STRESS CORROSION CRACKING OF 304 STAINLESS STEEL IN H2SO4-NaF AQUEOUS SOLUTION.

被引：0
|
作者：
Asawa, Mitsuo
机构：
来源：
Nippon Kinzoku Gakkai-si | 1980年 / 44卷 / 10期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Stress corrosion behavior of Type 304 wire in 2 kmol/m**3 H//2SO//4-NaF at 368 K was examined as functions of both the amount of alpha prime martensite induced by prestraining at various temperatures under a stress of 324 MPa and the NaF concentration. Results have been interpreted in terms of preferential dissolution of alpha prime martensite and chemical stability of the protective corrosion product.
引用
收藏
页码：1194 / 1199
相关论文
共 50 条
  • [1] STRESS-CORROSION CRACKING OF 304 STAINLESS-STEEL IN H2SO4-NAF AQUEOUS-SOLUTION
    ASAWA, M
    [J]. JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1980, 44 (10) : 1194 - 1199
  • [2] STRESS-CORROSION CRACKING OF 304 STAINLESS-STEEL IN H2SO4-NAI AQUEOUS-SOLUTION
    ASAWA, M
    [J]. JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1980, 44 (08) : 955 - 959
  • [3] INITIATION OF STRESS CORROSION CRACKING OF SUS 304 STAINLESS STEEL IN LOW CONCENTRATED MgCl2 SOLUTION.
    Takeyama, Shozoh
    Gohda, Susumu
    [J]. Zairyo/Journal of the Society of Materials Science, Japan, 1986, 35 (391) : 381 - 387
  • [4] EFFECT OF HYDROGEN CHARGING ON STRESS CORROSION CRACKING OF 18-8 STAINLESS STEEL IN H2SO4-NaCl SOLUTION.
    Kamide, Hidehiko
    Sugawara, Hideo
    [J]. 1600, (42):
  • [5] Influences of concentrations of H2SO4 and NaCl on stress corrosion cracking of SUS304 stainless steel in H2SO4-NaCl aqueous solutions
    Sunada, S
    Kariba, M
    Majima, K
    Sugimoto, K
    [J]. MATERIALS TRANSACTIONS, 2006, 47 (02) : 364 - 370
  • [6] Stress Corrosion Cracking of 304 Austenitic Stainless Steel in H2SO4/NaCl Media at Room Temperature
    Alshamsi, Ahmed S.
    [J]. Corrosion, 2024, 80 (09) : 910 - 921
  • [7] STRESS CORROSION CRACKING OF AUSTENITE STAINLESS STEEL IN CONCENTRATED CHLORIDE SOLUTION.
    Shinohara, Nobuyuki
    [J]. Boshoku gijutsu, 1980, 29 (10): : 497 - 501
  • [8] Stress corrosion cracking of sensitized Type 304 stainless steel in thiosulphate solution. II. Dynamics of fracture
    Gomez-Duran, Monika
    Macdonald, Digby D.
    [J]. CORROSION SCIENCE, 2006, 48 (07) : 1608 - 1622
  • [9] Stress Corrosion Cracking of a 304 Stainless Steel Elbow
    Guo, Weimin
    Ding, Ning
    Liu, Long
    Xu, Na
    Li, Nan
    Zhang, Feng
    Chen, Lizong
    [J]. JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2020, 20 (02) : 483 - 493
  • [10] Stress Corrosion Cracking of a 304 Stainless Steel Elbow
    Weimin Guo
    Ning Ding
    Long Liu
    Na Xu
    Nan Li
    Feng Zhang
    Lizong Chen
    [J]. Journal of Failure Analysis and Prevention, 2020, 20 : 483 - 493
12345