Anisotropy in Mechanical Properties and Corrosion of X-52 Pipeline Steel at Different Pipe Angles

被引：0
|
作者：
R. Ashari
A. Eslami
机构：
[1] Isfahan University of Technology,
[2] Department of Materials Engineering,undefined
[3] ,undefined
来源：
Protection of Metals and Physical Chemistry of Surfaces | 2019年 / 55卷
关键词：
corrosion; mechanical properties; pipeline steel; near-neutral pH;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：546 / 553
页数：7
相关论文
共 50 条
  • [1] Anisotropy in Mechanical Properties and Corrosion of X-52 Pipeline Steel at Different Pipe Angles
    Ashari, R.
    Eslami, A.
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2019, 55 (03) : 546 - 553
  • [2] Microstructural and mechanical properties in the weld bead of the API X-52 steel pipeline
    Albiter, A
    Contreras, A
    Angeles-Chavez, C
    Pérez, R
    EMERGING FIELDS IN SOL-GEL SCIENCE AND TECHNOLOGY, 2003, : 409 - 417
  • [3] Microscopy study of intergranular stress corrosion cracking of X-52 line pipe steel
    Li, J
    Elboujdaini, M
    Fang, B
    Revie, RW
    Phaneuf, MW
    CORROSION, 2006, 62 (04) : 316 - 322
  • [4] Effect of solution composition and electrochemical potential on stress corrosion cracking of X-52 pipeline steel
    Rebak, RB
    Xia, Z
    Safruddin, R
    SzklarskaSmialowska, Z
    CORROSION, 1996, 52 (05) : 396 - 405
  • [5] Erosion-corrosion of X-52 steel pipe under turbulent swirling impinging jets
    Sedano-de la Rosa, C.
    Vite-Torres, M.
    Godinez-Salcedo, J. G.
    Gallardo-Hernandez, E. A.
    Cuamatzi-Melendez, R.
    Farfan-Cabrera, L. I.
    WEAR, 2017, 376 : 549 - 556
  • [6] Effect of thermal and mechanical treatments on corrosion of API X-52 grade line pipe steel in flowing 3.5% NaCl solution
    Amarnath
    Upadhyay, SN
    Namboodhiri, TKG
    INDIAN JOURNAL OF CHEMICAL TECHNOLOGY, 2003, 10 (06) : 611 - 614
  • [7] Effect of artificial aging time on the mechanical properties of weldment on API 5L X-52 line pipe steel
    Vargas-Arista, B.
    Albiter, A.
    Angeles-Chavez, C.
    Hallen, J. M.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2006, 37A (09): : 2683 - 2690
  • [8] Mechanical and microstructural effects on the stress corrosion cracking of weld beads of X-52 and X-70 pipeline steels
    Contreras, A
    Albiter, A
    Angeles-Chavez, C
    Pérez, R
    REVISTA MEXICANA DE FISICA, 2004, 50 : 49 - 53
  • [9] STRESS-CORROSION CRACK INITIATION IN X-52 PIPELINE STEEL IN NEAR-NEUTRAL PH SOLUTION
    Fang, B.
    Eadie, R.
    Elboujdaini, M.
    PROCEEDINGS OF THE ASME INTERNATIONAL PIPELINE CONFERENCE 2010, VOL 1, 2010, : 347 - 356
  • [10] Advanced characterization of a stress corrosion crack from an in-field serviced X-52 steel line pipe
    Li, J
    Elboujdaini, M
    Gertsman, VY
    Gao, M
    Katz, DC
    AEROSPACE MATERIALS AND MANUFACTURING: DEVELOPMENT, TESTING, AND LIFE CYCLE ISSUES - HONORING WILLIAM WALLACE, 2004, : 515 - 523
12345