Effect of PgTPhPBr on the electrochemical and corrosion behaviour of 304 stainless steel in H2SO4 solution

被引：0
|
作者：
A.A. Hermas
M.S. Morad
M.H. Wahdan
机构：
[1] Assiut University,Chemistry Department, Faculty of Science
来源：
Journal of Applied Electrochemistry | 2004年 / 34卷
关键词：
corrosion; EIS; inhibition; phosphonium compounds; stainless steel;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Weight-loss, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) measurements were used to study the inhibition of 304 stainless steel corrosion in 1 M H2SO4 at 50 °C by propargyltriphenylphosphonium bromide (PgTPhPBr). The inhibiting effects of propyltriphenylphosphonium bromide (PrTPhPBr) and propargyl alcohol (PA) were also studied for the sake of comparison. For the investigated compounds, Tafel extrapolation in the cathodic region gave a corrosion inhibition efficiency of 98% at 1 × 10−3 M. Adsorption of both PgTPhPBr and PA was found to follow Frumkin's isotherm while adsorption of PrTPhPBr obeys that of Temkin. In the anodic domain, PgTPhPBr acted as a good passivator. The impedance spectra recorded at the corrosion potential (Ecor) revealed that the charge transfer process in the inhibited and uninhibited states controls corrosion of 304 stainless steel.
引用
收藏
页码：95 / 102
页数：7
相关论文
共 50 条
  • [31] Kinetics of Passive Film Growth on 304 Stainless Steel in H2SO4 Pickling Solution under Chemical Oxidation
    Yue, Yingying
    Liu, Chengjun
    Asselin, Edouard
    Shi, Peiyang
    Jiang, Maofa
    [J]. CORROSION, 2018, 74 (06) : 705 - 714
  • [32] STRESS CORROSION CRACKING OF 304 STAINLESS STEEL IN H2SO4-NaF AQUEOUS SOLUTION.
    Asawa, Mitsuo
    [J]. Nippon Kinzoku Gakkai-si, 1980, 44 (10): : 1194 - 1199
  • [33] Hemisynthesis, crystal structure and inhibitory effect of sesquiterpenic thiosemicarbazones and thiazolidin-4-ones on the corrosion behaviour of stainless steel in 1 M H2SO4 solution
    Bimoussa, Abdoullah
    Koumya, Yassine
    Abouelfida, Abdesselam
    Ait Itto, Moulay Youssef
    Benyaich, Abdelaziz
    Mentre, Olivier
    Ketatni, El Mostafa
    Auhmani, Aziz
    Auhmani, Abdelwahed
    [J]. ACTA CRYSTALLOGRAPHICA SECTION C-STRUCTURAL CHEMISTRY, 2019, 75 : 623 - +
  • [34] THE EFFECT OF CU ADDITION ON THE CORROSION BEHAVIOR OF SINTERED STAINLESS-STEEL IN H2SO4 ENVIRONMENT
    ITZHAK, D
    PELED, P
    [J]. CORROSION SCIENCE, 1986, 26 (01) : 49 - 54
  • [35] Corrosion resistance mechanism of palladium film-plated stainless steel in boiling H2SO4 solution
    Tang, Junlei
    Zhang, Zhiheng
    Wang, Yingying
    Ju, Pengfei
    Tang, Yuming
    Zuo, Yu
    [J]. CORROSION SCIENCE, 2018, 135 : 222 - 232
  • [36] Polarisation of low phosphorus AISI 304 stainless steel in H2SO4 containing arsenite
    Hermas, AA
    [J]. BRITISH CORROSION JOURNAL, 1999, 34 (02): : 132 - 138
  • [37] The secondary passive film for type 304 stainless steel in 0.5 M H2SO4
    Atrens, A
    Baroux, B
    Mantel, M
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1997, 144 (11) : 3697 - 3704
  • [38] EFFECT OF Ni ADDITION ON THE CORROSION BEHAVIOUR OF SINTERED STAINLESS STEEL IN H2SO4.
    Peled, P.
    Harush, S.
    Itzhak, D.
    [J]. Corrosion Science, 1988, 28 (04): : 327 - 332
  • [39] Corrosion Inhibition of l-Methionine Amino Acid as a Green Corrosion Inhibitor for Stainless Steel in the H2SO4 Solution
    M. Yeganeh
    I. Khosravi-Bigdeli
    M. Eskandari
    S. R. Alavi Zaree
    [J]. Journal of Materials Engineering and Performance, 2020, 29 : 3983 - 3994
  • [40] Effect of nitrogen on the electrochemical behavior of 301LN stainless steel in H2SO4 solutions
    Chou, SL
    Tsai, MJ
    Tsai, WT
    Lee, JT
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 1997, 51 (02) : 97 - 101
12345