Creep deformation of TiAl-Si alloys with aligned γ/α2 lamellar microstructures

被引：0
|
作者：
D. R. Johnson
Y. Masuda
T. Yamanaka
H. Inui
M. Yamaguchi
机构：
[1] Purdue University,the School of Materials Engineering
[2] Kyoto University,the Department of Materials Science and Engineering
来源：
Metallurgical and Materials Transactions A | 2000年 / 31卷
关键词：
Material Transaction; Creep Rate; Creep Testing; Creep Strain; Primary Creep;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Creep tests were conducted on directionally solidified TiAl-Si alloys to discern the effect of lamellar spacing and lamellar orientation on the high-temperature strength. Directional solidification of a Ti-43Al-3Si alloy was used to produce a model microstructure consisting of a single γ/α2 lamellar colony of controlled orientation for creep testing. Different heat treatments were used to vary the lamellar spacing and tensile creep tests were performed at 750 °C using applied stresses of 180, 210, and 240 MPa. In addition, ingots with large columnar grains of various lamellar orientation were also tested. The results clearly show the beneficial effect of microstructural control with the aligned microstructure having a much superior creep resistance. Furthermore, for specimens with aligned lamellar microstructure, decreasing the lamellar spacing greatly improved creep resistance, as both the primary creep strain and secondary creep rate are much smaller for materials with the fine lamellar spacing.
引用
收藏
页码：2463 / 2473
页数：10
相关论文
共 50 条
  • [1] Creep deformation of TiAl-Si alloys with aligned γ/α2 lamellar microstructures
    Johnson, DR
    Masuda, Y
    Yamanaka, T
    Inui, H
    Yamaguchi, M
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (10): : 2463 - 2473
  • [2] Creep of TiAl-Si alloys with aligned lamellar microstrucures
    Johnson, DR
    Masuda, Y
    Yamanaka, T
    Inui, H
    Yamaguchi, M
    [J]. GAMMA TITANIUM ALUMINIDES 1999, 1999, : 627 - 631
  • [3] Directional solidification and creep deformation of TiAl-Si alloys
    Yamanaka, T
    Johnson, DR
    Masuda, Y
    Inui, H
    Yamaguchi, M
    [J]. GAMMA TITANIUM ALUMINIDES 1999, 1999, : 295 - 300
  • [4] Creep deformation of directionally-solidified TiAl-based alloys with aligned lamellar microstructures
    Omiya, Y
    Muto, S
    Yamanaka, T
    Johnson, DR
    Inui, H
    Yamaguchi, M
    [J]. PRICM 4: FORTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, VOLS I AND II, 2001, : 915 - 918
  • [5] Directional solidification of TiAl-Re-Si alloys with aligned γ/α2 lamellar microstructures
    Yamanaka, T
    Johnson, DR
    Inui, H
    Yamaguchi, M
    [J]. INTERMETALLICS, 1999, 7 (07) : 779 - 784
  • [6] Creep deformation in gamma TiAl alloys with lamellar structures
    Nieh, TG
    Wang, JN
    Hsiung, LM
    [J]. THERMEC '97 - INTERNATIONAL CONFERENCE ON THERMOMECHANICAL PROCESSING OF STEELS AND OTHER MATERIALS, VOLS I-II, 1997, : 1423 - 1431
  • [7] Crystal Plasticity Modeling of Creep in Alloys with Lamellar Microstructures at the Example of Fully Lamellar TiAl
    Schnabel, Jan E.
    Scheider, Ingo
    [J]. FRONTIERS IN MATERIALS, 2021, 7
  • [8] .1. Creep deformation of duplex and lamellar TiAl alloys
    Morris, MA
    Lipe, T
    [J]. INTERMETALLICS, 1997, 5 (05) : 329 - 337
  • [9] Directional solidification and microstructural control of the TiAl/Ti3Al lamellar microstructure in TiAl-Si alloys
    Johnson, DR
    Inui, H
    Yamaguchi, M
    [J]. ACTA MATERIALIA, 1996, 44 (06) : 2523 - 2535
  • [10] Development of TiAl-Si Alloys-A Review
    Knaislova, Anna
    Novak, Pavel
    Cabibbo, Marcello
    Jaworska, Lucyna
    Vojtech, Dalibor
    [J]. MATERIALS, 2021, 14 (04) : 1 - 22
12345