The effect of etching on low-stress mechanical properties of polypropylene fabrics under helium/oxygen atmospheric pressure plasma

被引：0
|
作者：
Yoon J. Hwang
Jae Sang An
Marian G. McCord
Shin Woong Park
Bok Choon Kang
机构：
[1] Inha University,Department of Textile Engineering
[2] North Carolina State University,Department of Textile Engineering, Chemistry and Science, College of Textiles
[3] Apparel & Sweater Technical Service Center,Korea Institute of Industrial Technology
来源：
Fibers and Polymers | 2003年 / 4卷
关键词：
Atmospheric pressure plasma; KES-FB; XPS; SEM; Polypropylene;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Polypropylene nonwoven fabrics were exposed to He/O2 atmospheric pressure glow discharge plasma. Surface chemical analysis and contact angle measurement revealed the surface oxidation by formation of new functional groups after plasma treatment. Weight loss (%) measurement and scanning electron microscopy analysis showed a significant plasma etching effect. It was investigated in low-stress mechanical properties of the fabrics using Kawabata Evaluation System (KES-FB). The surface morphology change by plasma treatment increased surface friction due to an enhancement of fiber-to-fiber friction, resulting in change of other low-stress mechanical properties of fabric.
引用
收藏
页码：145 / 150
页数：5
相关论文
共 50 条
  • [21] Low-stress mechanical properties and fabric hand of cotton and polylactic acid fibre blended knitted fabrics
    Guruprasad, R.
    Prasad, G Krishna
    Prabu, G.T.V.
    Raj, Sheela
    Patil, P.G.
    Indian Journal of Fibre and Textile Research, 2018, 43 (03): : 381 - 384
  • [22] The effect of denier per filament (DPF) on low-stress mechanical and transmission behaviour of polyester filament fabrics
    Singh, Mukesh Kumar
    Behera, Bijoy Kumar
    JOURNAL OF THE TEXTILE INSTITUTE, 2022, 113 (07) : 1487 - 1495
  • [23] Effect of oxygen plasma etching on graphene's mechanical and electrical properties
    Jia, Pengfei
    Pan, Fengming
    Chen, Tianhang
    17TH IUMRS INTERNATIONAL CONFERENCE IN ASIA (IUMRS-ICA 2016), 2017, 182
  • [24] Comparative actions of a low pressure oxygen plasma and an atmospheric pressure glow discharge on the surface modification of polypropylene
    Choi, HS
    Rybkin, VV
    Titov, VA
    Shikova, TG
    Ageeva, TA
    SURFACE & COATINGS TECHNOLOGY, 2006, 200 (14-15): : 4479 - 4488
  • [25] Helium plasma treatment of ethanol-pretreated ramie fabrics for improving the mechanical properties of ramie/polypropylene composites
    Li, Ying
    Moyo, Senelisile
    Ding, Zhiyue
    Shan, Zhongde
    Qiu, Yiping
    INDUSTRIAL CROPS AND PRODUCTS, 2013, 51 : 299 - 305
  • [26] Effect of atmospheric pressure helium plasma on felting and low temperature dyeing of wool
    Panda, Prasanta Kumar
    Rastogi, Deepali
    Jassal, Manjeet
    Agrawal, Ashwini K.
    JOURNAL OF APPLIED POLYMER SCIENCE, 2012, 124 (05) : 4289 - 4297
  • [27] Development of hemp-blended cotton fabrics and analysis on handle behavior, low-stress mechanical and aesthetic properties
    Ahirwar, Meenakshi
    Behera, B. K.
    JOURNAL OF THE TEXTILE INSTITUTE, 2022, 113 (05) : 934 - 942
  • [28] The effect of atmospheric pressure helium plasma treatment on the surface and mechanical properties of ultrahigh-modulus polyethylene fibers
    Qiu, Y
    Zhang, C
    Hwang, YJ
    Bures, BL
    McCord, M
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2002, 16 (01) : 99 - 107
  • [29] Ring frame process parameters and fabric comfort. Part I - low-stress mechanical properties of fabrics
    Ishtiaque, S. M.
    Das, A.
    Kundu, A. K.
    JOURNAL OF THE TEXTILE INSTITUTE, 2014, 105 (03) : 348 - 355
  • [30] Low-stress mechanical properties of weft knitted fabrics produced from regular and compact cotton spun yarns
    Farid, Afrose Fathima
    Roshanara
    Subramaniam, V.
    INDIAN JOURNAL OF FIBRE & TEXTILE RESEARCH, 2017, 42 (04) : 426 - 430
12345