Characterization of as-deposited and annealed Cr-C alloy coatings produced from a trivalent chromium bath

被引：69
|
作者：
Ghaziof, S. [1 ]
Golozar, M. A. [1 ]
Raeissi, K. [1 ]
机构：
[1] Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran
来源：
JOURNAL OF ALLOYS AND COMPOUNDS | 2010年 / 496卷 / 1-2期
关键词：
Cr-C alloy; Coating; Amorphous; Nanocrystalline; Annealing; Corrosion resistance; ELECTROCHEMICAL-BEHAVIOR; MECHANICAL-PROPERTIES; FORMIC-ACID; ELECTRODEPOSITION; LAYER;
D O I：
10.1016/j.jallcom.2010.02.101
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Amorphous Cr-C alloy coatings were electrodeposited from a trivalent chromium bath containing formic acid. The effects of plating parameters such as pH and current density on composition, structure, morphology and corrosion behaviour of as-deposited coatings were investigated. Results showed that the suitable current density for Cr-C alloy electrodeposition is increased as the pH is decreased. Furthermore, by decreasing the pH, higher amount of carbon was introduced into the coatings. The Cr-C alloy coatings deposited at lower pH showed higher passive current density on Tafel plot. By annealing the amorphous Cr-C alloy coatings at 300 degrees C. a nanocrystalline structure having higher hardness was obtained. However, the corrosion resistance was seen to be impaired. Annealing at 600 degrees C led to the precipitation of Cr23C6 which resulted in a higher hardness. The formation of Cr23C6 enhanced the corrosion resistance of coatings due to an increase in corrosion potential. However, formation of micro-cells between the Cr23C6 precipitates and bulk chromium prevented the passive film formation. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码：164 / 168
页数：5
相关论文
共 50 条
  • [41] Characterization of Cr-ZrO2 composite coatings electrodeposited from Cr(III) bath
    Bikulcius, G.
    Cesuniene, A.
    Selskiene, A.
    Grigucevciene, A.
    Jasulaitiene, V
    Ger, M.
    CHEMIJA, 2018, 29 (02): : 97 - 107
  • [42] Properties of nanocrystalline Cr coatings prepared by cathode plasma electrolytic deposition from trivalent chromium electrolyte
    Beijing Key Laboratory for Corrosion, Erosion and Surface Technology, University of Science and Technology Beijing, Beijing
    100083, China
    Surf. Coat. Technol., 1 (319-323):
  • [43] Properties of nanocrystalline Cr coatings prepared by cathode plasma electrolytic deposition from trivalent chromium electrolyte
    Quan, Cheng
    He, Yedong
    SURFACE & COATINGS TECHNOLOGY, 2015, 269 : 319 - 323
  • [44] Improving hardness and tribological characteristics of nanocrystalline Cr-C films obtained from Cr(III) plating bath using pulsed electrodeposition
    Protsenko, V. S.
    Danilov, F. I.
    Gordiienko, V. O.
    Baskevich, A. S.
    Artemchuk, V. V.
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2012, 31 : 281 - 283
  • [45] Electrodeposition of corrosion-resistant Cr–P and Cr–P–W coatings from solutions based on compounds of trivalent chromium
    V. V. Kuznetsov
    E. G. Vinokurov
    A. V. Telezhkina
    E. A. Filatova
    Journal of Solid State Electrochemistry, 2019, 23 : 2367 - 2376
  • [46] Influence of the deposition process and substrate on microstructure, phase composition, and residual stress state on as-deposited Cr-Al-C coatings
    Heinze, Stefan
    Kruelle, Tim
    Ewenz, Lars
    Krywka, Christina
    Davydok, Anton
    Stark, Andreas
    Cremer, Rainer
    Leyens, Christoph
    MATERIALS & DESIGN, 2023, 225
  • [47] Antifriction coatings of Pb-Sn-Cu alloy electro-deposited from methanesulphonate bath
    Danilov, F. I.
    Protsenko, V. S.
    Vasil'eva, E. A.
    Kabat, O. S.
    TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 2011, 89 (03): : 151 - 154
  • [48] Establishing relationships between bath chemistry, electrodeposition and microstructure of Co-W alloy coatings produced from a gluconate bath
    Weston, D. P.
    Harris, S. J.
    Shipway, P. H.
    Weston, N. J.
    Yap, G. N.
    ELECTROCHIMICA ACTA, 2010, 55 (20) : 5695 - 5708
  • [49] Effect of the Incorporation of SiC Fine Particle on the Tribological Behaviors of Chromium Coating Deposited from Trivalent Chromium Bath (Investigation on Dry Sliding Characteristics against Alumina)
    Sakurai, Takuto
    Sato, Hideaki
    Shimpo, Ryokichi
    Kameyama, Yutaka
    Zairyo/Journal of the Society of Materials Science, Japan, 2024, 73 (11) : 853 - 860
  • [50] Characterization of Cr-Ni-ZrO2 Composite Coatings Electrodeposited from Cr(III) Plating Bath
    He, Xiangzhu
    Zhou, Xinli
    Zhang, Xiaowei
    Sun, Xin
    ADVANCED MATERIALS, PTS 1-4, 2011, 239-242 : 2733 - 2737
12345