Investigation of the initiation of corrosion cracks in the cladding layer of a bimetal

被引：0
|
作者：
V. A. Levchenko
A. N. Kuzyukov
V. A. Varenyuk
机构：
来源：
Materials Science | 1997年 / 33卷
关键词：
Residual Stress; Crack Initiation; Nonmetallic Inclusion; Residual Tensile Stress; Corrosion Testing;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
We describe a specially-designed installation for the corrosion testing of bimetals, study the effect of the state of the surface of the cladding layer of a bimetal on the initiation of corrosion cracks, investigate the influence of the disclocation structure on the processes of pitting and crack initiation, analyze distinctive features of the process of propagation of corrosion cracks in the cladding layer along the interface of the metals, and suggest a method for the protection of two-layer structures against corrosion cracking by polishing and etching with aqua regia.
引用
收藏
页码：104 / 107
页数：3
相关论文
共 50 条
  • [1] Investigation of the initiation of corrosion cracks in the cladding layer of a bimetal
    Levchenko, VA
    Kuzyukov, AN
    Varenyuk, VA
    MATERIALS SCIENCE, 1997, 33 (01) : 104 - 107
  • [2] CORROSION-RESISTANCE OF WELD SEAMS OF A CLADDING LAYER OF BIMETAL
    DUBEN, LV
    DIKUN, VN
    KLYACHKO, YA
    DEKHTYAR.NG
    WELDING PRODUCTION, 1972, 19 (11): : 46 - 50
  • [3] CORROSION RESISTANCE OF THE WELD SEAMS OF A CLADDING LAYER OF BIMETAL.
    Duben, L.V.
    Dikun, V.N.
    Klyachko, Yu.A.
    Dekhtyarenko, N.G.
    1600, (19):
  • [4] Use of Corrosion-Resistant Steels Alloyed with Nitrogen as a Bimetal Cladding Layer Prepared by Explosion Welding
    K. A. Udod
    I. G. Rodionova
    L. B. Pervukhin
    Metallurgist, 2016, 60 : 867 - 870
  • [5] Use of Corrosion-Resistant Steels Alloyed with Nitrogen as a Bimetal Cladding Layer Prepared by Explosion Welding
    Udod, K. A.
    Rodionova, I. G.
    Pervukhin, L. B.
    METALLURGIST, 2016, 60 (7-8) : 867 - 870
  • [6] Thermodynamic Development of Austenite-Martensite Class Corrosion-Resistant Steels Intended for a Bimetal Cladding Layer
    N. G. Shaposhnikov
    I. G. Rodionova
    A. A. Pavlov
    Metallurgist, 2016, 59 : 1195 - 1200
  • [7] Thermodynamic Development of Austenite-Martensite Class Corrosion-Resistant Steels Intended for a Bimetal Cladding Layer
    Shaposhnikov, N. G.
    Rodionova, I. G.
    Pavlov, A. A.
    METALLURGIST, 2016, 59 (11-12) : 1195 - 1200
  • [8] The initiation of cracks in cladding tubes of Zr-1%Nb alloy under stress corrosion cracking conditions
    Bibilashvili, YK
    Dolgov, YN
    Novikov, VV
    Glazkov, AG
    ATOMIC ENERGY, 1996, 80 (04) : 242 - 247
  • [9] Investigation on a corrosion product deposit layer on a boiling water reactor fuel cladding
    Orlov, A. V.
    Restani, R.
    Kuri, G.
    Degueldre, C.
    Valizadeh, S.
    NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2010, 268 (3-4): : 297 - 305
  • [10] Effect of Concrete Settlement Cracks on Corrosion Initiation
    O'Reilly, M.
    Lafikes, J.
    Farshadfar, O.
    Grayli, P. Vosough
    Al-Qassag, O.
    Darwin, D.
    ACI MATERIALS JOURNAL, 2022, 119 (04) : 117 - 124
12345