Investigation of the initiation of corrosion cracks in the cladding layer of a bimetal

被引：0
|
作者：
V. A. Levchenko
A. N. Kuzyukov
V. A. Varenyuk
机构：
来源：
Materials Science | 1997年 / 33卷
关键词：
Residual Stress; Crack Initiation; Nonmetallic Inclusion; Residual Tensile Stress; Corrosion Testing;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
We describe a specially-designed installation for the corrosion testing of bimetals, study the effect of the state of the surface of the cladding layer of a bimetal on the initiation of corrosion cracks, investigate the influence of the disclocation structure on the processes of pitting and crack initiation, analyze distinctive features of the process of propagation of corrosion cracks in the cladding layer along the interface of the metals, and suggest a method for the protection of two-layer structures against corrosion cracking by polishing and etching with aqua regia.
引用
收藏
页码：104 / 107
页数：3
相关论文
共 50 条
  • [41] INITIATION AND EARLY GROWTH MECHANISMS OF CORROSION FATIGUE CRACKS IN STAINLESS-STEELS
    MATHIS, R
    JOURNAL OF MATERIALS SCIENCE, 1987, 22 (03) : 907 - 914
  • [42] Microstructure and electrochemical corrosion behavior of fecrnimo layer fabricated by laser cladding
    Huang, Jie
    He, Ding-Yong
    Du, Kai-Ping
    Yang, Yan-Ge
    Guo, Xing-Ye
    Wu, Xu
    Yu, Yue-Guang
    Zhou, Zheng
    Surface Technology, 2020, 49 (12): : 228 - 234
  • [43] INVESTIGATION OF ANODE PROCESSES DURING THE FORMATION OF CRACKS IN METALS BY CORROSION
    TOMASHOV, ND
    ISAEV, NI
    DOKLADY AKADEMII NAUK SSSR, 1960, 132 (02): : 409 - 412
  • [44] INVESTIGATION OF THE PROCESS OF THE INITIATION AND DEVELOPMENT OF CRACKS IN STEELS LIABLE TO TEMPERING BRITTLENESS
    TOMENKO, YS
    INDUSTRIAL LABORATORY, 1963, 29 (01): : 92 - 96
  • [45] Experimental investigation on the initiation and propagation of corrosion fatigue cracks in EA4T axle steel treated by ultrasonic surface rolling
    Ji, Dongdong
    Zhang, Jiwang
    Li, Hang
    Su, Kaixin
    JOURNAL OF MATERIALS SCIENCE, 2025, 60 (01) : 604 - 624
  • [46] THE INITIATION OF WEAR CRACKS
    HILLS, DA
    ASHELBY, DW
    WEAR, 1981, 70 (03) : 365 - 371
  • [47] Investigation on Corrosion Model of Cr-coated Zirconium Alloy Cladding
    Shen, Yong
    Zeng, Xiehu
    Duan, Zhengang
    Wen, Qinglong
    Yuan, Bo
    He, Liang
    Gao, Shixin
    Hedongli Gongcheng/Nuclear Power Engineering, 2024, 45 : 175 - 180
  • [48] AGR Cladding Corrosion: Investigation of the Effect of Temperature on Unsensitized Stainless Steel
    Elizabeth Howett
    Colin Boxall
    David Hambley
    MRS Advances, 2017, 2 (11) : 615 - 620
  • [49] INVESTIGATION ON THE CORROSION BEHAVIOR OF HAHA-4 CLADDING BY OXIDE CHARACTERIZATION
    Park, Jeong-Yong
    Choi, Byung-Kwon
    Jeong, Yong Hwan
    NUCLEAR ENGINEERING AND TECHNOLOGY, 2009, 41 (02) : 149 - 154
  • [50] Effects of Different Parameters on Initiation and Propagation of Stress Corrosion Cracks in Pipeline Steels: A Review
    Mohtadi-Bonab, M. A.
    METALS, 2019, 9 (05)
12345