/polyetherimide (PEI) laminates have been investigated. The laminates were exposed to hydrothermal aging at two different temperatures and high moisture rates. The properties of as-received and hydrothermally aged samples were compared. The hydrothermally aged laminates contained a large amount of moisture which caused decrease in the glass transition temperature and deterioration in mechanical properties (interlaminar shear strength, flexural modulus, bearing strength, etc.). Fractographic analysis revealed interfacial debonding as the dominant failure mechanism, indicating a strong influence of water degradation on fracture toughness results. Alterations in visco-elastic properties of glass/PEI composite which was exposed to hydrothermal aging were analyzed with the dynamic mechanical thermal analysis (DMTA) method. DMTA tests give evidence of plasticization of the PEI matrix.

引用

页码：399 / 404

页数：5

共 50 条

[31] Effects of hydrothermal aging on the dielectric properties of epoxy composites
Gonon, P
Bourdelais, S
Lesaint, O
Hong, TP
Guuinic, P
Debruyne, H
PROCEEDINGS OF THE 7TH INTERNATIONAL CONFERENCE ON PROPERTIES AND APPLICATIONS OF DIELECTRIC MATERIALS, VOLS 1-3, 2003, : 936 - 939
[32] The Role of Interfacial Effects in Hydrothermal Aging of Aramid Composites
A. A. Dalinkevich
T. A. Nenasheva
I. G. Kalinina
Protection of Metals and Physical Chemistry of Surfaces, 2021, 57 : 352 - 360
[33] The Role of Interfacial Effects in Hydrothermal Aging of Aramid Composites
Dalinkevich, A. A.
Nenasheva, T. A.
Kalinina, I. G.
PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2021, 57 (02) : 352 - 360
[34] Effects of Hydrothermal Seawater Aging on the Mechanical Properties and Water Absorption of Glass/Aramid/Epoxy Hybrid Composites
Oguz, Z. A.
Erklig, A.
Bozkurt, O. Y.
INTERNATIONAL POLYMER PROCESSING, 2021, 36 (01) : 79 - 93
[35] HYGROTHERMAL AGING AND FRACTURE OF GLASS-FIBER EPOXY COMPOSITES
ANSTICE, PD
BEAUMONT, PWR
JOURNAL OF MATERIALS SCIENCE, 1983, 18 (11) : 3404 - 3408
[36] Water immersion aging of polydicyclopentadiene resin and glass fiber composites
Hu, Yinghui
Li, Xiaochen
Lang, Augustus W.
Zhang, Yunpeng
Nutt, Steven R.
POLYMER DEGRADATION AND STABILITY, 2016, 124 : 35 - 42
[37] Effects of Hydrothermal Aging of Carbon Fiber Reinforced Polycarbonate Composites on Mechanical Performance and Sand Erosion Resistance
Fang, Mei
Zhang, Na
Huang, Ming
Lu, Bo
Lamnawar, Khalid
Liu, Chuntai
Shen, Changyu
POLYMERS, 2020, 12 (11) : 1 - 11
[38] Thermal Aging Effects on the Mechanical Behavior of Glass-Fiber-Reinforced Polyphenylene Sulfide Composites
Deng, Jiangang
Song, You
Xu, Zhuolin
Nie, Yu
Lan, Zhenbo
POLYMERS, 2022, 14 (07)
[39] Effects of Accelerated Climatic Aging on Volume and Surface Resistivity of Glass Fiber Reinforced Thermoset Composites
Prosr, Pavel
Polansky, Radek
Pihera, Josef
Kadlec, Petr
Hirman, Martin
Krejnicka, Tereza
Musil, Ondrej
Komarek, Josef
Pavlica, Richard
2020 INTERNATIONAL CONFERENCE ON DIAGNOSTICS IN ELECTRICAL ENGINEERING, DIAGNOSTIKA, 2020, : 243 - 246
[40] Hydrothermal Aging and Mechanical Property of Injection Molded Jute/Glass/Polypropylene Composites
Wang, Jian
Uawongsuwan, Putinun
Yang, Yuqiu
Inoya, Hiroyuki
Hojo, Toshihiko
Hamada, Hiroyuki
PROCEEDINGS OF THE ASME INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION, 2013, VOL 15, 2014,

← 1 2 3 4 5 →