Investigation of the initiation of corrosion cracks in the cladding layer of a bimetal

被引：0
|
作者：
V. A. Levchenko
A. N. Kuzyukov
V. A. Varenyuk
机构：
来源：
Materials Science | 1997年 / 33卷
关键词：
Residual Stress; Crack Initiation; Nonmetallic Inclusion; Residual Tensile Stress; Corrosion Testing;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
We describe a specially-designed installation for the corrosion testing of bimetals, study the effect of the state of the surface of the cladding layer of a bimetal on the initiation of corrosion cracks, investigate the influence of the disclocation structure on the processes of pitting and crack initiation, analyze distinctive features of the process of propagation of corrosion cracks in the cladding layer along the interface of the metals, and suggest a method for the protection of two-layer structures against corrosion cracking by polishing and etching with aqua regia.
引用
收藏
页码：104 / 107
页数：3
相关论文
共 50 条
  • [31] Hot cracks as stress corrosion cracking initiation sites in laser welded corrosion resistant alloys
    Stelling, K
    Böllinghaus, T
    Wolf, M
    Schöler, A
    Burkert, A
    Isecke, B
    HOT CRACKING PHENOMENA IN WELDS, 2005, : 165 - 182
  • [32] Gel structure of the corrosion layer on cladding pipes of nuclear fuel
    Medek, Jiri
    Weishauptova, Zuzana
    JOURNAL OF NUCLEAR MATERIALS, 2009, 393 (02) : 306 - 310
  • [33] Research status of erosion-corrosion of laser cladding layer
    Pei, Rui
    Wang, Qin-Ying
    Tang, Miao
    Jiang, Yu-Man
    Xi, Yu-Chen
    Surface Technology, 2019, 48 (11): : 179 - 187
  • [34] INVESTIGATION ON ELECTROCHEMISTRY INSIDE STRESS CORROSION CRACKS OR PITS
    左景伊
    刘幼平
    许淳淳
    金志强
    Chinese Journal of Chemical Engineering, 1995, (04) : 32 - 39
  • [35] Investigation on electrochemistry inside stress corrosion cracks or pits
    Zuo, JY
    Liu, YP
    Xu, CC
    Jin, ZQ
    CHINESE JOURNAL OF CHEMICAL ENGINEERING, 1995, 3 (04) : 215 - 222
  • [36] Investigation of multi-layer spray deposition of aluminum/steel bimetal
    Ning, Hong-Long
    Wang, Yi-Ping
    Huang, Fu-Xiang
    Ma, Ju-Sheng
    Geng, Zhi-Ting
    Chen, Zhen-Hua
    Gongneng Cailiao/Journal of Functional Materials, 2002, 33 (02): : 166 - 168
  • [37] Estimating Critical Corrosion for Initiation of Longitudinal Cracks in RC Structures Considering Phases and Composition of Corrosion Products
    Behera, Prasanna Kumar
    Moon, Abhijeet Prem Kumar
    Mondal, Kallol
    Misra, Sudhir
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2016, 28 (12)
  • [38] An evaluation of the resistance of pipeline steels to initiation and early growth of stress corrosion cracks
    Cerny, I
    Linhart, V
    ENGINEERING FRACTURE MECHANICS, 2004, 71 (4-6) : 913 - 921
  • [39] INITIATION AND EARLY STAGES OF GROWTH OF CORROSION FATIGUE CRACKS IN A STRUCTURAL-STEEL
    HUSAIN, Z
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 119 : L1 - L4
  • [40] The initiation and propagation of stress corrosion cracks in high temperature and high pressure conditions
    Novotny, R
    Sajdl, P
    Vosta, J
    Macák, J
    HYDROGEN EFFECTS ON MATERIAL BEHAVIOR AND CORROSION DEFORMATION INTERACTIONS, 2003, : 791 - 798
12345